美国杜邦PBT CE15315 15%玻纤增强 防火阻燃PBT
DuPont Performance Polymers Crastin? CE15315 NC010 PBT (Unverified Data**)
Polymer,Thermoplastic,Polyester, TP,Polybutylene Terephthalate (PBT),Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
DuPont Performance Polymers
产品说明:
Crastin? CE15315 NC010 is a 15% glass reinforced flame retardant polybutylene terephthalate molding resin. It is recognized as UL94 V-0 at 0.71mm(0.028in).
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Crastin? CE15315 NC010 PBT (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.499 g/cc | 0.05415 lb/in3 | ISO 1183 |
| 线性成型收缩率,Flow | 0.0030 - 0.0050 cm/cm
@Thickness 2.00 mm
|
0.0030 - 0.0050 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| 线性成型收缩率，横向 | 0.0050 - 0.0090 cm/cm
@Thickness 2.00 mm
|
0.0050 - 0.0090 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 101 MPa
@Temperature 23.0 °C
|
14600 psi
@Temperature 73.4 °F
|
ISO 527 |
| 伸长率 (断裂) | 3.1 %
@Temperature 23.0 °C
|
3.1 %
@Temperature 73.4 °F
|
ISO 527 |
| 拉伸模量 | 5.96 GPa
@Temperature 23.0 °C
|
864 ksi
@Temperature 73.4 °F
|
ISO 527 |
| 简支梁无缺口冲击强度 | 3.01 J/cm2
@Temperature -30.0 °C
|
14.3 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eU |
| 3.18 J/cm2
@Temperature 23.0 °C
|
15.1 ft-lb/in2
@Temperature 73.4 °F
|
ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.620 J/cm2
@Temperature -30.0 °C
|
2.95 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eA |
| 0.620 J/cm2
@Temperature 23.0 °C
|
2.95 ft-lb/in2
@Temperature 73.4 °F
|
ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 223 °C | 433 °F | 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(1.8 MPa) | 200 °C | 392 °F | ISO 75-1/-2 |
| UL RTI | 130 °C
@Thickness 0.710 mm
|
266 °F
@Thickness 0.0280 in
|
UL 746B |
| 130 °C
@Thickness 1.50 mm
|
266 °F
@Thickness 0.0591 in
|
UL 746B | |
| 130 °C
@Thickness 3.00 mm
|
266 °F
@Thickness 0.118 in
|
UL 746B | |
| UL RTI，机械冲击 | 110 °C
@Thickness 0.710 mm
|
230 °F
@Thickness 0.0280 in
|
UL 746B |
| 110 °C
@Thickness 1.50 mm
|
230 °F
@Thickness 0.0591 in
|
UL 746B | |
| 120 °C
@Thickness 3.00 mm
|
248 °F
@Thickness 0.118 in
|
UL 746B | |
| UL RTI，机械无冲击 | 130 °C
@Thickness 3.00 mm
|
266 °F
@Thickness 0.118 in
|
UL 746B |
| 130 °C
@Thickness 1.50 mm
|
266 °F
@Thickness 0.0591 in
|
UL 746B | |
| 130 °C
@Thickness 0.710 mm
|
266 °F
@Thickness 0.0280 in
|
UL 746B | |
| 可燃性(UL94) | V-0
@Thickness 3.00 mm
|
V-0
@Thickness 0.118 in
|
UL94 |
| V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
UL94 | |
| V-0
@Thickness 0.710 mm
|
V-0
@Thickness 0.0280 in
|
UL94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 250 °C | 482 °F | Optimum; Injection Molding |
| 240 - 260 °C | 464 - 500 °F | Injection Molding | |
| 模具温度 | 60.0 °C | 140 °F | optimum; Injection Molding |
| 10.0 - 110 °C | 50.0 - 230 °F | Injection Molding | |
| 干燥温度 | 100 - 140 °C | 212 - 284 °F | Injection Molding |
| 干燥时间 | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Injection Molding |
| 水分含量 | = 0.040 % | = 0.040 % | Injection Molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 形式 | Pellets | |
| Generic | PBT | |
| Material Status | Current | |
| 部件标识代码 | PBT-GF15FR(17) | ISO 11469 |
| 加工方法 | Injection Molding | |
| 产品分类 | Extrusion Resins | |
| Glass Reinforced Resins | ||
| 树脂识别 | PBT-GF15FR(17) | ISO 1043 |
聚对苯二甲酸丁二醇酯（Polybutylene terephthalate），又名聚对苯二甲酸四次甲基酯。简称PBT。它是对苯二甲酸与1,4-丁二醇的缩聚物。PBT和PET一起被称为热塑性聚酯。
a、机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；
b、耐热老化性：增强后的UL温度指数达120~140℃（户外长期老化性也很好）；
c、耐溶剂性：无应力开裂；
d、对水稳定性：PBT遇水不易分解；
e、电气性能：
1、绝缘性能：优良（潮湿、高温也能保持电性能稳定,是制造电子、电气零件的理想材料）；
2、介电系数：3.0-3.2；
3、耐电弧性：120s
f、成型加工性：普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程塑料要求低。在加工薄壁制件时，仅需几秒钟，对大部件也只要40-60s即可。
2、PBT的应用（通常指改性品种）；
a、电子电器：连接器、开关零件、家用电器、配件零件、小型电动罩盖或（耐热性、阻燃性、电气绝缘性、成型加工性）；
b、汽车：
1、外装零件：主要有转角格珊、发动机放热孔罩等；
2、内部零部件：主要有内镜撑条、刮水器支架和控制系统阀；
3、汽车电器零件：汽车点火线圈绞管和各种电器连接器等。
（PBT用于汽车上的数目还不及尼龙、聚碳和聚甲醛，但随着低翘曲性PBT的出现，今后必将在汽车零部件上得到更多的应用）
c、机械设备：视频磁带录音机的带式传动轴、电子计算机罩、水银灯罩、电熨斗罩、烘烤机零件以及大量的齿轮、凸轮、按钮、电子表外壳、照相机的零件（有耐热、阻燃要求）
三、PBT塑料的粘接：
根据不同需要，可以选择以下粘合剂：
1. TG-3200：单组分常温固化软弹性防震粘合剂，耐高低温，但粘接速度慢，胶水通常要1天或几天时间才能固化完毕。
2. TS-8602瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PBT，但胶层硬脆，不耐水。
3. TE-9270类，双组分胶，胶层柔软，适合PBT大面积粘接或复合。但耐高温性能较差。
4.TE-9249类胶：双组分胶，耐高温。
5.sili-1706:单组份室温硫化胶，固化后是弹性体具有优秀的防水，防震粘合剂，耐高低温， 1-2mm厚度的话，5-6小时基本固化，有一定的强度。完全固化的话需要至少24小时。单组份，不需要混合，挤出后涂抹静置即可，无需加温。
工艺特点编辑
PBT注塑之前一定要在110～120℃的温度下干燥3小时左右，成型加工温度为250～270℃，模温控制在50～75℃为宜。因该料从熔融状态一经冷却，则会立即凝固结晶，故其冷却时间较短；若喷嘴温度控制不当（偏低），流道（水口）易冷却固化，会出现堵嘴现象。若料筒温度超过275℃或熔料在料筒中停留时间超过30分钟，易引起材料分解变脆。PBT注塑时需用较大水口进胶，不宜使用热流道系统，模具排气要良好，宜用“高速、中压、中温”的条件成型加工，防火料或加玻纤的PBT水口料不宜再回收利用，停机时需用PE或PP料及时清洗料管，以免碳化。