美国杜邦PBT SK641FR 10%玻纤增强 卤素阻燃PBT
DuPont Performance Polymers Crastin? SK641FR NC010 Polybutylene Terephthalate (PBT)
Polymer,Thermoplastic,Polyester, TP,Polybutylene Terephthalate (PBT),Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
DuPont Performance Polymers
产品说明:
10% Glass Reinforced Flame Retardant Polybutylene Terephthalate
Information provided by DuPont Performance Polymers
10% Glass Reinforced Flame Retardant Polybutylene Terephthalate
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Crastin? SK641FR NC010 Polybutylene Terephthalate (PBT) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.54 g/cc | 0.0556 lb/in3 | ISO 1183 |
| 吸水率 | 0.35 %
@Thickness 2.00 mm
|
0.35 %
@Thickness 0.0787 in
|
Sim. to ISO 62 |
| 水分吸收 | 0.150 %
@Thickness 2.00 mm
|
0.150 %
@Thickness 0.0787 in
|
Sim. to ISO 62 |
| 线性成型收缩率,Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.013 cm/cm | 0.013 in/in | ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 93.0 MPa | 13500 psi | ISO 527-1/-2 |
| 抗张强度 | 3.73 MPa
@Strain 0.250 %, Temperature 160 °C
|
541 psi
@Strain 0.250 %, Temperature 320 °F
|
ISO 11403-1 -2 |
| 10.4 MPa
@Strain 0.250 %, Temperature 40.0 °C
|
1510 psi
@Strain 0.250 %, Temperature 104 °F
|
ISO 11403-1 -2 | |
| 12.5 MPa
@Strain 0.250 %, Temperature 23.0 °C
|
1810 psi
@Strain 0.250 %, Temperature 73.4 °F
|
ISO 11403-1 -2 | |
| 15.0 MPa
@Strain 0.250 %, Temperature 0.000 °C
|
2180 psi
@Strain 0.250 %, Temperature 32.0 °F
|
ISO 11403-1 -2 | |
| 15.5 MPa
@Strain 1.50 %, Temperature 160 °C
|
2250 psi
@Strain 1.50 %, Temperature 320 °F
|
ISO 11403-1 -2 | |
| 16.3 MPa
@Strain 0.250 %, Temperature -20.0 °C
|
2360 psi
@Strain 0.250 %, Temperature -4.00 °F
|
ISO 11403-1 -2 | |
| 17.0 MPa
@Strain 0.250 %, Temperature -40.0 °C
|
2470 psi
@Strain 0.250 %, Temperature -40.0 °F
|
ISO 11403-1 -2 | |
| 22.4 MPa
@Strain 3.00 %, Temperature 160 °C
|
3250 psi
@Strain 3.00 %, Temperature 320 °F
|
ISO 11403-1 -2 | |
| 49.4 MPa
@Strain 1.50 %, Temperature 40.0 °C
|
7160 psi
@Strain 1.50 %, Temperature 104 °F
|
ISO 11403-1 -2 | |
| 63.6 MPa
@Strain 3.00 %, Temperature 40.0 °C
|
9220 psi
@Strain 3.00 %, Temperature 104 °F
|
ISO 11403-1 -2 | |
| 63.6 MPa
@Strain 1.50 %, Temperature 23.0 °C
|
9220 psi
@Strain 1.50 %, Temperature 73.4 °F
|
ISO 11403-1 -2 | |
| 74.6 MPa
@Strain 1.50 %, Temperature 0.000 °C
|
10800 psi
@Strain 1.50 %, Temperature 32.0 °F
|
ISO 11403-1 -2 | |
| 79.6 MPa
@Strain 1.50 %, Temperature -20.0 °C
|
11500 psi
@Strain 1.50 %, Temperature -4.00 °F
|
ISO 11403-1 -2 | |
| 82.6 MPa
@Strain 1.50 %, Temperature -40.0 °C
|
12000 psi
@Strain 1.50 %, Temperature -40.0 °F
|
ISO 11403-1 -2 | |
| 84.8 MPa
@Strain 3.10 %, Temperature 23.0 °C
|
12300 psi
