PMMA PLEXIGLAS HFI7G 产品说明：

Plexiglas? HFI7G is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications.This grade is formulated for approved medical applications and has improved gamma resistance compared to HFI7. It is heat resistant, has high melt flow and provides 7 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Supplemental moldflow simulation data is available.

物理性能	额定值	单位制	测试方法
比重	1.17	g/cm3	ASTM D792
熔流率（熔体流动速率）(230°C/3.8 kg)	10	g/10 min	ASTM D1238
收缩率 - 流动	0.30 到 0.60	%	ASTM D955
吸水率(24 hr)	0.30	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度(M 级)	65		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量	2450	MPa	ASTM D638
抗张强度(屈服)	46.9	MPa	ASTM D638
伸长率(断裂)	35	%	ASTM D638
弯曲模量	2450	MPa	ASTM D790
弯曲强度(屈服)	85.5	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度(23°C)	32	J/m	ASTM D256

PMMA PLEXIGLAS HFI7G

PMMA 特性

①高度透明性。有机玻璃是优良的高分子透明材料，透光率达到92%，比玻璃的透光度高。被称为人造小太阳的太阳灯的灯管是石英做的，这是因为石英能完全透过紫外线。普通玻璃只能透过0.6%的紫外线，但有机玻璃却能透过73%。

②机械强度高。有机玻璃的相对分子质量大约为200万，是长链的高分子化合物，而且形成分子的链很柔软，因此，有机玻璃的强度比较高，抗拉伸和抗冲击的能力比普通玻璃高7-18倍。有一种经过加热和拉伸处理过的有机玻璃，其中的分子链段排列得非常有次序，使材料的韧性有显著提高。用钉子钉进这种有机玻璃，即使钉子穿透了，有机玻璃上也不产生裂纹。这种有机玻璃被子弹击穿后同样不会破成碎片。因此，拉伸处理的有机玻璃可用作防弹玻璃，也用作军用飞机上的座舱盖。

优点

一、有机玻璃的美观性：呈镜面效果，工艺精美，无褶皱，无接缝；

二、有机玻璃的视觉效果：色彩多种多样、视觉冲击力很强；

三、有机玻璃的透光性：透光率可达到96%，透光率极佳、光线比较柔和；

四、有机玻璃的耐冲击性：是普通玻璃产品的200倍以上，几乎没有任何断裂的危险；

五、有机玻璃的耐久性：产品对内置光源有很良好的保护，延长光源产品使用的寿命；

六、有机玻璃的耐侯性：可保长久不褪色，质量好的板材使用年限长达6-13年之久；

七、有机玻璃的耐燃性：不会有自燃并具自熄性；

八、有机玻璃的节能性：透光性非常好，相对减少光源，省电，降低使用的成本；

九、有机玻璃的合理性：合理性的设计和防雨防潮，开启式的结构，便于清洁维修等。

应用

1.建筑应用:橱窗、隔音门窗、采光罩、电话亭等

2.广告应用:灯箱、招牌、指示牌、展架等

3.交通应用:火车、汽车等车辆门窗等

4.医学应用:婴儿保育箱、各种手术医疗器具 民用品：卫浴设施、工艺品、化妆品、支架、水族箱等

5.工业应用：仪器表面板及护盖等

6.照明应用：日光灯、吊灯、街灯罩等

7.家居应用：果盘，纸巾盒，亚克力艺术画等家居日用产品

PMMA PLEXIGLAS HFI7G 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！