东莞市广裕塑胶原料有限公司
塞拉尼斯PPS 1140LC6 40%玻纤增强 高强度 高刚性 耐水解
Celanese FORTRON 1140LC6 PPS, 40% Specialty
Polymer,Thermoplastic,Polyphenylene Sulfide (PPS),Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Celanese Corporation
产品说明:
Fortron 1140LC6 is a 40% glass fiber reinforced material with a total chlorine content less than or equal to 900 ppm*. It offers excellent physical properties similar to those of the Fortron 1140L6 product.
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be = - 30° C. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (= 60 h).
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be = - 30° C. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (= 60 h).
Information provided by Celanese Corporation.
Celanese FORTRON 1140LC6 PPS, 40% Specialty 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.66 g/cc | 0.0600 lb/in3 | ISO 1183 |
| 线性成型收缩率,Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ISO 294-4 |
| 线性成型收缩率，横向 | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 190 MPa | 27600 psi | 5mm/min; ISO 527-2/1A |
| 伸长率 (断裂) | 1.9 % | 1.9 % | 5mm/min; ISO 527-2/1A |
| 弯曲强度 | 265 MPa | 38400 psi | ISO 178 |
| 弯曲模量 | 13.5 GPa | 1960 ksi | ISO 178 |
| 悬壁梁缺口冲击强度 | 11.0 kJ/m2 | 5.23 ft-lb/in2 | ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 43.0 kJ/m2
@Temperature 23.0 °C
|
20.5 ft-lb/in2
@Temperature 73.4 °F
|
ISO 180/1U |
| 简支梁无缺口冲击强度 | 4.50 J/cm2 | 21.4 ft-lb/in2 | ISO 179/1eU |
| 简支梁缺口冲击强度 | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | = 1.00e+13 ohm-cm | = 1.00e+13 ohm-cm | IEC 60093 |
| 表面电阻 | = 1.00e+15 ohm | = 1.00e+15 ohm | IEC 60093 |
| 介电常数 | 3.7
@Frequency 10000 Hz
|
3.7
@Frequency 10000 Hz
|
IEC 60250 |
| 介电强度 | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| 耗散因数 | 0.0010
@Frequency 1000 Hz
|
0.0010
@Frequency 1000 Hz
|
IEC 60250 |
| 相比耐漏电起痕指数(CTI) | 175 V | 175 V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 17.0 μm/m-°C | 9.44 μin/in-°F | ISO 11359-2 |
| 线性热膨胀系数,横向流动 | 44.0 μm/m-°C | 24.4 μin/in-°F | ISO 11359-2 |
| 载荷下热变形温度(1.8 MPa) | 260 °C | 500 °F | ISO 75-1, -2 |
| 载荷下热变形温度(8.0 MPa) | 170 °C | 338 °F | ISO 75-1, -2 |
PPS塑胶原料：聚苯硫醚英文简写为PPS，是一种新型高性能热塑性树脂，具有机械强度高、耐高温、耐化学药品性、难燃、热稳定性好、电性能优良等优点。在电子、汽车、机械及化工领域均有广泛应用。
PPS是一种综合性能优异的特种工程塑料。PPS具有优良的耐高温、耐腐蚀、耐辐射、阻燃、均衡的物理机械性能和极好的尺寸稳定性以及优良的电性能等特点，被广泛用作结构性高分子材料，通过填充、改性后广泛用作特种工程塑料。同时，还可制成各种功能性的薄膜、涂层和复合材料，在电子电器、航空航天、汽车运输等领域获得成功应用。国内企业积极研发，并初步形成了一定的生产能力，改变了以往完全依赖进口的状况。但是，中国PPS技术还存在产品品种少、高功能产品少、产能急待扩大等问题，这些将是PPS下一步发展的重点。
PPS的特性如下：1：耐化学性能好。2：蠕变量低.3：吸水率低.4：尺寸稳定性好. 5：弹性模量高.6：·阻燃
（1）一般性能：PPS为一种外观白色，高结晶度、硬而脆的聚合物，纯PPS的相对密度为1.3，但改性后会增大。PPS吸水率极小，一般只有0.03%左右。PPS的阻燃性好，其氧指数高达44%以上，与其他塑料相比，它在塑料中属于高阻燃材料（纯PVA的氧指数为47%，PSF为30%，PA66为29%，MPPO为28%，PC为25%)。
（2）机械性能：纯PPS的机械性能不高，尤其冲击强度低。以玻璃纤维增强后会大幅度提高冲击强度，有27J/m,增大到76J/m，增大3倍：拉伸强度由6Mpa增大到 137Mpa，增大1倍。PPS的刚性很高。在工程材料少见。纯PPS的弯曲模量可达到3.8Gpa，无机填充改性后可到到12.6Gpa，增大5倍之多。而以刚性著称的PPO仅为2.55Gpa，PC仅为2.1Gpa。PPS在负荷下的耐蠕变性好；硬度高；耐磨性高，其1000转时的模量仅为0.04g，填充F4及二硫化钼后还会进一步得到改善；PPS还具有一定的自润性。PPS的机械性能对温度的敏感性能小。
（3）热学性能：PPS又有优异的热性能，短期可耐260℃，并可在200~240℃下长期使用；其耐性与PI相当，仅次于F4塑料，这是在热固性塑料中也不多见。
（4）电学性能：PPS的电性能十分突出，与其它工程材料相比，其介电常数与介电耗损角成切值都比较低，并且在较大的频率、温度及温度范围内变化不大；PPS的耐电弧好，可与热固性塑料媲美。PPS常用于电器绝缘材料，这在热固性材料中也不多见；其用量占30%左右。
（5）环境性能：PPS最大的特点之一为耐化学腐蚀性好，其化学稳定性仅次于F4：
PPS对大多酸。酯、铜、酚、及脂肪经、芳香经、氯代经等稳定，不耐氯代v 联苯及氧化性酸、氧化剂、浓硫酸、浓硝酸、王水、过氧化氢及次氯酸钠等。PPS耐辐射性好。
广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，,PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。