东莞市广裕塑胶原料有限公司
沙伯基础创新PBT DR51M 15%玻纤增强 高刚性 耐高温
SABIC Innovative Plastics Valox? DR51M PBT (Asia Pacific)
Polymer,Thermoplastic,Polyester, TP,Polybutylene Terephthalate (PBT)
SABIC Innovative Plastics (GE Plastics)
产品说明:
15% GR; exc. mechanical/thermal/electrical performance; nonflame retardant. For spotlights, appliance housings, handles. Easy flow/int. mold release.
This data was supplied by SABIC-IP for the Asia Pacific region.
15% GR; exc. mechanical/thermal/electrical performance; nonflame retardant. For spotlights, appliance housings, handles. Easy flow/int. mold release.
This data was supplied by SABIC-IP for the Asia Pacific region.
SABIC Innovative Plastics Valox? DR51M PBT (Asia Pacific) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.41 g/cc | 1.41 g/cc | ASTM D 792 |
| 吸水率 | 0.070 %
@Time 86400 sec
|
0.070 %
@Time 24.0 hour
|
ASTM D 570 |
| 线性模具收缩，Flow | 0.0040 - 0.0060 cm/cm
@Thickness 1.50 - 3.20 mm
|
0.0040 - 0.0060 in/in
@Thickness 0.0591 - 0.126 in
|
SABIC Method |
| 0.0060 - 0.0090 cm/cm
@Thickness 3.20 - 4.60 mm
|
0.0060 - 0.0090 in/in
@Thickness 0.126 - 0.181 in
|
SABIC Method | |
| 线性成型收缩率,横向 | 0.0050 - 0.0080 cm/cm
@Thickness 1.50 - 3.20 mm
|
0.0050 - 0.0080 in/in
@Thickness 0.0591 - 0.126 in
|
SABIC Method |
| 0.0080 - 0.011 cm/cm
@Thickness 3.20 - 4.60 mm
|
0.0080 - 0.011 in/in
@Thickness 0.126 - 0.181 in
|
SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 118 | 118 | ASTM D 785 |
| 抗张强度(断裂) | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D 638 |
| 伸长率 (断裂) | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D 638 |
| 弯曲强度 | 144 MPa | 20900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 弯曲模量 | 4.82 GPa | 699 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 悬壁梁缺口冲击强度 | 0.530 J/cm
@Temperature 23.0 °C
|
0.993 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 |
| 悬壁梁无缺口冲击强度 | 5.34 J/cm
@Temperature 23.0 °C
|
10.0 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 4812 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 3.30e+16 ohm-cm | 3.30e+16 ohm-cm | ASTM D 257 |
| 介电常数 | 3.4
@Frequency 1.00e+6 Hz
|
3.4
@Frequency 1.00e+6 Hz
|
ASTM D 150 |
| 3.6
@Frequency 100 Hz
|
3.6
@Frequency 100 Hz
|
ASTM D 150 | |
| 介电强度 | 19.6 kV/mm
@Thickness 3.20 mm
|
498 kV/in
@Thickness 0.126 in
|
in air; ASTM D 149 |
| 23.2 kV/mm
@Thickness 1.60 mm
|
589 kV/in
@Thickness 0.0630 in
|
in oil; ASTM D 149 | |
| 耗散因数 | 0.0020
@Frequency 100 Hz
|
0.0020
@Frequency 100 Hz
