POM HOSTAFORM S 27063 产品说明：

Chemical abbreviation according to ISO 1043-1: POM-HI,
Molding compound ISO 9988- POM-K, M-GNPR, 05-001

POM copolymer, modified

Easy flowing elastomer-containing injection molding type based on
HOSTAFORM C 27021; with higher impact strength and slightly lower
hardness, rigidity and chemical resistance than the basic type; high
resistance to thermal and oxidative degradation.

UL-registration in natural and a thickness more than 1.57 mm as UL
94 HB.

Burning rate ISO 3795 and FMVSS 302 100 mm/min for a thickness
more than 1 mm thickness.

Ranges of applications: For thin-walled molded parts with higher
energy-absorbing capacity

POM HOSTAFORM S 27063

POM用途

各种滑动、转动机械零件，做各种齿轮、杠杆、滑轮、链轮，特别适宜做轴承，热水阀门、精密计量阀、输送机的链环和辊子、流量计、汽车内外部把手、曲柄等车窗转动机械，油泵轴承座和叶轮燃气开关阀、电子开关零件、紧固体、接线柱镜面罩、电风扇零件、加热板、仪表钮 ；录音录像带的轴承 ；各种管道和农业喷灌系统以及阀门、喷头、水龙头、洗浴盆零件；开关键盘、按钮、音像带卷轴；温控定时器；动力工具，庭园整理工具零件；另外可作为冲浪板、帆船及各种雪撬零件，手表微型齿轮、体育用设备的框架辅件和背包用各种环扣、紧固件、打火机、拉链、扣环；医疗器械中的心脏起博器；人造心脏瓣膜、顶椎、假肢等

POM特点

（1）POM加工前可不用干燥,最好在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.

（2） POM的加工温度很窄(0～215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.

（3） POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;

（4） POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80～100℃),产品脱模时很烫,需防止烫伤手指.

（5） POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温

（6）具高机械强度和刚性

（7）最高的疲劳强度

（8）环境抵抗性、耐有机溶剂性佳

（9）耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优.

POM HOSTAFORM S 27063 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

物理性能	额定值	单位制	测试方法
密度	1.39	g/cm3	ISO 1183
溶化体积流率（MVR）(190°C/2.16 kg)	20.0	cm3/10min	ISO 1133
收缩率			ISO 294-4
垂直流动方向	1.8	%	ISO 294-4
流动方向	1.9	%	ISO 294-4
吸水率(饱和, 23°C)	0.65	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	2200	MPa	ISO 527-2/1A/1
拉伸应力(屈服)	54.0	MPa	ISO 527-2/1A/50
拉伸应变(屈服)	9.0	%	ISO 527-2/1A/50
标称拉伸断裂应变	30	%	ISO 527-2/1A/50
拉伸蠕变模量			ISO 899-1
1 hr	1850	MPa	ISO 899-1
1000 hr	1050	MPa	ISO 899-1
弯曲模量(23°C)	2100	MPa	ISO 178