PMMA PLEXIGLAS HFI10 产品说明：

Plexiglas? HFI10 is an impact modified thermoplastic acrylic resin formulated for injection molding. It has high melt flow, enhanced mold release properties and provides 10 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Supplemental moldflow simulation data is available.

物理性能	额定值	单位制	测试方法
比重	1.15	g/cm3	ASTM D792
熔流率（熔体流动速率）(230°C/3.8 kg)	3.3	g/10 min	ASTM D1238
收缩率 - 流动	0.30 到 0.80	%	ASTM D955
吸水率(24 hr)	0.40	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度(M 级)	38		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量	1860	MPa	ASTM D638
抗张强度(断裂)	37.9	MPa	ASTM D638
伸长率(断裂)	50	%	ASTM D638
弯曲模量	1860	MPa	ASTM D790
弯曲强度(屈服)	71.0	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度(23°C)	48	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度1			ASTM D648
0.45 MPa, 退火	88.9	°C	ASTM D648
1.8 MPa, 退火	79.4	°C	ASTM D648
维卡软化温度
--	93.9	°C	ASTM D15252
--	82.8	°C	ASTM D15253
导热系数	0.22	W/m/K	ASTM C177

PMMA PLEXIGLAS HFI10

PMMA 性能

电性能

聚甲基丙烯酸甲酯由于主链侧位含有极性的甲酯基，电性能不及聚烯烃和聚苯乙烯等非极性塑料。甲酯基的极性并不太大，聚甲基丙烯酸甲酯仍具有良好的介电和电绝缘性能。值得指出的是，聚甲基丙烯酸甲酯乃至整个丙烯酸类塑料，都具有优异的抗电弧性，在电弧作用下，表面不会产生碳化的导电通路和电弧径迹现象。20℃是一个二级转变温度，相应于侧甲酯基开始运动的温度，低于20℃，侧甲酯基处于冻结状态，材料的电性能比处于20℃以上时会有所提高。

物理性能

聚甲基丙烯酸甲酯具有良好的综合力学性能，在通用塑料中居前列，拉伸、弯曲、压缩等强度均高于聚烯烃，也高于聚苯乙烯、聚氯乙烯等，冲击韧性较差，但也稍优于聚苯乙烯。浇注的本体聚合聚甲基丙烯酸甲酯板材（例如航空用有机玻璃板材）拉伸、弯曲、压缩等力学性能更高一些，可以达到聚酰胺、聚碳酸酯等工程塑料的水平。

PMMA 用途

PMMA具有质轻、价廉，易於成型等优点。溶于有机溶剂如苯甲醚等，可以形成良好的薄膜和良好的介电性能，可以作为有机场效应管的介质层。

它的成型方法有浇铸，射出成型，机械加工、热成型等。尤其是射出成型，可以大批量生产，制程简单，成本低。因此，它的应用日趋广泛，它广泛用于仪器仪表零件、汽车车灯、光学镜片、透明管道。

有机玻璃压克力（亚克力）在建筑业中的应用在建筑方面，有机玻璃压克力（亚克力）主要应用于建筑采光体、透明屋顶、棚顶、电话亭、楼梯和房间墙壁护板等方面；卫生洁具方面有浴缸、洗脸盆、化妆台等产品。在高速公路及高等级道路照明灯罩及汽车灯具方面的应用发展也相当快。其中，建筑采光体、浴缸、街头广告灯箱和电话亭等方面的市场增长较快，今后的发展空间较大，市场前景十分广阔。

PMMA PLEXIGLAS HFI10 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！