Tritan? WX500
共聚多酯
产品说明：
Eastman Tritan? WX500 is a resin specifically developed for blow molded bottles. Extremely high melt strength makes the resin an excellent choice when manufacturing large bottles. This new-generation copolyester most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan? WX500 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations.
| 基本信息 |
|
| 特性 |
- 抗撞击性，良好
- 可加工性，良好
- 良好的熔体强度
- 耐化学性良好
- 耐热性，高
- 清晰度，高
- 韧性良好
- 食品接触的合规性
- 水解稳定
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
- Injection Stretch Blow Molding
- 吹塑成型
- 挤出吹塑成型
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.18 |
g/cm3 |
ASTM D792 |
| 收缩率 - 流动 |
0.60 |
% |
ASTM D955 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度(R 级, 23°C) |
110 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| 23°C |
1610 |
MPa |
ASTM D638 |
| 23°C |
1570 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
| 屈服, 23°C |
45.0 |
MPa |
ASTM D638, ISO 527-2 |
| 断裂, 23°C |
52.0 |
MPa |
ASTM D638 |
| 断裂, 23°C |
51.0 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
ASTM D638, ISO 527-2 |
| 屈服, 23°C |
7.0 |
% |
ASTM D638, ISO 527-2 |
| 断裂, 23°C |
140 |
% |
ASTM D638, ISO 527-2 |
| 弯曲模量 |
|
|
|
| 23°C |
1520 |
MPa |
ASTM D790 |
| 23°C |
1490 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
|
| 23°C |
60.0 |
MPa |
ISO 178 |
| 屈服, 23°C |
64.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
|
| 23°C |
840 |
J/m |
ASTM D256 |
| -40°C |
12 |
kJ/m2 |
ISO 180 |
| 23°C |
78 |
kJ/m2 |
ISO 180 |
| 无缺口悬臂梁冲击(23°C) |
无断裂 |
|
ASTM D4812 |
| 装有测量仪表的落镖冲击 |
|
|
ASTM D3763 |
| -40°C, Energy at Peak Load |
67.0 |
J |
ASTM D3763 |
| 0°C, Energy at Peak Load |
65.0 |
J |
ASTM D3763 |
| 23°C, Energy at Peak Load |
62.0 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火 |
101 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
85.0 |
°C |
ASTM D648 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 透射率(总计) |
91.0 |
% |
ASTM D1003 |
| 雾度 |
1.0 |
% |
ASTM D1003 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
88.0 |
°C |
|
| 干燥时间 |
4.0 到 6.0 |
hr |
|
| 加工（熔体）温度 |
260 到 280 |
°C |
|
| 模具温度 |
40.0 到 65.0 |
°C |
|
| 注射说明 |
| ISBM Blow Mold Temperature: 35 to 55°C |
| 挤出 |
额定值 |
单位制 |
|
| 干燥温度 |
88.0 |
°C |
|
| 干燥时间 |
4.0 到 6.0 |
hr |
|
| 熔体温度 |
235 到 255 |
°C |
|
| 挤压说明 |
| EBM Blow Mold Temperature: 15 to 50°C |