东莞市崀峰塑胶原料有限公司
Eastar GN007, Natural
乙二醇改性 - 聚对苯二甲酸乙二醇酯
Eastman Chemical Company
产品说明：
Eastar? GN007 Copolyester is a water-clear glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar? GN007 copolyester will not crystallize and thus offers wider processing latitude than conventional crystallizable polyesters. This material offers an excellent combination of clarity, toughness, and melt strength that makes it useful for a variety of processing techniques and end-use applications.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED?.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED?.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED? Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman? Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
Eastar GN007, Natural 物性表
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.27 | g/cm3 | ASTM D792 |
| 收缩率 - 流动(3.20 mm) | 0.20 到 0.50 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度(R 级, 23°C) | 108 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| 23°C | 2030 | MPa | ASTM D638 |
| 23°C | 2000 | MPa | ISO 527-2 |
| 抗张强度 | |||
| 屈服, 23°C | 50.0 | MPa | ASTM D638 |
| 屈服, 23°C | 48.0 | MPa | ISO 527-2 |
| 断裂, 23°C | 30.0 | MPa | ASTM D638 |
| 断裂, 23°C | 29.0 | MPa | ISO 527-2 |
| 伸长率 | |||
| 屈服, 23°C | 4.4 | % | ASTM D638 |
| 屈服, 23°C | 4.0 | % | ISO 527-2 |
| 断裂, 23°C | 180 | % | ASTM D638 |
| 断裂, 23°C | 200 | % | ISO 527-2 |
| 弯曲模量 | |||
| 23°C | 2060 | MPa | ASTM D790 |
| 23°C | 2100 | MPa | ISO 178 |
| 弯曲强度 | |||
| 23°C | 68.0 | MPa | ASTM D790 |
| 23°C | 67.0 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | |||
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -40°C | 4.4 | kJ/m2 | ISO 180 |
| 23°C | 9.4 | kJ/m2 | ISO 180 |
| 无缺口悬臂梁冲击 | ASTM D4218 | ||
| -40°C | 无断裂 | ASTM D4218 | |
| 23°C | 无断裂 | ASTM D4218 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火 | 70.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, 未退火 | 62.0 | °C | ASTM D648, ISO 75-2/A |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 透射率(总计) | 90.0 | % | ASTM D1003 |
| 雾度 | 0.20 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 71.0 | °C | |
| 干燥时间 | 6.0 | hr | |
| 加工（熔体）温度 | 249 到 271 | °C | |
| 模具温度 | 16.0 到 38.0 | °C |