PARA IXEF FC-1022 产品说明:
Ixef? FC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.
Ixef? FC-1022 is approved for food contact and meets FDA regulations for Ixef? FC-1022 NT 000 (natural) and Ixef? FC-1022 BK 000 (black) based on clearances granted by FCN 001242 for repeated use food contact applications with all food types, under FDA conditions of use B through H as described in Tables 1 and 2 of 21 CFR 176.170(c).
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
密度 | 1.64 | -- | g/cm3 | ISO 1183 |
收缩率 | 0.10 到 0.30 | -- | % | ISO 294-4 |
吸水率(23°C, 24 hr) | 0.16 | -- | % | ISO 62 |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
拉伸模量 | 19500 | 19500 | MPa | ISO 527-2 |
拉伸应力(断裂) | 280 | 260 | MPa | ISO 527-2 |
拉伸应变(断裂) | 1.9 | 2.2 | % | ISO 527-2 |
弯曲模量 | 18500 | -- | MPa | ISO 178 |
弯曲应力 | 380 | -- | MPa | ISO 178 |
PARA IXEF FC-1022
主要生产方法
1.树脂生产
以对氨基苯甲酸为单位、N-甲基吡咯烷酮为溶剂,在催化剂、助催化剂存在和80~90℃的条件下,反应3小时。然后,将物料沉析到酒精中,用水洗涤树脂,干燥,即可得到纺丝用树脂。树脂的特性粘度控制在1.8~2.2范围内。
2.液晶浆液的制备
将芳纶-I树脂溶解在含有4~6%助溶剂的有机溶剂(二甲基乙酰胺或N-甲基吡咯烷酮)中,聚合物浓度控制在9~10%左右,即可得到光学上各向异性的液晶浆液。
3.湿法纺丝
将上述液晶浆液过滤,置于贮料筒中脱泡24小时,纺丝液经纺丝计量泵计量后,再经过滤器送至喷丝头,通过Φ0.05~0.08×500~1000孔纺丝帽,以每分钟10~20米的速度从喷丝孔喷入到凝固浴中。凝固浴为20~40%的有机溶剂水溶液,温度为40~50℃。从凝固出来的纤维经水充分洗净,干燥后,即得芳纶-I原丝。原丝在惰性气体中(3~5升/分,500~550℃)热处理3~5秒,即得到芳纶-I纤维。
PARA IXEF FC-1022 我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
我司供应其它品牌原料:
通用型塑胶原料种类如下:
ABS ABS高胶粉 ADPOLY AS(SAN) CA CAB EAA EVA GPPS HDPE HIPS LDPE LLDPE MBS MDPE MS MVLDPE(茂金属) PP PVC ULDPE
工程塑胶原料种类如下:
PA (尼龙)类 : 包括PA6 PA66 PA12 PA11 PA612 PA610 PA46
高耐温材料 :LCP PEEK PEI PPA PTFE PVDF
合金类: PA ABS PC ABS PA PTFE POM PTFE PC/TPFE PBT/ABS PBT/ASA PBT/F/PTFE PBT/PC PBT/PET
高刚性材料类: POM 以有 POM加各种填充合金
热塑弹性体: BR EMA CPE OBCs POE PBE POP SBR SBS SEBS SURLYN SIS SSBR TPE TPEE TPO TPR TPSIV TPU TPV TPX