Polymer,Thermoplastic,Nylon,Nylon 66
SABIC Innovative Plastics (GE Plastics)
产品说明:
LNP* Verton* RX93407D is a compound based on Nylon 66 resin.
This data was supplied by SABIC-IP for the Americas region.
SABIC Innovative Plastics LNP Verton RX93407D PA 66 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.50 g/cc | 1.50 g/cc | ASTM D 792 |
| 密度 | 1.51 g/cc | 0.0546 lb/in3 | ASTM D 792 |
| 1.54 g/cc | 0.0556 lb/in3 | ASTM D 792 | |
| 平衡吸湿 | 0.93 % | 0.93 % | 23°C / 50% RH; ISO 62 |
| 0.64 %
@Time 86400 sec
|
0.64 %
@Time 24.0 hour
|
50% RH; ASTM D 570 | |
| 线性模具收缩，Flow | 0.0010 - 0.0030 cm/cm
@Time 86400 sec
|
0.0010 - 0.0030 in/in
@Time 24.0 hour
|
ASTM D 955 |
| 0.0040 cm/cm
@Time 86400 sec
|
0.0040 in/in
@Time 24.0 hour
|
ASTM D 955 | |
| 线性成型收缩率，横向 | 0.0060 - 0.0080 cm/cm
@Time 86400 sec
|
0.0060 - 0.0080 in/in
@Time 24.0 hour
|
ASTM D 955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 211 MPa | 30600 psi | Type I, 5 mm/min; ASTM D 638 |
| 214 MPa | 31000 psi | ASTM D 638 | |
| 220 MPa | 31900 psi | 5 mm/min; ISO 527 | |
| 伸长率 (断裂) | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D 638 | |
| 2.1 % | 2.1 % | ASTM D 638 | |
| 拉伸模量 | 14.24 GPa | 2065 ksi | 5 mm/min; ASTM D 638 |
| 14.75 GPa | 2139 ksi | 1 mm/min; ISO 527 | |
| 15.9 GPa | 2310 ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | 304 MPa | 44100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 310 MPa | 45000 psi | ISO 178 | |
| 330 MPa | 47900 psi | ASTM D 790 | |
| 306 MPa | 44400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 11.83 GPa | 1716 ksi | 2 mm/min; ISO 178 | |
| 13.67 GPa | 1983 ksi | ASTM D 790 | |
| 悬壁梁缺口冲击强度 | 2.22 J/cm
@Temperature 23.0 °C
|
4.16 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 |
| 2.67 J/cm
@Temperature 23.0 °C
|
5.00 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Unnotched | 11.8 J/cm
@Temperature 23.0 °C
|
22.1 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 |
| 14.75 J/cm
@Temperature 23.0 °C
|
27.63 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 | |
| 悬壁梁缺口冲击强度 | 27.0 kJ/m2
@Temperature 23.0 °C
|
12.8 ft-lb/in2
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 75.0 kJ/m2
@Temperature 23.0 °C
|
35.7 ft-lb/in2
@Temperature 73.4 °F
|
80*10*4; ISO 180/1U |
| 简支梁无缺口冲击强度 | 8.80 J/cm2
@Temperature 23.0 °C
|
41.9 ft-lb/in2
@Temperature 73.4 °F
|
ISO 179/2C |
| 简支梁缺口冲击强度 | 2.40 J/cm2
@Temperature 23.0 °C
|
11.4 ft-lb/in2
@Temperature 73.4 °F
|
ISO 179/2C |
| 冲击试验 | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| 17.0 J
@Temperature 23.0 °C
|
12.5 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 33.0 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
18.3 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
ASTM D 696 |
| 线性热膨胀系数,横向流动 | 61.0 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
33.9 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
ASTM D 696 |
| 载荷下热变形温度(0.46 MPa) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C
@Thickness 3.20 mm
|
493 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 249 °C | 480 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 249 °C
@Thickness 3.20 mm
|
480 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| 251 °C
@Thickness 3.20 mm
|
484 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 |