|
ASTM D 150 |
| 0.020
@Frequency 1.00e+6 Hz
|
0.020
@Frequency 1.00e+6 Hz
|
ASTM D 150 | |
| 耐电弧性 | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| 相比耐漏电起痕指数(CTI) | 250 - 400 V | 250 - 400 V | PLC code 2; UL 746A |
| 高压电弧跟踪率，HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | PLC code 1; UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 21.6 μm/m-°C
@Temperature 60.0 - 138 °C
|
12.0 μin/in-°F
@Temperature 140 - 280 °F
|
ASTM E 831 |
| 21.6 μm/m-°C
@Temperature -40.0 - 95.0 °C
|
12.0 μin/in-°F
@Temperature -40.0 - 203 °F
|
ASTM E 831 | |
| 载荷下热变形温度(0.46 MPa) | 210 °C
@Thickness 6.40 mm
|
410 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 |
| 载荷下热变形温度(1.8 MPa) | 190 °C
@Thickness 6.40 mm
|
374 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 |
| UL RTI | 130 °C | 266 °F | UL 746B |
| UL RTI，机械冲击 | 130 °C | 266 °F | UL 746B |
| UL RTI，机械无冲击 | 140 °C | 284 °F | UL 746B |
| 可燃性(UL94) | HB
@Thickness 0.710 mm
|
HB
@Thickness 0.0280 in
|
UL 94 |
PBT塑料是指聚对苯二甲酸丁二醇酯为主体所构成的一类塑料
聚对苯二甲酸丁二醇酯（Polybutylene terephthalate），又名聚对苯二甲酸四次甲基酯。简称PBT。它是对苯二甲酸与1,4-丁二醇的缩聚物。PBT和PET一起被称为热塑性聚酯。
聚对苯二甲酸丁二醇酯（Polybutylene terephthalate），又名聚对苯二甲酸四次甲基酯。简称PBT。它是对苯二甲酸与1,4-丁二醇的缩聚物。PBT和PET一起被称为热塑性聚酯。
特性编辑
a、机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；
b、耐热老化性：增强后的UL温度指数达120~140℃（户外长期老化性也很好）；
c、耐溶剂性：无应力开裂；
d、对水稳定性：PBT遇水不易分解；
e、电气性能：
1、绝缘性能：优良（潮湿、高温也能保持电性能稳定,是制造电子、电气零件的理想材料）；
2、介电系数：3.0-3.2；
3、耐电弧性：120s
f、成型加工性：普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程塑料要求低。在加工薄壁制件时，仅需几秒钟，对大部件也只要40-60s即可。
2、PBT的应用（通常指改性品种）；
a、电子电器：连接器、开关零件、家用电器、配件零件、小型电动罩盖或（耐热性、阻燃性、电气绝缘性、成型加工性）；
b、汽车：
1、外装零件：主要有转角格珊、发动机放热孔罩等；
2、内部零部件：主要有内镜撑条、刮水器支架和控制系统阀；
3、汽车电器零件：汽车点火线圈绞管和各种电器连接器等。
（PBT用于汽车上的数目还不及尼龙、聚碳和聚甲醛，但随着低翘曲性PBT的出现，今后必将在汽车零部件上得到更多的应用）
c、机械设备：视频磁带录音机的带式传动轴、电子计算机罩、水银灯罩、电熨斗罩、烘烤机零件以及大量的齿轮、凸轮、按钮、电子表外壳、照相机的零件（有耐热、阻燃要求）
三、PBT塑料的粘接：
根据不同需要，可以选择以下粘合剂：
1. TG-3200：单组分常温固化软弹性防震粘合剂，耐高低温，但粘接速度慢，胶水通常要1天或几天时间才能固化完毕。
2. TS-8602瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PBT，但胶层硬脆，不耐水。
3. TE-9270类，双组分胶，胶层柔软，适合PBT大面积粘接或复合。但耐高温性能较差。
4.TE-9249类胶：双组分胶，耐高温。
5.sili-1706:单组份室温硫化胶，固化后是弹性体具有优秀的防水，防震粘合剂，耐高低温， 1-2mm厚度的话，5-6小时基本固化，有一定的强度。完全固化的话需要至少24小时。单组份，不需要混合，挤出后涂抹静置即可，无需加温。
工艺特点编辑
PBT注塑之前一定要在110～120℃的温度下干燥3小时左右，成型加工温度为250～270℃，模温控制在50～75℃为宜。因该料从熔融状态一经冷却，则会立即凝固结晶，故其冷却时间较短；若喷嘴温度控制不当（偏低），流道（水口）易冷却固化，会出现堵嘴现象。若料筒温度超过275℃或熔料在料筒中停留时间超过30分钟，易引起材料分解变脆。PBT注塑时需用较大水口进胶，不宜使用热流道系统，模具排气要良好，宜用“高速、中压、中温”的条件成型加工，防火料或加玻纤的PBT水口料不宜再回收利用，停机时需用PE或PP料及时清洗料管，以免碳化。