美国杜邦PPA HTN53G60LRHF BK083 60%玻纤增强 高刚性 热稳定
DuPont Performance Polymers Zytel? HTN 53G60LRHF BK083 Polyphthalamide (PPA) (Unverified Data**)
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 50% Glass Fiber Reinforced
DuPont Performance Polymers
产品说明:
60% Glass Reinforced High Performance Polyamide with High Stiffness and Improved Flow
Zytel HTN53G60LRHF BK083 is a 60% glass reinforced lubricated high performance polyamide resin with improved flow. It was developed for structural applications requir
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel? HTN 53G60LRHF BK083 Polyphthalamide (PPA) (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.72 g/cc | 0.0621 lb/in3 | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.0010 cm/cm | 0.0010 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0050 cm/cm | 0.0050 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 225 MPa | 32600 psi | 50%RH; ISO 527-1/-2 |
| 265 MPa | 38400 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 | 4.08 MPa
@Strain 0.0600 %, Temperature 150 °C
|
592 psi
@Strain 0.0600 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 |
| 4.40 MPa
@Strain 0.0600 %, Temperature 180 °C
|
638 psi
@Strain 0.0600 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 5.17 MPa
@Strain 0.0600 %, Temperature 150 °C
|
750 psi
@Strain 0.0600 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 5.69 MPa
@Strain 0.0400 %, Temperature 0.000 °C
|
825 psi
@Strain 0.0400 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 5.88 MPa
@Strain 0.0500 %, Temperature 23.0 °C
|
853 psi
@Strain 0.0500 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 5.98 MPa
@Strain 0.0600 %, Temperature 90.0 °C
|
867 psi
@Strain 0.0600 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 7.13 MPa
@Strain 0.0600 %, Temperature -20.0 °C
|
1030 psi
@Strain 0.0600 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 7.38 MPa
@Strain 0.0500 %, Temperature 0.000 °C
|
1070 psi
@Strain 0.0500 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 7.56 MPa
@Strain 0.0500 %, Temperature 90.0 °C
|
1100 psi
@Strain 0.0500 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 7.63 MPa
@Strain 0.0600 %, Temperature -20.0 °C
|
1110 psi
@Strain 0.0600 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 8.40 MPa
@Strain 0.0400 %, Temperature 40.0 °C
|
1220 psi
@Strain 0.0400 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 9.24 MPa
@Strain 0.0400 %, Temperature 23.0 °C
|
1340 psi
@Strain 0.0400 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 10.59 MPa
@Strain 0.0400 %, Temperature 40.0 °C
|
1536 psi
@Strain 0.0400 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 11.75 MPa
@Strain 0.200 %, Temperature 150 °C
|
1704 psi
@Strain 0.200 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 12.49 MPa
@Strain 0.220 %, Temperature 180 °C
|
1812 psi
@Strain 0.220 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 15.02 MPa
@Strain 0.230 %, Temperature 150 °C
|
2178 psi
@Strain 0.230 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 17.25 MPa
@Strain 0.200 %, Temperature 90.0 °C
|
2502 psi
@Strain 0.200 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 22.5 MPa
@Strain 0.210 %, Temperature 90.0 °C
|
3260 psi
@Strain 0.210 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 25.67 MPa
@Strain 0.150 %, Temperature 40.0 °C
|
3723 psi
@Strain 0.150 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 28.51 MPa
@Strain 0.140 %, Temperature 23.0 °C
|
4135 psi
@Strain 0.140 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 29.52 MPa
@Strain 0.130 %, Temperature 23.0 °C
|
4282 psi
@Strain 0.130 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 29.75 MPa
@Strain 0.760 %, Temperature 150 °C
|
4315 psi
@Strain 0.760 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 30.63 MPa
@Strain 0.800 %, Temperature 180 °C
|
4443 psi
@Strain 0.800 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 31.13 MPa
@Strain 0.150 %, Temperature 0.000 °C
|
4515 psi
@Strain 0.150 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 31.52 MPa
@Strain 0.150 %, Temperature 0.000 °C
|
4572 psi
@Strain 0.150 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 32.16 MPa
@Strain 0.140 %, Temperature 40.0 °C
|
4664 psi
@Strain 0.140 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 37.36 MPa
@Strain 0.170 %, Temperature -20.0 °C
|
5419 psi
@Strain 0.170 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 37.9 MPa
@Strain 0.240 %, Temperature 40.0 °C
|
5500 psi
@Strain 0.240 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 38.73 MPa
@Strain 0.150 %, Temperature -20.0 °C
|
5617 psi
@Strain 0.150 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 40.49 MPa
@Strain 0.200 %, Temperature 23.0 °C
|
5873 psi
@Strain 0.200 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 40.61 MPa
