美国杜邦PPA HTNFR52G30BL NC010 30%玻纤增强高刚性防火阻燃

DuPont Performance Polymers Zytel? HTN FR52G30BL NC010 Polyphthalamide (PPA) (Unverified Data**)

Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 30% Glass Fiber Reinforced

DuPont Performance Polymers

产品说明:

30% Glass Reinforced Flame Retardant PPA High Performance Polyamide

Zytel HTNFR52G30BL NC010 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin that has been developed for connector applications.

Information provided by DuPont Performance Polymers

DuPont Performance Polymers Zytel? HTN FR52G30BL NC010 Polyphthalamide (PPA) (Unverified Data**) 物性表

物理性能额定值 (公制) 额定值 (英制) 测试方法

密度 1.62 g/cc 0.0585 lb/in3 DAM; ISO 1183

粘度测试 120 cm3/g 120 cm3/g DAM; ISO 307 1157 1628

线性成型收缩率,Flow 0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577

线性成型收缩率，横向 0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577

熔体流动速率 26 g/10 min
@Load 2.16 kg, Temperature 325 °C
26 g/10 min
@Load 4.76 lb, Temperature 617 °F
DAM; cm3/10min; ISO 1133

机械性能额定值 (公制) 额定值 (英制) 测试方法

抗张强度(断裂) 150 MPa 21800 psi 50%RH; ISO 527-1/-2

170 MPa 24700 psi DAM; ISO 527-1/-2

抗张强度 18.83 MPa
@Strain 0.330 %, Temperature 150 °C
2731 psi
@Strain 0.330 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

20.45 MPa
@Strain 0.290 %, Temperature 90.0 °C
2966 psi
@Strain 0.290 %, Temperature 194 °F
50%RH; ISO 11403-1 -2

21.71 MPa
@Strain 0.180 %, Temperature 0.000 °C
3149 psi
@Strain 0.180 %, Temperature 32.0 °F
50%RH; ISO 11403-1 -2

22.15 MPa
@Strain 0.350 %, Temperature 150 °C
3213 psi
@Strain 0.350 %, Temperature 302 °F
DAM; ISO 11403-1 -2

22.19 MPa
@Strain 0.190 %, Temperature 40.0 °C
3218 psi
@Strain 0.190 %, Temperature 104 °F
DAM; ISO 11403-1 -2

22.3 MPa
@Strain 0.180 %, Temperature -20.0 °C
3230 psi
@Strain 0.180 %, Temperature -4.00 °F
50%RH; ISO 11403-1 -2

22.54 MPa
@Strain 0.260 %, Temperature 90.0 °C
3269 psi
@Strain 0.260 %, Temperature 194 °F
DAM; ISO 11403-1 -2

22.73 MPa
@Strain 0.240 %, Temperature 40.0 °C
3297 psi
@Strain 0.240 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

22.8 MPa
@Strain 0.190 %, Temperature 0.000 °C
3310 psi
@Strain 0.190 %, Temperature 32.0 °F
DAM; ISO 11403-1 -2

23.63 MPa
@Strain 0.210 %, Temperature 23.0 °C
3427 psi
@Strain 0.210 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

25.24 MPa
@Strain 0.210 %, Temperature -20.0 °C
3661 psi
@Strain 0.210 %, Temperature -4.00 °F
DAM; ISO 11403-1 -2

25.57 MPa
@Strain 0.200 %, Temperature 23.0 °C
3709 psi
@Strain 0.200 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

52.02 MPa
@Strain 1.32 %, Temperature 150 °C
7545 psi
@Strain 1.32 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

60.09 MPa
@Strain 1.37 %, Temperature 150 °C
8715 psi
@Strain 1.37 %, Temperature 302 °F
DAM; ISO 11403-1 -2

62.98 MPa
@Strain 1.17 %, Temperature 90.0 °C
9134 psi
@Strain 1.17 %, Temperature 194 °F
50%RH; ISO 11403-1 -2

65.3 MPa
@Strain 2.32 %, Temperature 150 °C
9470 psi
@Strain 2.32 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

69.2 MPa
@Strain 3.31 %, Temperature 150 °C
10000 psi
@Strain 3.31 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

74.6 MPa
@Strain 1.00 %, Temperature 90.0 °C
10800 psi
@Strain 1.00 %, Temperature 194 °F
DAM; ISO 11403-1 -2

75.91 MPa
@Strain 2.39 %, Temperature 150 °C
11010 psi
@Strain 2.39 %, Temperature 302 °F
DAM; ISO 11403-1 -2

78.74 MPa
@Strain 0.920 %, Temperature 40.0 °C
11420 psi
@Strain 0.920 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

