ABS MAGNUM 375 HH

Overview: High Heat, Low Gloss, Medium Impact ABS resin for injection molding

Applications:

• Automotive interior trim applications requiring low volatile organic compounds (VOC)

Automotive Specifications:

• CHRYSLER MS-DB-191
• CHRYSLER MS-DB-300
• VAG VW-TL 527
• VAG VW-TL 527 B
• VAG VW-TL 527 A

Physical Properties	Metric	English	Comments
Density	1.06g/cc	0.0383lb/in3	ASTM D792; ISO 1183/B
Linear Mold Shrinkage, Flow	0.0057cm/cm	0.0057in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0056cm/cm	0.0056in/in	ASTM D955
Melt Flow	2.1g/10 min @Load 3.80 kg, Temperature 230 °C	2.1g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	47.0MPa	6820psi	ISO 527-2
	49.0MPa	7110psi	51 mm/min; ASTM D638
Elongation at Break	3.5 %	3.5 %	ISO 527-2/50
	8.8 %	8.8 %	51 mm/min; ASTM D638
Elongation at Yield	2.9 %	2.9 %	ISO 527-2/50
	3.1 %	3.1 %	51 mm/min; ASTM D638

ABS MAGNUM 375 HH

ABS是一种综合性能十分良好的树脂，在比较宽广的温度范围内具有较高的冲击强度和表面硬度，热变形温度比PA、PVC高，尺寸稳定性好。

一般性能 ：

ABS的外观为不透明呈象牙色的粒料，无毒、无味、吸水率低其制品可着成各种颜色，并具有90%的高光泽度。ABS同其它材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18.2，属易燃聚合物，火焰呈黄色，有黑烟，烧焦但不滴落，并发出特殊的肉桂味。

（1）力学性能

ABS有优良的力学性能，其冲击强度较好，可以在极低的温度下使用。即使ABS制品被破坏，也只能是拉伸破坏而不会是冲击破坏。ABS的耐磨性能优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的蠕变性比PSF及PC大，但比PA和POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。

（2）热学性能

ABS属于无定形聚合物，无明显熔点；熔体粘度较高，流动性差，耐候性较差，紫外线可使变色；热变形温度为70—107℃（85左右），制品经退火处理后还可提高10℃左右。对温度，剪切速率都比较敏感；ABS在－40℃时仍能表现出一定的韧性，可在 -40℃到85℃的温度范围内长期使用。

应用：

1、汽车产业

汽车产业中有众多零件是用ABS或ABS合金制造的，如上海的桑塔纳轿车，每辆车用ABS11kg，位列汽车中所用塑料第三。在其它车辆中，ABS的使用量也颇惊人。2000年我国就汽车用ABS的量就达到3.5万吨。轿车中主要零部件使用ABS的如仪表板用PC/ABS作骨架，表面再复以PVC/ABS/BOVC制成的薄膜。此外，车内装饰件大量使用了ABS，如手套箱、杂物箱总成是用耐热ABS制成，门槛上下饰件、水箱面罩用ABS制成，另外还有很多零件采用ABS为原料。

2、办公室机器

由于ABS有高的光泽和易成型性，办公室设备机器需要有漂亮的外观，有良好的手感，如电话机外壳、存储器外壳以及计算机、传真机、复印机中都大量使用了ABS制作的零件。

3、家用电器

由于ABS有高的光泽和易成型性，所以在家电和小家电中更有着广泛的市场，如家用传真机、音响、VCD中也大量选用ABS为原料，吸尘器中也使用了很多ABS制作的零件，厨房用具也大量使用了ABS制作的零件。