美国杜邦PPA HTN54G15HSLR NC010 15%玻纤增强 高抗冲 耐水解
DuPont Performance Polymers Zytel? HTN 54G15HSLR NC010 Polyphthalamide (PPA) (Unverified Data**)
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 20% Glass Fiber Reinforced
DuPont Performance Polymers
产品说明:
15% Glass Reinforced Toughened PPA High Performance Polyamide
Zytel HTN54G15HSLR NC010 is a 15% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It is a PPA resin.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel? HTN 54G15HSLR NC010 Polyphthalamide (PPA) (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.25 g/cc | 0.0452 lb/in3 | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.0040 cm/cm | 0.0040 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0070 cm/cm | 0.0070 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 100 MPa | 14500 psi | 50%RH; ISO 527-1/-2 |
| 130 MPa | 18900 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 | 2.45 MPa
@Strain 0.100 %, Temperature 150 °C
|
355 psi
@Strain 0.100 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
| 4.73 MPa
@Strain 0.100 %, Temperature 23.0 °C
|
686 psi
@Strain 0.100 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 5.02 MPa
@Strain 0.100 %, Temperature -40.0 °C
|
728 psi
@Strain 0.100 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 7.92 MPa
@Strain 0.400 %, Temperature 150 °C
|
1150 psi
@Strain 0.400 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 13.94 MPa
@Strain 0.700 %, Temperature 150 °C
|
2022 psi
@Strain 0.700 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 18.24 MPa
@Strain 0.400 %, Temperature 23.0 °C
|
2645 psi
@Strain 0.400 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 18.85 MPa
@Strain 0.400 %, Temperature -40.0 °C
|
2734 psi
@Strain 0.400 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 18.99 MPa
@Strain 1.00 %, Temperature 150 °C
|
2754 psi
@Strain 1.00 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 29.48 MPa
@Strain 1.90 %, Temperature 150 °C
|
4276 psi
@Strain 1.90 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 33.54 MPa
@Strain 2.40 %, Temperature 150 °C
|
4865 psi
@Strain 2.40 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 33.77 MPa
@Strain 0.700 %, Temperature 23.0 °C
|
4898 psi
@Strain 0.700 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 34.94 MPa
@Strain 0.700 %, Temperature -40.0 °C
|
5068 psi
@Strain 0.700 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 37.3 MPa
@Strain 3.00 %, Temperature 150 °C
|
5410 psi
@Strain 3.00 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 39.13 MPa
@Strain 3.40 %, Temperature 150 °C
|
5675 psi
@Strain 3.40 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 40.8 MPa
@Strain 3.90 %, Temperature 150 °C
|
5920 psi
@Strain 3.90 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 42.88 MPa
@Strain 4.70 %, Temperature 150 °C
|
6219 psi
@Strain 4.70 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 43.11 MPa
@Strain 4.80 %, Temperature 150 °C
|
6253 psi
@Strain 4.80 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 45.5 MPa
@Strain 7.00 %, Temperature 150 °C
|
6600 psi
@Strain 7.00 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 46.44 MPa
@Strain 10.0 %, Temperature 150 °C
|
6736 psi
@Strain 10.0 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 47.96 MPa
@Strain 1.00 %, Temperature 23.0 °C
|
6956 psi
@Strain 1.00 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 50.14 MPa
@Strain 1.00 %, Temperature -40.0 °C