@Strain 3.10 %, Temperature 73.4 °F
|
ISO 11403-1 -2 | |
| 95.0 MPa
@Strain 2.80 %, Temperature 0.000 °C
|
13800 psi
@Strain 2.80 %, Temperature 32.0 °F
|
ISO 11403-1 -2 | |
| 105 MPa
@Strain 2.80 %, Temperature -20.0 °C
|
15200 psi
@Strain 2.80 %, Temperature -4.00 °F
|
ISO 11403-1 -2 | |
| 114 MPa
@Strain 2.80 %, Temperature -40.0 °C
|
16500 psi
@Strain 2.80 %, Temperature -40.0 °F
|
ISO 11403-1 -2 | |
| 伸长率 (断裂) | 3.6 % | 3.6 % | ISO 527-1/-2 |
| 拉伸模量 | 6.00 GPa | 870 ksi | ISO 527-1/-2 |
| 割线模量 | 1.05 GPa
@Strain 3.50 %, Temperature 100 °C
|
152 ksi
@Strain 3.50 %, Temperature 212 °F
|
ISO 11403-1 -2 |
| 1.20 GPa
@Strain 3.50 %, Temperature 80.0 °C
|
174 ksi
@Strain 3.50 %, Temperature 176 °F
|
ISO 11403-1 -2 | |
| 1.57 GPa
@Strain 1.50 %, Temperature 100 °C
|
227 ksi
@Strain 1.50 %, Temperature 212 °F
|
ISO 11403-1 -2 | |
| 1.76 GPa
@Strain 1.50 %, Temperature 80.0 °C
|
255 ksi
@Strain 1.50 %, Temperature 176 °F
|
ISO 11403-1 -2 | |
| 1.94 GPa
@Strain 3.30 %, Temperature 40.0 °C
|
281 ksi
@Strain 3.30 %, Temperature 104 °F
|
ISO 11403-1 -2 | |
| 2.06 GPa
@Strain 0.250 %, Temperature 100 °C
|
299 ksi
@Strain 0.250 %, Temperature 212 °F
|
ISO 11403-1 -2 | |
| 2.312 GPa
@Strain 0.250 %, Temperature 80.0 °C
|
335.3 ksi
@Strain 0.250 %, Temperature 176 °F
|
ISO 11403-1 -2 | |
| 3.29 GPa
@Strain 1.50 %, Temperature 40.0 °C
|
478 ksi
@Strain 1.50 %, Temperature 104 °F
|
ISO 11403-1 -2 | |
| 4.16 GPa
@Strain 0.250 %, Temperature 40.0 °C
|
603 ksi
@Strain 0.250 %, Temperature 104 °F
|
ISO 11403-1 -2 | |
| 4.24 GPa
@Strain 1.50 %, Temperature 23.0 °C
|
615 ksi
@Strain 1.50 %, Temperature 73.4 °F
|
ISO 11403-1 -2 | |
| 4.97 GPa
@Strain 1.50 %, Temperature 0.000 °C
|
721 ksi
@Strain 1.50 %, Temperature 32.0 °F
|
ISO 11403-1 -2 | |
| 5.00 GPa
@Strain 0.250 %, Temperature 23.0 °C
|
725 ksi
@Strain 0.250 %, Temperature 73.4 °F
|
ISO 11403-1 -2 | |
| 5.31 GPa
@Strain 1.50 %, Temperature -20.0 °C
|
770 ksi
@Strain 1.50 %, Temperature -4.00 °F
|
ISO 11403-1 -2 | |
| 5.51 GPa
@Strain 1.50 %, Temperature -40.0 °C
|
799 ksi
@Strain 1.50 %, Temperature -40.0 °F
|
ISO 11403-1 -2 | |
| 6.00 GPa
@Strain 0.250 %, Temperature 0.000 °C
|
870 ksi
@Strain 0.250 %, Temperature 32.0 °F
|
ISO 11403-1 -2 | |
| 6.52 GPa
@Strain 0.250 %, Temperature -20.0 °C
|
946 ksi
@Strain 0.250 %, Temperature -4.00 °F
|
ISO 11403-1 -2 | |
| 6.80 GPa
@Strain 0.250 %, Temperature -40.0 °C
|
986 ksi
@Strain 0.250 %, Temperature -40.0 °F
|
ISO 11403-1 -2 | |
| 简支梁无缺口冲击强度 | 5.10 J/cm2 | 24.3 ft-lb/in2 | ISO 179/1eU |
| 3.70 J/cm2
@Temperature -30.0 °C
|
17.6 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.650 J/cm2 | 3.09 ft-lb/in2 | ISO 179/1eA |
| 0.470 J/cm2
@Temperature -30.0 °C
