TRITAN GX100 Eastman Chemical Company 共聚多酯
TRITAN FX200 Eastman Chemical Company 共聚多酯
TRITAN LX151HF Eastman Chemical Company 共聚多酯
TRITAN LX101 Eastman Chemical Company 共聚多酯
TRITAN LX150HF Eastman Chemical Company 共聚多酯
TRITAN LX201 Eastman Chemical Company 共聚多酯
TRITAN FX100 Eastman Chemical Company 共聚多酯
TRITAN EX401 Eastman Chemical Company 共聚多酯
TRITAN LX500 Eastman Chemical Company 共聚多酯
TRITAN MX710 Eastman Chemical Company 共聚多酯
TRITAN TX1001 Eastman Chemical Company 共聚多酯
TRITAN TX1501HF Eastman Chemical Company 共聚多酯
TRITAN TX1500HF Eastman Chemical Company 共聚多酯
TRITAN TX1800 Eastman Chemical Company 共聚多酯
TRITAN TX1000 Eastman Chemical Company 共聚多酯
TRITAN MP100 Eastman Chemical Company 共聚多酯
Tritan? MP100 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.19 | g/cm3 | ASTM D1505 |
| 吸水率(23°C, 24 hr) | 0.50 | % | ASTM D570 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 耐磨耗性 (23°C)1 | 23% Haze | ASTM D1044 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C, 250.0 μm) | 150 | cm3·mm/m2/atm/24 hr | ASTM D1434 |
| PPT Tear Resistance | ASTM D2582 | ||
| MD : 23°C, 250.0 μm | 42 | N | ASTM D2582 |
| TD : 23°C, 250.0 μm | 56 | N | ASTM D2582 |
| 抗撕裂蔓延性 | ASTM D1938 | ||
| MD, Split Tear Method : 23°C, 250.0 μm | 410 | gf | ASTM D1938 |
| TD, Split Tear Method : 23°C, 250.0 μm | 310 | gf | ASTM D1938 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UV Transmittance2 | 89 | % |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Surface Energy - Polar (23°C) | 45 | dyne/cm | ASTM D5946 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 250 | μm | ASTM D374 |
| 弹性模量 - MD(250 μm) | 1460 | MPa | ASTM D882 |
| 弹性模量 - TD(250 μm) | 1380 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 250 μm | 41.0 | MPa | ASTM D882 |
| TD : 屈服, 250 μm | 40.0 | MPa | ASTM D882 |
| MD : 断裂, 250 μm | 59.0 | MPa | ASTM D882 |
| TD : 断裂, 250 μm | 52.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 屈服, 250 μm | 7.0 | % | ASTM D882 |
| TD : 屈服, 250 μm | 7.0 | % | ASTM D882 |
| MD : 断裂, 250 μm | 180 | % | ASTM D882 |
| TD : 断裂, 250 μm | 200 | % | ASTM D882 |
| 落锤冲击3 | ASTM D1709A | ||
| -30°C, 250 μm | 910 | g | ASTM D1709A |
| -18°C, 250 μm | 870 | g | ASTM D1709A |
| 23°C, 250 μm | 880 | g | ASTM D1709A |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 250 μm | 520 | g | ASTM D1922 |
| TD : 250 μm | 580 | g | ASTM D1922 |
| 裤型撕裂耐性4 | ISO 6383-1 | ||
| MD : 250 μm | 11.0 | N/mm | ISO 6383-1 |
| TD : 250 μm | 11.0 | N/mm | ISO 6383-1 |
| 透氧率(23°C, 250 μm, 50% RH) | 32 | cm3·mm/m2/atm/24 hr | ASTM D3985 |
| 水气透过率 | ASTM F1249 | ||
| 23°C, 100% RH, 250 μm | 4.0 | g/m2/24 hr | ASTM F1249 |
| 38°C, 100% RH, 250 μm | 11 | g/m2/24 hr | ASTM F1249 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 装有测量仪表的落镖冲击(23°C, Total Energy) | 4.60 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | -60.0 | °C | ASTM D746 |
| 玻璃转化温度 | 110 | °C | DSC |
| 线形热膨胀系数 - 流动(23°C) | 8.8E-5 | cm/cm/°C | ASTM D696 |
| 比热 | DSC | ||
| 60°C | 1710 | J/kg/°C | DSC |
| 100°C | 1890 | J/kg/°C | DSC |
| 150°C | 2250 | J/kg/°C | DSC |
| 200°C | 2400 | J/kg/°C | DSC |
| 250°C | 2570 | J/kg/°C | DSC |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度(60°, 250 μm) | 161 | ASTM D2457 | |
| 折射率 | 1.545 | ASTM D542 | |
| 透射率(总计, 250 μm) | 92.0 | % | ASTM D1003 |
| 雾度(250 μm) | 1.0 | % | ASTM D1003 |
| 备注 | |
|---|---|
| 1 . | 25 cycles |
| 2 . | UV/Vis Spectro, 380 nm |
| 3 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 4 . | 200 mm/min |