东莞市崀峰塑胶原料有限公司
Hostaform C 9021 G
聚甲醛（POM）共聚物
Celanese Corporation
产品说明：
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNS, 02-002
POM copolymer
Injection molding type with (R) GUR (PE-UHMW) modified; good
chemical resistance to solvents, fuel and strong alkalis as well as
good hydrolysis resistance; high resistance to thermal and oxidative
degradation.
Burning rate ISO 3795 and FMVSS 302 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: for parts under abrasion stress.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Molding compound ISO 9988- POM-K, M-GNS, 02-002
POM copolymer
Injection molding type with (R) GUR (PE-UHMW) modified; good
chemical resistance to solvents, fuel and strong alkalis as well as
good hydrolysis resistance; high resistance to thermal and oxidative
degradation.
Burning rate ISO 3795 and FMVSS 302 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: for parts under abrasion stress.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Hostaform C 9021 G 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 多点数据 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.34 | g/cm3 | ISO 1183 |
| 溶化体积流率（MVR）(190°C/2.16 kg) | 5.50 | cm3/10min | ISO 1133 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.8 | % | ISO 294-4 |
| 流动方向 | 2.3 | % | ISO 294-4 |
| 吸水率(饱和, 23°C) | 0.80 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2300 | MPa | ISO 527-2/1A/1 |
| 拉伸应力(屈服) | 45.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变(屈服) | 9.0 | % | ISO 527-2/1A/50 |
| 标称拉伸断裂应变 | 10 | % | ISO 527-2/1A/50 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 2000 | MPa | ISO 899-1 |
| 1000 hr | 1300 | MPa | ISO 899-1 |
| 弯曲模量(23°C) | 2100 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m2 | ISO 179/1eA |
| 23°C | 3.5 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| -30°C | 30 | kJ/m2 | ISO 179/1eU |
| 23°C | 30 | kJ/m2 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度(1.8 MPa, 未退火) | 88.0 | °C | ISO 75-2/A |
| 熔融温度1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 - 流动 | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度 | 35 | kV/mm | IEC 60243-1 |
| 相对电容率 | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.80 | IEC 60250 | |
| 耗散因数 | IEC 60250 | ||
| 100 Hz | 2.5E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 | |
| 漏电起痕指数 | 600 | V | IEC 60112 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 100 到 120 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 料斗温度 | 20.0 到 30.0 | °C | |
| 料筒后部温度 | 170 到 180 | °C | |
| 料筒中部温度 | 180 到 190 | °C | |
| 料筒前部温度 | 190 到 200 | °C | |
| 射嘴温度 | 190 到 210 | °C | |
| 加工（熔体）温度 | 190 到 210 | °C | |
| 模具温度 | 80.0 到 120 | °C | |
| 注塑压力 | 60.0 到 120 | MPa | |
| 注射速度 | 慢 | ||
| 保压 | 60.0 到 120 | MPa | |
| 背压 | 0.00 到 2.00 | MPa |
POM美国杜邦
DELRIN 500AF 聚甲醛（POM）均聚物
DELRIN 100AF 聚甲醛（POM）均聚物
DELRIN FG511DP NC010 聚甲醛（POM）均聚物
DELRIN FG500P NC010D 聚甲醛（POM）均聚物
DELRIN FG900P NC010 聚甲醛（POM）均聚物
DELRIN PC652 NC010 聚甲醛（POM）均聚物
DELRIN FG100P NC010 聚甲醛（POM）均聚物
尼龙6T三井
ARLEN E630N Mitsui Chemicals, Inc.尼龙 6T
ARLEN E440NK Mitsui Chemicals, Inc.尼龙 6T
ARLEN G335 Mitsui Chemicals America, Inc.尼龙 6T
ARLEN A350 Mitsui Chemicals America, Inc.尼龙 6T
ARLEN A315 Mitsui Chemicals America, Inc.尼龙 6T