|
2.24 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | 4600 MPa
@Time 3600 sec
|
667000 psi
@Time 1.00 hour
|
ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 3500 MPa
@Time 3.60e+6 sec
|
508000 psi
@Time 1000 hour
|
ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | = 1.00e+15 ohm-cm | = 1.00e+15 ohm-cm | IEC 60093 |
| 表面电阻 | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| 介电常数 | 3.6
@Frequency 100 Hz
|
3.6
@Frequency 100 Hz
|
IEC 60250 |
| 介电强度 | 26.0 kV/mm | 660 kV/in | IEC 60243-1 |
| 耗散因数 | 0.0030
@Frequency 100 Hz
|
0.0030
@Frequency 100 Hz
|
IEC 60250 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 60.0 μm/m-°C | 33.3 μin/in-°F | ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 110 μm/m-°C | 61.1 μin/in-°F | ISO 11359-1/-2 |
| 熔融温度 | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 215 °C | 419 °F | ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 200 °C | 392 °F | ISO 75-1/-2 |
| 可燃性(UL94) | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
IEC 60695-11-10 |
| V-0
@Thickness 0.800 mm
|
V-0
@Thickness 0.0315 in
|
IEC 60695-11-10 | |
| 极限氧指数 | 31 % | 31 % | ISO 4589-1/-2 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Delivery Form | Pellets | |
| 加工 | Injection Moulding | |
| 供货地区 | Europe | |
| Near East/Africa | ||
| UL recognition | UL |
PBT塑胶原料：
PBT塑料是指聚对苯二甲酸丁二醇酯为主体所构成的一类塑料
聚对苯二甲酸丁二醇酯（Polybutylene terephthalate），又名聚对苯二甲酸四次甲基酯。简称PBT。它是对苯二甲酸与1,4-丁二醇的缩聚物。PBT和PET一起被称为热塑性聚酯。
a、机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；
b、耐热老化性：增强后的UL温度指数达120~140℃（户外长期老化性也很好）；
c、耐溶剂性：无应力开裂；
d、对水稳定性：PBT遇水不易分解；
e、电气性能：
1、绝缘性能：优良（潮湿、高温也能保持电性能稳定,是制造电子、电气零件的理想材料）；
2、介电系数：3.0-3.2；
3、耐电弧性：120s
f、成型加工性：普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程塑料要求低。在加工薄壁制件时，仅需几秒钟，对大部件也只要40-60s即可。
2、PBT的应用（通常指改性品种）；
a、电子电器：连接器、开关零件、家用电器、配件零件、小型电动罩盖或（耐热性、阻燃性、电气绝缘性、成型加工性）；
b、汽车：
1、外装零件：主要有转角格珊、发动机放热孔罩等；
2、内部零部件：主要有内镜撑条、刮水器支架和控制系统阀；
3、汽车电器零件：汽车点火线圈绞管和各种电器连接器等。
（PBT用于汽车上的数目还不及尼龙、聚碳和聚甲醛，但随着低翘曲性PBT的出现，今后必将在汽车零部件上得到更多的应用）
c、机械设备：视频磁带录音机的带式传动轴、电子计算机罩、水银灯罩、电熨斗罩、烘烤机零件以及大量的齿轮、凸轮、按钮、电子表外壳、照相机的零件（有耐热、阻燃要求）
三、PBT塑料的粘接：
根据不同需要，可以选择以下粘合剂：
1. TG-3200：单组分常温固化软弹性防震粘合剂，耐高低温，但粘接速度慢，胶水通常要1天或几天时间才能固化完毕。
2. TS-8602瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PBT，但胶层硬脆，不耐水。
3. TE-9270类，双组分胶，胶层柔软，适合PBT大面积粘接或复合。但耐高温性能较差。
4.TE-9249类胶：双组分胶，耐高温。
5.sili-1706:单组份室温硫化胶，固化后是弹性体具有优秀的防水，防震粘合剂，耐高低温， 1-2mm厚度的话，5-6小时基本固化，有一定的强度。完全固化的话需要至少24小时。单组份，不需要混合，挤出后涂抹静置即可，无需加温。
工艺特点编辑
PBT注塑之前一定要在110～120℃的温度下干燥3小时左右，成型加工温度为250～270℃，模温控制在50～75℃为宜。因该料从熔融状态一经冷却，则会立即凝固结晶，故其冷却时间较短；若喷嘴温度控制不当（偏低），流道（水口）易冷却固化，会出现堵嘴现象。若料筒温度超过275℃或熔料在料筒中停留时间超过30分钟，易引起材料分解变脆。PBT注塑时需用较大水口进胶，不宜使用热流道系统，模具排气要良好，宜用“高速、中压、中温”的条件成型加工，防火料或加玻纤的PBT水口料不宜再回收利用，停机时需用PE或PP料及时清洗料管，以免碳化。