ULTRAMID? A3XZG5 BASF Corporation 尼龙66
ULTRAMID? A3ZG6 BASF Corporation 尼龙66
ULTRAMID? A3Z3 BASF Corporation 尼龙66
ULTRAMID? A3Z BASF Corporation 尼龙66
ULTRAMID? A3HG7 BASF Corporation 尼龙66
ULTRAMID? A3UG5 BASF Corporation 尼龙66
Ultramid A3WG5 BK00564
聚酰胺66
25% 玻璃纤维增强材料
BASF Corporation
产品说明：
Ultramid A3WG5 BK00564 is a 25% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade.
Applications
Applications
Typical applications include machinery components and housings of high stiffness and dimensional stability such as coil formers and bearing cages. A3EG5 and A3HG5 are the preferred grades for producing electrically insulating parts.
Ultramid A3WG5 BK00564 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.32 | g/cm3 | ISO 1183 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 6.0 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 1.9 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量(23°C) | 8100 | MPa | ISO 527-2 |
| 拉伸应力(断裂, 23°C) | 150 | MPa | ISO 527-2 |
| 拉伸应变(断裂, 23°C) | 2.7 | % | ISO 527-2 |
| 弯曲模量(23°C) | 7480 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度(23°C) | 6.7 | kJ/m2 | ISO 180 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度(1.8 MPa, 未退火) | 250 | °C | ISO 75-2/A |
| 溶融温度（DSC） | 260 | °C | ISO 3146 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 加工（熔体）温度 | 280 到 305 | °C | |
| 模具温度 | 80.0 到 90.0 | °C | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 |