KetaSpire? KT-820 SL30 is a polyetheretherketone (PEEK) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and externally lubricated applications. The resin is formulated with a ternary anti-friction/anti-wear additive system comprised of carbon fiber, graphite, and polytetrafluoroethylene (PTFE).

KetaSpire? PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases.

These properties make it well-suited for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production. The resin is black in color in its natural state.

东莞市崀峰是一般纳税人可以开13%税 ，主营: ABS、PC/ABS、PBT/ABS、PBT/ASA、PC/ASA、PC/PBT、PC/PTFE、POM/PTFE、POM/FEP、SAS、HDPE、LDPE、GPPS、HIPS(475) 、PP、PE、PPA、PFA、PVDF、PA、PMMA、POM、PC、PBT、PPO、PPS、LCP、TPU、TPR、TPV、TPEE、PTFE、TPE、PVC、K胶、PET、EVA、ASA、PSU、PPU、PUR、PA6T、PA46 PA9T 等高性能（耐高温）塑胶原料,13652520830,周先生:13423483121,Q:642774036,材料订购说明：提供物性、报价、UL报告、ROSH标准、SGS检测报告,本公司为华东地区长期经销代理韩国乐天化学公司秉承“以诚为本,信誉至上”的经营宗旨,【诚信经营 】【服务至上 】【品质保障 】创立了自己的经营理念.

基本信息
添加剂	碳素纤维 + 石墨 + PFTE 润滑剂
特性	尺寸稳定性良好 耐化学性良好 耐磨损性良好 耐疲劳性能 耐热性，高 阻燃性
用途	棒材 薄膜 衬套 齿轮 飞机应用 工业应用 管件 片材 型材 轴承
RoHS 合规性	联系制造商
外观	黑色
形式	粒子
加工方法	机器加工 型材挤出成型 注射成型

物理性能	额定值	单位制	测试方法
比重	1.45	g/cm3	ASTM D792
熔流率（熔体流动速率）(400°C/2.16 kg)	2.4	g/10 min	ASTM D1238
收缩率1			ASTM D955
流动 : 3.18 mm	0.10 到 0.30	%	ASTM D955
横向流动 : 3.18 mm	1.5 到 1.7	%	ASTM D955
吸水率(24 hr)	0.14	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度(M 级)	80		ASTM D785
肖氏硬度(邵氏 D, 1 秒)	86		ASTM D2240

机械性能	额定值	单位制	测试方法
拉伸模量
--2	11000	MPa	ASTM D638
--	14400	MPa	ISO 527-2/1A/1
拉伸应力
屈服	150	MPa	ISO 527-2/1A/5
--	133	MPa	ASTM D638
伸长率
断裂3	2.8	%	ASTM D638
断裂	2.8	%	ISO 527-2/1A/5
弯曲模量
--	10500	MPa	ASTM D790
--	14900	MPa	ISO 178
弯曲强度
--	221	MPa	ASTM D790
--	218	MPa	ISO 178
压缩强度	110	MPa	ASTM D695
剪切强度	70.3	MPa	ASTM D732
摩擦系数			ASTM D3702
--4	0.090		ASTM D3702
--5	0.080		ASTM D3702
--6	0.25		ASTM D3702
--7	0.30		ASTM D3702

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度
--	69	J/m	ASTM D256
--	9.0	kJ/m2	ISO 180
无缺口悬臂梁冲击
--	530	J/m	ASTM D4812
--	34	kJ/m2	ISO 180

热性能	额定值	单位制	测试方法
载荷下热变形温度			ASTM D648
1.8 MPa, 未退火	291	°C	ASTM D648
1.8 MPa, 退火	291	°C	ASTM D648
玻璃转化温度	152	°C	ASTM D3418
熔融峰值温度	342	°C	ASTM D3418
线形热膨胀系数 - 流动			ASTM E831
0 到 150°C	2.2E-5	cm/cm/°C	ASTM E831
-50 到 50°C	2.2E-5	cm/cm/°C	ASTM E831
比热			DSC
50°C	1360	J/kg/°C	DSC
200°C	1840	J/kg/°C	DSC
导热系数	0.40	W/m/K	ASTM E1530

可燃性	额定值		测试方法
UL 阻燃等级			UL 94
0.800 mm	V-0		UL 94
1.60 mm	V-0		UL 94

充模分析	额定值	单位制	测试方法
熔体粘度(400°C, 1000 sec^-1)	270	Pa·s	ASTM D3835

注射	额定值	单位制
干燥温度	150	°C
干燥时间	4.0	hr
料筒后部温度	366	°C
料筒中部温度	370	°C
料筒前部温度	375	°C
射嘴温度	380	°C
模具温度	175 到 205	°C
注射速度	快速
螺杆压缩比	2.5:1.0 到 3.5:1.0

注射说明
Back Pressure: minimum

备注
1 .	5" x 0.5" x 0.125" bars
2 .	5.0 mm/min
3 .	5.0 mm/min
4 .	润滑条件：: 75 fpm ， 1000 psi ( 0.38 m/s ， 6895 kPa)
5 .	润滑条件： 800 fpm ， 750 psi (4.06 m/s ， 5171 kPa)
6 .	干燥条件： 800 fpm and 31.25 psi (4.06 m/s and 215 kPa
7 .	干燥条件：干燥条件： 200 fpm ，125 psi (1.02 m/s ， 862 kPa. 不推荐 50 fpm ，500 psi (0.25 m/s ， 3447 kPa).）