|
7272 psi
@Strain 1.00 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 85.99 MPa
@Strain 1.90 %, Temperature 23.0 °C
|
12470 psi
@Strain 1.90 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 90.8 MPa
@Strain 1.90 %, Temperature -40.0 °C
|
13200 psi
@Strain 1.90 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 102.61 MPa
@Strain 2.40 %, Temperature 23.0 °C
|
14882 psi
@Strain 2.40 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 110.52 MPa
@Strain 2.40 %, Temperature -40.0 °C
|
16030 psi
@Strain 2.40 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 116.99 MPa
@Strain 3.00 %, Temperature 23.0 °C
|
16968 psi
@Strain 3.00 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 123.08 MPa
@Strain 3.40 %, Temperature 23.0 °C
|
17851 psi
@Strain 3.40 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 2.7 % | 2.7 % | 50%RH; ISO 527-1/-2 |
| 3.7 % | 3.7 % | DAM; ISO 527-1/-2 | |
| 拉伸模量 | 5.50 GPa | 798 ksi | 50%RH; ISO 527-1/-2 |
| 5.60 GPa | 812 ksi | DAM; ISO 527-1/-2 | |
| 弯曲模量 | 4.90 GPa | 711 ksi | DAM; ISO 178 |
| 割线模量 | 2.7555 GPa
@Strain 2.00 %, Temperature 100 °C
|
399.66 ksi
@Strain 2.00 %, Temperature 212 °F
|
DAM; ISO 11403-1 -2 |
| 3.02 GPa
@Strain 1.60 %, Temperature 100 °C
|
438 ksi
@Strain 1.60 %, Temperature 212 °F
|
DAM; ISO 11403-1 -2 | |
| 3.2325 GPa
@Strain 1.20 %, Temperature 100 °C
|
468.84 ksi
@Strain 1.20 %, Temperature 212 °F
|
DAM; ISO 11403-1 -2 | |
| 3.3225 GPa
@Strain 0.400 %, Temperature 100 °C
|
481.90 ksi
@Strain 0.400 %, Temperature 212 °F
|
DAM; ISO 11403-1 -2 | |
| 3.44 GPa
@Strain 0.800 %, Temperature 100 °C
|
498 ksi
@Strain 0.800 %, Temperature 212 °F
|
DAM; ISO 11403-1 -2 | |
| 3.90 GPa
@Strain 0.100 %, Temperature 100 °C
|
566 ksi
@Strain 0.100 %, Temperature 212 °F
|
DAM; ISO 11403-1 -2 | |
| 4.484 GPa
@Strain 2.00 %, Temperature 23.0 °C
|
650.4 ksi
@Strain 2.00 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 4.56 GPa
@Strain 0.400 %, Temperature 23.0 °C
|
661 ksi
@Strain 0.400 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 4.65 GPa
@Strain 1.60 %, Temperature 23.0 °C
|
675 ksi
@Strain 1.60 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 4.7125 GPa
@Strain 0.400 %, Temperature -40.0 °C
|
683.50 ksi
@Strain 0.400 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 4.73 GPa
@Strain 0.100 %, Temperature 23.0 °C
|
686 ksi
@Strain 0.100 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 4.746 GPa
@Strain 2.00 %, Temperature -40.0 °C
|
688.4 ksi
@Strain 2.00 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 4.765 GPa
@Strain 1.20 %, Temperature 23.0 °C
|
691.1 ksi
@Strain 1.20 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 4.85 GPa
@Strain 0.800 %, Temperature 23.0 °C
|
703 ksi
@Strain 0.800 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 4.87 GPa
@Strain 1.60 %, Temperature -40.0 °C
|
706 ksi
@Strain 1.60 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 4.97 GPa
@Strain 1.20 %, Temperature -40.0 °C
|
720 ksi
@Strain 1.20 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 5.02 GPa
@Strain 0.100 %, Temperature -40.0 °C
|
728 ksi
@Strain 0.100 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 5.0825 GPa
@Strain 0.800 %, Temperature -40.0 °C
|
737.17 ksi
@Strain 0.800 %, Temperature -40.0 °F
|
DAM; ISO 11403-1 -2 | |
| 简支梁无缺口冲击强度 | 6.00 J/cm2 | 28.6 ft-lb/in2 | 50%RH; ISO 179/1eU |
| 7.00 J/cm2 | 33.3 ft-lb/in2 | DAM; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.600 J/cm2 | 2.86 ft-lb/in2 | DAM; ISO 179/1eA |
| 拉伸蠕变模量(1 hr) | 5500 MPa
@Time 3600 sec
|
798000 psi
@Time 1.00 hour
|
50%RH; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 5000 MPa
@Time 3.60e+6 sec
|
725000 psi
@Time 1000 hour
|
50%RH; ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | = 1.00e+15 ohm-cm | = 1.00e+15 ohm-cm | DAM; IEC 60093 |
| = 1.00e+15 ohm-cm | = 1.00e+15 ohm-cm | 50%RH; IEC 60093 | |
| 表面电阻 | = 1.00e+15 ohm | = 1.00e+15 ohm | 50%RH; IEC 60093 |
| 介电强度 | 16.5 kV/mm | 419 kV/in | DAM; IEC 60243-1 |
| 耗散因数 | 0.015
@Frequency 100 Hz
|
0.015
@Frequency 100 Hz
|
DAM; IEC 60250 |
| 0.015
@Frequency 1.00e+6 Hz
|
0.015
@Frequency 1.00e+6 Hz
|
DAM; IEC 60250 |
美国杜邦PA66 HTN51G35FWS BK083 35%玻纤增强 热稳定 耐疲劳 耐水解级，
美国杜邦PA66 HTN51G35HSLR BK420J 35%玻纤增强 热稳定 耐疲劳 耐水解级
美国杜邦PA66 HTNFR51G35L BK337 35%玻纤增强 高刚性 防火阻燃。
美国杜邦PA66 HTN51G50HSL BK083 50%玻纤增强 热稳定 耐水解，
美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强 热稳定 耐水解 耐化学
美国杜邦PA66 HTN51G45HSL BK083 45%玻纤增强 热稳定 耐水解 耐化学
美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强 热稳定 耐水解 耐化学
美国杜邦PA66 HTN52G35HSL BK083 35%玻纤增强 高刚性 热稳定。
美国杜邦PA66 HTN52G35EF BK420 35%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN52G45HSL BK083 45%玻纤增强 高刚性 热稳定。
美国杜邦PA66 HTNFR52G30NH BK337 30%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G30NH NC010 30%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G30BL NC010 30%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNFR52G30BL BK337 30%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNFR52G35NHF BK337 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G35NHF WT010 35%玻纤增强 高刚性 阻燃白色
美国杜邦PA66 HTNFG52G35HSL BK011 35%玻纤增强 热稳定 食品级
美国杜邦PA66 HTNFG52G35HSLR BK011 35%玻纤增强 热稳定 耐水解 食品级
美国杜邦PA66 HTNFR52G20NH NC010 20%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G45NHF NC010 45%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G45NHF BK337 45%玻纤增强 高刚性 无卤阻燃 黑色
美国杜邦PA66 HTNFR52G45BL BK337 45%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNLT52G30NH BL662 30%玻纤增强 高刚性 无卤阻燃 蓝色
美国杜邦PA66 HTN59G55LWSF BK083 55%玻纤增强 高刚性 低吸水
美国杜邦PA66 HTNFE350064 BK544 15%碳纤增强 高刚性 耐磨损
美国杜邦PA66 HTNFR55G50NHLW BK046 50%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR55G50NHLW NC010 50%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTN510EFT NC010 高抗冲击 热稳定 高温尼龙树脂
美国杜邦PA66 HTNFE18502 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 BK431 超高抗冲击强度 耐高低温 耐疲劳 耐化学
美国杜邦PA66 HTN53G50HSLR BK083 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN53G50HSL NC010 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN54G15HSLR NC010 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G15HSL BK031 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G35HSLR NC010 35%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN42G30EF NC010 30%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN53G60LRHF BK083 60%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN55G55TLW BK117 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN55G55TLW BK773 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN53G55LWSF BK045P 55%玻纤增强 高刚性 耐化学
美国杜邦PA66 HTN53G50LWSF BK702A 55%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN92G35DH2 BK083 35%玻纤增强 高刚性 高流动
美国杜邦PA66 HTNFR42G30NH NC010 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR42G30NH BK337 35%玻纤增强 高刚性 无卤阻燃 黑色
广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，PA46，PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。