东莞市崀峰塑胶原料有限公司
SABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer
Polymer,Thermoplastic,Acetal (POM),Acetal Copolymer, Unreinforced
SABIC Innovative Plastics (GE Plastics)
产品说明:
LNP LUBRICOMP* KL004XXC is a compound based on Acetal Copolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
ABIC Innovative Plastics LNP LUBRICOMP KL004XXC Acetal Copolymer 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.50 g/cc | 0.0542 lb/in3 | ASTM D792 |
| 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 | |
| 水分吸收 | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| 线性模具收缩，Flow | 0.0197 - 0.025 cm/cm
@Time 86400 sec
|
0.0197 - 0.025 in/in
@Time 24.0 hour
|
ASTM D955 |
| 0.0197 - 0.025 cm/cm
@Time 86400 sec
|
0.0197 - 0.025 in/in
@Time 24.0 hour
|
ISO 294 | |
| 线性成型收缩率,横向 | 0.0197 - 0.025 cm/cm
@Time 86400 sec
|
0.0197 - 0.025 in/in
@Time 24.0 hour
|
ASTM D955 |
| 0.0197 - 0.025 cm/cm
@Time 86400 sec
|
0.0197 - 0.025 in/in
@Time 24.0 hour
|
ISO 294 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 46.0 MPa | 6670 psi | ISO 527 |
| 50.0 MPa | 7250 psi | ASTM D638 | |
| 抗张强度(屈服) | 47.0 MPa | 6820 psi | ISO 527 |
| 51.0 MPa | 7400 psi | ASTM D638 | |
| 伸长率 (断裂) | 17.9 % | 17.9 % | ASTM D638 |
| 22.7 % | 22.7 % | ISO 527 | |
| 屈服伸长率 | 9.6 % | 9.6 % | ISO 527 |
| 11.2 % | 11.2 % | ASTM D638 | |
| 拉伸模量 | 2.13 GPa | 309 ksi | 50 mm/min; ASTM D638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 75.0 MPa | 10900 psi | ASTM D790 |
| 79.0 MPa | 11500 psi | ISO 178 | |
| 弯曲模量 | 2.06 GPa | 299 ksi | ASTM D790 |
| 2.60 GPa | 377 ksi | ISO 178 | |
| 悬壁梁缺口冲击强度 | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 6.51 J/cm | 12.2 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 落锤总能量 | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 动态摩擦系数 | 0.30 | 0.30 | ASTM D3702 Modified |
| 静态摩擦系数 | 0.18 | 0.18 | ASTM D3702 Modified |
| K (wear) Factor | 20.1 x 10-8mm3/N-M | 10.0 x 10-10in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 110 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
61.1 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 110 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
61.1 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 111 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
61.7 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 111 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
61.7 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | 157 °C
@Thickness 3.20 mm
|
315 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C
@Thickness 3.20 mm
|
210 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |