美国杜邦PPA HTN54G35HSLR BK031 35%玻纤增强 高抗冲 耐水解
DuPont Performance Polymers Zytel? HTN 54G35HSLR BK031 Polyphthalamide (PPA) (Unverified Data**)
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 40% Glass Fiber Reinforced
DuPont Performance Polymers
产品说明:
35% Glass Reinforced Toughened PPA High Performance Polyamide
Zytel HTN54G35HSLR BK031 is a 35% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It is also a PPA resin.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel? HTN 54G35HSLR BK031 Polyphthalamide (PPA) (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.42 g/cc | 0.0513 lb/in3 | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0050 cm/cm | 0.0050 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 166 MPa | 24100 psi | 50%RH; ISO 527-1/-2 |
| 180 MPa | 26100 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 | 8.18 MPa
@Strain 0.200 %, Temperature 160 °C
|
1190 psi
@Strain 0.200 %, Temperature 320 °F
|
DAM; ISO 11403-1 -2 |
| 10.34 MPa
@Strain 0.240 %, Temperature 150 °C
|
1500 psi
@Strain 0.240 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 10.35 MPa
@Strain 0.280 %, Temperature 180 °C
|
1501 psi
@Strain 0.280 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 19.46 MPa
@Strain 0.660 %, Temperature 150 °C
|
2822 psi
@Strain 0.660 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 23.18 MPa
@Strain 0.510 %, Temperature 90.0 °C
|
3362 psi
@Strain 0.510 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 34.46 MPa
@Strain 1.68 %, Temperature 180 °C
|
4998 psi
@Strain 1.68 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 35.54 MPa
@Strain 1.88 %, Temperature 150 °C
|
5155 psi
@Strain 1.88 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 38.47 MPa
@Strain 0.410 %, Temperature 40.0 °C
|
5580 psi
@Strain 0.410 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 38.99 MPa
@Strain 1.46 %, Temperature 150 °C
|
5655 psi
@Strain 1.46 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 41.77 MPa
@Strain 0.420 %, Temperature 23.0 °C
|
6058 psi
@Strain 0.420 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 42.56 MPa
@Strain 2.96 %, Temperature 150 °C
|
6173 psi
@Strain 2.96 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 42.6 MPa
@Strain 2.83 %, Temperature 180 °C
|
6180 psi
@Strain 2.83 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 43.27 MPa
@Strain 2.12 %, Temperature 160 °C
|
6276 psi
@Strain 2.12 %, Temperature 320 °F
|
DAM; ISO 11403-1 -2 | |
| 46.19 MPa
@Strain 0.520 %, Temperature 90.0 °C
|
6699 psi
@Strain 0.520 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 46.8 MPa
@Strain 1.48 %, Temperature 90.0 °C
|
6790 psi
@Strain 1.48 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 47.43 MPa
@Strain 4.18 %, Temperature 150 °C
|
6879 psi
@Strain 4.18 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 48.05 MPa
@Strain 4.06 %, Temperature 180 °C
|
6969 psi
@Strain 4.06 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 49.84 MPa
@Strain 2.55 %, Temperature 150 °C
|
7229 psi
@Strain 2.55 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 50.98 MPa
@Strain 3.26 %, Temperature 160 °C
|
7394 psi
@Strain 3.26 %, Temperature 320 °F
|
DAM; ISO 11403-1 -2 | |
| 53.25 MPa
@Strain 0.530 %, Temperature 0.000 °C
|
7723 psi
@Strain 0.530 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 56.27 MPa
@Strain 4.49 %, Temperature 160 °C
|
8161 psi
@Strain 4.49 %, Temperature 320 °F
|
DAM; ISO 11403-1 -2 | |
| 56.53 MPa
@Strain 8.18 %, Temperature 180 °C
|
8199 psi
@Strain 8.18 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 56.83 MPa
@Strain 3.74 %, Temperature 150 °C
|
8243 psi
@Strain 3.74 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 57.85 MPa
@Strain 2.41 %, Temperature 90.0 °C
|
8390 psi
@Strain 2.41 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 64.81 MPa
@Strain 3.58 %, Temperature 90.0 °C
|
9400 psi
@Strain 3.58 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 71.62 MPa
@Strain 0.840 %, Temperature 40.0 °C
|
10390 psi
@Strain 0.840 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 73.53 MPa
@Strain 0.700 %, Temperature -20.0 °C
|
10660 psi
@Strain 0.700 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 74.28 MPa
@Strain 0.920 %, Temperature 90.0 °C
|
10770 psi
@Strain 0.920 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 92.13 MPa
@Strain 0.950 %, Temperature 0.000 °C
|
13360 psi
@Strain 0.950 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 93.07 MPa
@Strain 1.19 %, Temperature 40.0 °C
|
13500 psi
@Strain 1.19 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 96.7 MPa
@Strain 0.990 %, Temperature 23.0 °C
|
14000 psi
@Strain 0.990 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 97.7 MPa
@Strain 1.38 %, Temperature 90.0 °C
|
14200 psi
@Strain 1.38 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 105.87 MPa
@Strain 1.13 %, Temperature 40.0 °C
|
15355 psi
@Strain 1.13 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 113.12 MPa
@Strain 1.64 %, Temperature 40.0 °C
|
16407 psi
@Strain 1.64 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 113.98 MPa
@Strain 1.92 %, Temperature 90.0 °C
|
16531 psi
