Technical Datasheet |Supplied by LG Chem

Lupoy? GN5151RF is a general purpose, halogen-free flame retardant polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem, reinforced with 15% mineral. Exhibits high performance and high stiffness. Lupoy? GN5151RF is suitable for processing by injection molding. Used in IT/OA notebook PC, electrical and electronic housings. Complies with UL 94 V0 flame rating.

• 性能项目		试验条件[状态]	测试方法	测试数据	数据单位
  物理性能	比重		ASTMD792	1.25	g/cm3
  	熔流率（熔体流动速率）(250°C/2.16kg)		ASTMD1238	9.0	g/10min
  	收缩率-流动(3.20mm)		ASTMD955	0.20to0.40	%
  机械性能	抗张强度2(屈服,3.20mm)		ASTMD638	60.8	MPa
  	伸长率2(断裂,3.20mm)		ASTMD638	15	%
  	弯曲模量3(3.20mm)		ASTMD790	4120	MPa
  	弯曲强度4(屈服,3.20mm)		ASTMD790	108	MPa
  冲击性能	悬壁梁缺口冲击强度(23°C,3.20mm)		ASTMD256	98	J/m
  热性能	载荷下热变形温度4(0.45MPa,未退火,6.40mm)		ASTMD648	95.0	°C
  	RTIElec		UL746	60.0	°C
  	RTIImp		UL746	60.0	°C
  	RTIStr		UL746	60.0	°C
  可燃性	FlameRating(1.0mm)		UL94	V-0

PC/ABS LUPOY GN5151RF

PC/ABS合金，PC与ABS共混物可以综合PC和ABS的优良性能，提高ABS的耐热性、抗冲击和拉伸强度，降低PC成本和熔体粘度，改善加工性能，减少制品内应力和冲击强度对制品厚度的敏感性。PC/ABS合金发展迅速，全球产量约为80万吨/年左右，世界各大公司纷纷开发推出PC/ABS合金新品种，如阻燃、玻纤增强、电镀、耐紫外线等品种，尤其是在汽车工业中得到广泛应用，另外还广泛应用于计算机、复印机和电子电气部件等。我国也开始一定研究和生产，如上海杰事杰公司的PC/ABS合金材料已应用于汽车装饰件、灯壳和耐热电器壳体；中科院长春应用化学所开发的高耐热、高耐热高抗冲、高耐热阻燃三个品级的PC/ABS合金材料已被国内数家汽车制造公司使用，用做前装饰板、仪表板及物品箱盖专用料等。兰州大学研究在PC/ABS共混体系中加入高压聚乙烯进行增容改性，得到混合物流动性好且低温韧性与模量几乎不受影响，适用于制作薄壁板材；国内研究人员为了降低PC/ABS两相之间的界面能，在PC和ABS中加入抗冲击剂MBS，合金的空冲击度可以达到极高值，

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。

化学和物理特性: PC/ABS具有PC和ABS两者的综合特性。例如ABS的易加工特性和PC的优良机械特性和热稳定性。二者的比率将影响PC/ABS材料的热稳定性。PC/ABS这种混合材料还显示了优异的流动特性。收缩率在0.5%左右。

PC/ABS LUPOY GN5151RF 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！