@Strain 1.01 %, Temperature 150 °C
|
5890 psi
@Strain 1.01 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 40.78 MPa
@Strain 1.62 %, Temperature 150 °C
|
5915 psi
@Strain 1.62 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 41.26 MPa
@Strain 0.170 %, Temperature 23.0 °C
|
5984 psi
@Strain 0.170 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 41.27 MPa
@Strain 1.69 %, Temperature 180 °C
|
5986 psi
@Strain 1.69 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 43.31 MPa
@Strain 0.720 %, Temperature 90.0 °C
|
6282 psi
@Strain 0.720 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 44.86 MPa
@Strain 0.200 %, Temperature 40.0 °C
|
6506 psi
@Strain 0.200 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 46.01 MPa
@Strain 0.210 %, Temperature 0.000 °C
|
6673 psi
@Strain 0.210 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 47.63 MPa
@Strain 0.230 %, Temperature 0.000 °C
|
6908 psi
@Strain 0.230 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 52.16 MPa
@Strain 0.220 %, Temperature 23.0 °C
|
7565 psi
@Strain 0.220 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 52.67 MPa
@Strain 0.210 %, Temperature -20.0 °C
|
7639 psi
@Strain 0.210 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 53.08 MPa
@Strain 1.99 %, Temperature 150 °C
|
7699 psi
@Strain 1.99 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 54.46 MPa
@Strain 0.260 %, Temperature 23.0 °C
|
7899 psi
@Strain 0.260 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 55.7 MPa
@Strain 5.04 %, Temperature 180 °C
|
8080 psi
@Strain 5.04 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 56.01 MPa
@Strain 4.77 %, Temperature 150 °C
|
8124 psi
@Strain 4.77 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 56.33 MPa
@Strain 0.630 %, Temperature 90.0 °C
|
8170 psi
@Strain 0.630 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 56.48 MPa
@Strain 0.200 %, Temperature -20.0 °C
|
8192 psi
@Strain 0.200 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 56.96 MPa
@Strain 0.250 %, Temperature 40.0 °C
|
8261 psi
@Strain 0.250 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 58.58 MPa
@Strain 7.15 %, Temperature 180 °C
|
8496 psi
@Strain 7.15 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 59.14 MPa
@Strain 6.74 %, Temperature 150 °C
|
8578 psi
@Strain 6.74 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 60.57 MPa
@Strain 1.49 %, Temperature 90.0 °C
|
8785 psi
@Strain 1.49 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 63.55 MPa
@Strain 0.280 %, Temperature 0.000 °C
|
9217 psi
@Strain 0.280 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 65.21 MPa
@Strain 0.250 %, Temperature -20.0 °C
|
9458 psi
@Strain 0.250 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 70.92 MPa
@Strain 5.53 %, Temperature 150 °C
|
10290 psi
@Strain 5.53 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 71.95 MPa
@Strain 0.260 %, Temperature -20.0 °C
|
10440 psi
@Strain 0.260 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 74.29 MPa
@Strain 7.80 %, Temperature 150 °C
|
10770 psi
@Strain 7.80 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 74.49 MPa
@Strain 0.540 %, Temperature 40.0 °C
|
10800 psi
@Strain 0.540 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 82.47 MPa
@Strain 0.390 %, Temperature 0.000 °C
|
11960 psi
@Strain 0.390 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 84.81 MPa
@Strain 1.25 %, Temperature 90.0 °C
|
12300 psi
@Strain 1.25 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 85.83 MPa
@Strain 4.65 %, Temperature 90.0 °C
|
12450 psi
@Strain 4.65 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 |
美国杜邦PA66 HTN510EFT NC010 高抗冲击 热稳定 高温尼龙树脂
美国杜邦PA66 HTNFE18502 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 BK431 超高抗冲击强度 耐高低温 耐疲劳 耐化学
美国杜邦PA66 HTN53G50HSLR BK083 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN53G50HSL NC010 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN54G15HSLR NC010 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G15HSL BK031 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G35HSLR NC010 35%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN42G30EF NC010 30%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN53G60LRHF BK083 60%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN55G55TLW BK117 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN55G55TLW BK773 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN53G55LWSF BK045P 55%玻纤增强 高刚性 耐化学
美国杜邦PA66 HTN53G50LWSF BK702A 55%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN92G35DH2 BK083 35%玻纤增强 高刚性 高流动
美国杜邦PA66 HTNFR42G30NH NC010 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR42G30NH BK337 35%玻纤增强 高刚性 无卤阻燃 黑色
广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，PA46，PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。