东莞市广裕塑胶原料有限公司
35%长纤增强 PA6 PX06418 沙伯基础
SABIC Innovative Plastics LNP VERTON PX06418 PA 6
Polymer,Thermoplastic,Nylon,Nylon 6
SABIC Innovative Plastics (GE Plastics)
产品说明:
LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural.
SABIC Innovative Plastics LNP VERTON PX06418 PA 6 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| 密度 | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| 水分吸收 | 1.10 % | 1.10 % | 50% RH, 24 hrs; ASTM D570 |
| 1.70 % | 1.70 % | 23°C / 50% RH; ISO 62 | |
| 线性成型收缩率,Flow | 0.0010 - 0.0030 cm/cm
@Time 86400 sec
|
0.0010 - 0.0030 in/in
@Time 24.0 hour
|
ASTM D955 |
| 线性成型收缩率，横向 | 0.0040 - 0.0060 cm/cm
@Time 86400 sec
|
0.0040 - 0.0060 in/in
@Time 24.0 hour
|
ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 182 MPa | 26400 psi | 5 mm/min; ISO 527 |
| 203 MPa | 29400 psi | Type I, 5 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 193 MPa | 28000 psi | 5 mm/min; ISO 527 |
| 伸长率 (断裂) | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| 拉伸模量 | 10.9 GPa | 1580 ksi | 1 mm/min; ISO 527 |
| 11.96 GPa | 1735 ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | 290 MPa | 42100 psi | ISO 178 |
| 307 MPa | 44500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 309 MPa | 44800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 9.53 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| 10.0 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 2.84 J/cm | 5.32 ft-lb/in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 10.4 J/cm | 19.5 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 27.0 kJ/m2 | 12.8 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 64.0 kJ/m2 | 30.5 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 落锤总能量 | 15.0 J
@Temperature 23.0 °C
|
11.1 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| 冲击试验 | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 47.7 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
26.5 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
ASTM D696 |
| 线性热膨胀系数,横向流动 | 114 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
63.3 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
ASTM D696 |
| 载荷下热变形温度(0.46 MPa) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C
@Thickness 3.20 mm
|
415 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C
@Thickness 3.20 mm
|
406 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |