| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 雾度2 | 40 mil | ASTM D-1003 | 76.1 | |
| 硬度2 | Shore A,15 sec | ASTM D-2240 | 90 | ||
| 密度 | ExxonMobil Method | 0.902 | g/cm3 | ||
| 熔体流动速率 | ExxonMobil Method | 2.5 | g/10 min | ||
| 硬度2 | Shore D,15 sec | ASTM D-2240 | 36.8 | ||
| 熔融指数 | ExxonMobil Method | 1.1 | g/10 min | ||
| 物理性能 | 弯曲模量 | 1 secant | ASTM D-790 | 9842(67.9) | psi(MPa) |
| 冲击强度 | 23 | ASTM D-256 | No Break | ft-lb/in(J/m) | |
| 冲击强度 | -40 | ASTM D-256 | No Break | ft-lb/in(J/m) | |
| 拉伸强度3 | @Break | ASTM D-638 | No Break | psi(MPa) | |
| 拉伸率 | @Break | ASTM D-638 | No Break | ||
| 热性能 | 最高熔体温度 | ExxonMobil Method | 206.4(96.9) | ?H() | |
| 维卡软化点2 | 1000g | ASTM D-1525 | 182.7(83.7) | ?H() | |
| 维卡软化点2 | 200g | ASTM D-1525 | 205.2(96.2) | ?H() | |
| 其它性能 | 拉应力5 | @100 Elongation | ASTM D-412 | 1780(12.3) | psi(MPa) |
| 拉伸率 | @Break | ASTM D-412 | 1144 | ||
| 抗扯强度 | ASTM D-624 | 508.5(89.1) | lb-in(kN/m) | ||
| 拉伸强度 | @Peak | ASTM D-412 | 4454(30.7) | psi(MPa) | |
| 门尼粘度ML(1 4) | 125 | ASTM D-1646 | 3.9 | Torgue Units | |
| 抗环境应力开裂性 | ASTM D-1693 | 1000 | hr | ||
| 拉应力5 | @300 Elongation | ASTM D-412 | 2115(14.6) | psi(MPa) | |