@Strain 1.92 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 117.77 MPa
@Strain 1.19 %, Temperature 0.000 °C
|
17081 psi
@Strain 1.19 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 119.44 MPa
@Strain 1.28 %, Temperature 0.000 °C
|
17323 psi
@Strain 1.28 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 123 MPa
@Strain 1.24 %, Temperature -20.0 °C
|
17800 psi
@Strain 1.24 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 126.69 MPa
@Strain 1.58 %, Temperature 23.0 °C
|
18375 psi
@Strain 1.58 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 129.67 MPa
@Strain 1.41 %, Temperature 23.0 °C
|
18807 psi
@Strain 1.41 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 144.07 MPa
@Strain 1.65 %, Temperature 0.000 °C
|
20896 psi
@Strain 1.65 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 146.8 MPa
@Strain 2.07 %, Temperature 23.0 °C
|
21290 psi
@Strain 2.07 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 149.32 MPa
@Strain 1.84 %, Temperature 40.0 °C
|
21657 psi
@Strain 1.84 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 154.64 MPa
@Strain 1.66 %, Temperature 0.000 °C
|
22429 psi
@Strain 1.66 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 154.84 MPa
@Strain 1.82 %, Temperature 23.0 °C
|
22458 psi
@Strain 1.82 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 160.4 MPa
@Strain 2.83 %, Temperature 23.0 °C
|
23260 psi
@Strain 2.83 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 167.73 MPa
@Strain 1.81 %, Temperature -20.0 °C
|
24327 psi
@Strain 1.81 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 168.89 MPa
@Strain 2.36 %, Temperature 40.0 °C
|
24495 psi
@Strain 2.36 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 176.66 MPa
@Strain 2.29 %, Temperature 23.0 °C
|
25622 psi
@Strain 2.29 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 180.28 MPa
@Strain 3.17 %, Temperature 40.0 °C
|
26147 psi
@Strain 3.17 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 183.66 MPa
@Strain 2.16 %, Temperature 0.000 °C
|
26638 psi
@Strain 2.16 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 189.09 MPa
@Strain 2.22 %, Temperature -20.0 °C
|
27425 psi
@Strain 2.22 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 196.56 MPa
@Strain 2.28 %, Temperature -20.0 °C
|
28509 psi
@Strain 2.28 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 206.46 MPa
@Strain 2.72 %, Temperature 0.000 °C
|
29945 psi
@Strain 2.72 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 211.27 MPa
@Strain 2.82 %, Temperature -20.0 °C
|
30642 psi
@Strain 2.82 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 222.55 MPa
@Strain 2.86 %, Temperature -20.0 °C
|
32278 psi
@Strain 2.86 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 2.7 % | 2.7 % | 50%RH; ISO 527-1/-2 |
| 3.0 % | 3.0 % | DAM; ISO 527-1/-2 | |
| 拉伸模量 | 10.5 GPa | 1520 ksi | DAM; ISO 527-1/-2 |
| 10.8 GPa | 1570 ksi | 50%RH; ISO 527-1/-2 |
美国杜邦PA66 HTN52G35EF BK420 35%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN52G45HSL BK083 45%玻纤增强 高刚性 热稳定。
美国杜邦PA66 HTNFR52G30NH BK337 30%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G30NH NC010 30%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G30BL NC010 30%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNFR52G30BL BK337 30%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNFR52G35NHF BK337 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G35NHF WT010 35%玻纤增强 高刚性 阻燃白色
美国杜邦PA66 HTNFG52G35HSL BK011 35%玻纤增强 热稳定 食品级
美国杜邦PA66 HTNFG52G35HSLR BK011 35%玻纤增强 热稳定 耐水解 食品级
美国杜邦PA66 HTNFR52G20NH NC010 20%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G45NHF NC010 45%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G45NHF BK337 45%玻纤增强 高刚性 无卤阻燃 黑色
美国杜邦PA66 HTNFR52G45BL BK337 45%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNLT52G30NH BL662 30%玻纤增强 高刚性 无卤阻燃 蓝色
美国杜邦PA66 HTN59G55LWSF BK083 55%玻纤增强 高刚性 低吸水
美国杜邦PA66 HTNFE350064 BK544 15%碳纤增强 高刚性 耐磨损
美国杜邦PA66 HTNFR55G50NHLW BK046 50%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR55G50NHLW NC010 50%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTN510EFT NC010 高抗冲击 热稳定 高温尼龙树脂
美国杜邦PA66 HTNFE18502 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 BK431 超高抗冲击强度 耐高低温 耐疲劳 耐化学
美国杜邦PA66 HTN53G50HSLR BK083 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN53G50HSL NC010 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN54G15HSLR NC010 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G15HSL BK031 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G35HSLR NC010 35%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN42G30EF NC010 30%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN53G60LRHF BK083 60%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN55G55TLW BK117 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN55G55TLW BK773 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN53G55LWSF BK045P 55%玻纤增强 高刚性 耐化学
美国杜邦PA66 HTN53G50LWSF BK702A 55%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN92G35DH2 BK083 35%玻纤增强 高刚性 高流动
美国杜邦PA66 HTNFR42G30NH NC010 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR42G30NH BK337 35%玻纤增强 高刚性 无卤阻燃 黑色
广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，PA46，PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。