Fortron 1140E7
聚苯硫醚
40% 玻璃纤维增强材料
产品说明：
Fortron 1140E7 is an inherently flame-retardant grade exhibiting extremely low flash and fast cycle times. It has excellent electrical properties, high hardness and stiffness. This grade exhibits good high-temperature load-bearing capabilities. It is especially used for thinner walled and longer flow length parts requiring low flash behavior. Good weldability due to a modest filler level. Commonly used in electrical connectors and other thin wall/long flow length parts.
Fortron 1140E7 物性表
| 基本信息 |
|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 特性 |
- 刚性，高
- 可焊接
- 快的成型周期
- 良好的电气性能
- 耐热性，高
- 硬度高
- 阻燃性
|
| 用途 |
|
| RoHS 合规性 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
|
|
|
| -- |
1.60 |
g/cm3 |
ASTM D792 |
| -- |
1.65 |
g/cm3 |
ISO 1183 |
| 特定体积 |
0.611 |
cm3/g |
ASTM D792 |
| 补充信息 |
额定值 |
单位制 |
测试方法 |
| Specimen Thickness - Shrinkage |
3.18 |
mm |
内部方法 |
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 收缩率 |
|
|
|
| 流动 |
0.20 到 0.30 |
% |
ASTM D955 |
| 横向流动 |
0.50 到 0.70 |
% |
ASTM D955 |
| 垂直流动方向 |
0.40 到 0.60 |
% |
ISO 294-4 |
| 流动方向 |
0.20 到 0.60 |
% |
ISO 294-4 |
| 吸水率(饱和, 23°C) |
0.020 |
% |
ISO 62 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 |
|
|
|
| M 级 |
103 |
|
ASTM D785 |
| M 计秤 |
100 |
|
ISO 2039-2 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
15700 |
MPa |
ISO 527-2/1A/1 |
| 抗张强度 |
|
|
|
| 断裂, 23°C |
152 |
MPa |
ASTM D638 |
| 断裂 |
150 |
MPa |
ISO 527-2/1A/5 |
| 伸长率 |
|
|
|
| 断裂, 23°C |
1.4 |
% |
ASTM D638 |
| 断裂 |
1.2 |
% |
ISO 527-2/1A/5 |
| 弯曲模量(23°C) |
15000 |
MPa |
ISO 178 |
| 弯曲应力1 |
230 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179/1eA |
| -30°C |
7.0 |
kJ/m2 |
ISO 179/1eA |
| 23°C |
7.0 |
kJ/m2 |
ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
|
ISO 179/1eU |
| -30°C |
28 |
kJ/m2 |
ISO 179/1eU |
| 23°C |
28 |
kJ/m2 |
ISO 179/1eU |
| 悬壁梁缺口冲击强度 |
|
|
ISO 180/1A |
| -30°C |
7.0 |
kJ/m2 |
ISO 180/1A |
| 23°C |
7.0 |
kJ/m2 |
ISO 180/1A |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 退火 |
280 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
270 |
°C |
ASTM D648, ISO 75-2/A |
| 8.0 MPa, 未退火 |
215 |
°C |
ISO 75-2/C |
| 玻璃转化温度2 |
90.0 |
°C |
ISO 11357-2 |
| 熔融温度 |
|
|
|
| --3 |
280 |
°C |
ISO 11357-3 |
| -- |
282 |
°C |
ASTM D3418 |
| 线形热膨胀系数 |
|
|
ISO 11359-2 |
| 流动 |
2.0E-5 |
cm/cm/°C |
ISO 11359-2 |
| 横向 |
4.1E-5 |
cm/cm/°C |
ISO 11359-2 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+15 |
ohms |
IEC 60093 |
| 体积电阻率 |
|
|
|
| -- |
1.0E+17 |
ohms·cm |
ASTM D257 |
| -- |
1.0E+15 |
ohms·cm |
IEC 60093 |
| 介电强度 |
25 |
kV/mm |
IEC 60243-1 |
| 介电常数 |
|
|
|
| 1 kHz |
3.70 |
|
ASTM D150 |
| 1 MHz |
3.70 |
|
ASTM D150 |
| 1 MHz |
4.70 |
|
IEC 60250 |
| 耗散因数 |
|
|
|
| 1 kHz |
1.0E-3 |
|
ASTM D150 |
| 1 MHz |
1.0E-3 |
|
ASTM D150 |
| 1 MHz |
0.020 |
|
IEC 60250 |
| 耐电弧性 |
134 |
sec |
ASTM D495 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 0.850 mm |
V-0 |
|
UL 94 |
| 1.50 mm |
V-0 |
|
UL 94 |
| 极限氧指数 |
47 |
% |
ASTM D2863, ISO 4589-2 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
130 到 140 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 建议的最大水分含量 |
0.020 |
% |
|
| 料斗温度 |
20.0 到 30.0 |
°C |
|
| 料筒后部温度 |
290 到 300 |
°C |
|
| 料筒中部温度 |
310 到 320 |
°C |
|
| 料筒前部温度 |
330 到 340 |
°C |
|
| 射嘴温度 |
310 到 330 |
°C |
|
| 加工（熔体）温度 |
330 到 340 |
°C |
|
| 模具温度 |
140 到 160 |
°C |
|
| 注塑压力 |
50.0 到 100 |
MPa |
|
| 注射速度 |
快速 |
|
|
| 保压 |
30.0 到 70.0 |
MPa |
|
| 背压 |
0.00 到 3.00 |
MPa |
|
| 注射说明 |
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| 备注 |
| 1 . |
Break |
| 2 . |
10°C/min |
| 3 . |
10°C/min |
?FORTRON 1140E7 Celanese Corporation PPS
FORTRON 1115E7 Celanese Corporation PPS
FORTRON 1132L4 Celanese Corporation PPS
FORTRON 1140L4-T Celanese Corporation PPS
FORTRON ICE 506L Celanese Corporation PPS