Product TextsRubber modified (PC+SAN) blend10 % glass fiber filledinjection molding gradeoptimized heat ageing- and UV-stabilityvery good flowtensile modulus = 4800 MPahigh heat resistanceVicat/B 120 = 134 °C.
| 机械性能(机械性能(Mechanical properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据(ISO数据(CAMPUS/ISO) Data) | |||
| 拉伸模量(Tensile Modulus) | 4800 | MPa | ISO 527-1/-2 |
| 破坏时应变(Stress at break) | 95 | MPa | ISO 527-1/-2 |
| 破坏时应变(Strain at break) | 3.7 | % | ISO 527-1/-2 |
| 热性能(热性能(Thermal properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据(ISO数据(CAMPUS/ISO) Data) | |||
| 温度负荷变形(Temp. of deflection under load) (1.80 MPa) | 121 | °C | ISO 75-1/-2 |
| 温度负荷变形(Temp. of deflection under load) (0.45 MPa) | 133 | °C | ISO 75-1/-2 |
| 维卡软化温度（50℃/ h的50N）Vicat softening temperature | 132 | °C | ISO 306 |
| COEFF线性热(Coeff. of linear therm. expansion) (parallel) | 40 | E-6/K | ISO 11359-1/-2 |
| COEFF线性热(Coeff. of linear therm. expansion) (normal) | 67 | E-6/K | ISO 11359-1/-2 |
| 厚度测试(Thickness tested) | 1.5 | mm | IEC 60695-11-10 |
| 燃烧性(球压痕硬度(Burning behav)). at thickness h | HB | class | IEC 60695-11-10 |
| 厚度测试(Thickness tested) | 0.8 | mm | IEC 60695-11-10 |
| UL 识别(recognition) | UL | - | - |
| 电气性能(Electrical properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据(ISO数据(CAMPUS/ISO) Data) | |||
| 相对介电常数(Relative permittivity) (100Hz) | 3.2 | - | IEC 60250 |
| 相对介电常数(Relative permittivity) (1MHz) | 3 | - | IEC 60250 |
| 耗散因数(耗散因数(Dissipation factor)) (100Hz) | 25 | E-4 | IEC 60250 |
| 耗散因数(耗散因数(Dissipation factor)) (1MHz) | 90 | E-4 | IEC 60250 |
| 体积电阻率(Volume resistivity) | 1E13 | Ohm*m | IEC 60093 |
| 表面电阻率(Surface resistivity) | 1E15 | Ohm | IEC 60093 |
| 电气强度(Electric strength) | 35 | kV/mm | IEC 60243-1 |
| 相比漏电起痕指数(Comparative tracking index) | 200 | - | IEC 60112 |
| 其他属性(Other properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据(ISO数据(CAMPUS/ISO) Data) | |||
| 吸水率(Water absorption) | 0.4 | % | Sim. to ISO 62 |
| 吸湿性(Humidity absorption) | 0.2 | % | Sim. to ISO 62 |
| 密度(Density) | 1220 | kg/m3 | ISO 1183 |
| 流变计算属性(Rheological calculation properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据(ISO数据(CAMPUS/ISO) Data) | |||
| 密度(Density) of melt | 1050 | kg/m3 | - |
| 熔体热导率(Thermal conductivity of melt) | 0.207 | W/(m K) | - |
| 规格的热容融化(Spec. heat capacity of melt) | 1900 | J/(kg K) | - |
| Eff. thermal diffusivity | 1.04E-7 | m2/s | - |
| 喷射温度(Ejection temperature) | 130 | °C | - |
| Test specimen production | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据(ISO数据(CAMPUS/ISO) Data) | |||
| Injection Molding, melt temperature | 260 | °C | ISO 294 |
| Injection Molding, mold temperature | 80 | °C | ISO 10724 |
| Injection Molding, injection velocity | 240 | mm/s | ISO 294 |
Diagrams Water content: 0.02 %