80.8 MPa
@Strain 3.40 %, Temperature 150 °C
11700 psi
@Strain 3.40 %, Temperature 302 °F
DAM; ISO 11403-1 -2

82.4 MPa
@Strain 2.03 %, Temperature 90.0 °C
12000 psi
@Strain 2.03 %, Temperature 194 °F
50%RH; ISO 11403-1 -2

82.87 MPa
@Strain 0.720 %, Temperature 40.0 °C
12020 psi
@Strain 0.720 %, Temperature 104 °F
DAM; ISO 11403-1 -2

85.18 MPa
@Strain 0.730 %, Temperature 0.000 °C
12350 psi
@Strain 0.730 %, Temperature 32.0 °F
50%RH; ISO 11403-1 -2

87.81 MPa
@Strain 0.810 %, Temperature 23.0 °C
12740 psi
@Strain 0.810 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

88.7 MPa
@Strain 0.730 %, Temperature -20.0 °C
12900 psi
@Strain 0.730 %, Temperature -4.00 °F
50%RH; ISO 11403-1 -2

88.9 MPa
@Strain 2.91 %, Temperature 90.0 °C
12900 psi
@Strain 2.91 %, Temperature 194 °F
50%RH; ISO 11403-1 -2

91.67 MPa
@Strain 0.770 %, Temperature 0.000 °C
13300 psi
@Strain 0.770 %, Temperature 32.0 °F
DAM; ISO 11403-1 -2

91.76 MPa
@Strain 0.760 %, Temperature 23.0 °C
13310 psi
@Strain 0.760 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

97.54 MPa
@Strain 0.800 %, Temperature -20.0 °C
14150 psi
@Strain 0.800 %, Temperature -4.00 °F
DAM; ISO 11403-1 -2

104.12 MPa
@Strain 1.76 %, Temperature 90.0 °C
15101 psi
@Strain 1.76 %, Temperature 194 °F
DAM; ISO 11403-1 -2

112.47 MPa
@Strain 1.62 %, Temperature 40.0 °C
16312 psi
@Strain 1.62 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

118.53 MPa
@Strain 2.50 %, Temperature 90.0 °C
17191 psi
@Strain 2.50 %, Temperature 194 °F
DAM; ISO 11403-1 -2

128.53 MPa
@Strain 1.27 %, Temperature 40.0 °C
18642 psi
@Strain 1.27 %, Temperature 104 °F
DAM; ISO 11403-1 -2

129.37 MPa
@Strain 1.40 %, Temperature 23.0 °C
18764 psi
@Strain 1.40 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

130.1 MPa
@Strain 2.30 %, Temperature 40.0 °C
18870 psi
@Strain 2.30 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

132.82 MPa
@Strain 1.26 %, Temperature 0.000 °C
19264 psi
@Strain 1.26 %, Temperature 32.0 °F
50%RH; ISO 11403-1 -2

140.43 MPa
@Strain 1.34 %, Temperature 23.0 °C
20368 psi
@Strain 1.34 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

141.24 MPa
@Strain 1.27 %, Temperature -20.0 °C
20485 psi
@Strain 1.27 %, Temperature -4.00 °F
50%RH; ISO 11403-1 -2

143.2 MPa
@Strain 1.33 %, Temperature 0.000 °C
20770 psi
@Strain 1.33 %, Temperature 32.0 °F
DAM; ISO 11403-1 -2

153.44 MPa
@Strain 2.00 %, Temperature 23.0 °C
22255 psi
@Strain 2.00 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

154.25 MPa
@Strain 1.41 %, Temperature -20.0 °C
22372 psi
@Strain 1.41 %, Temperature -4.00 °F
DAM; ISO 11403-1 -2

157.6 MPa
@Strain 1.80 %, Temperature 40.0 °C
22860 psi
@Strain 1.80 %, Temperature 104 °F
DAM; ISO 11403-1 -2

163.4 MPa
@Strain 1.80 %, Temperature 0.000 °C
23700 psi
@Strain 1.80 %, Temperature 32.0 °F
50%RH; ISO 11403-1 -2

165.5 MPa
@Strain 1.80 %, Temperature 23.0 °C
24000 psi
@Strain 1.80 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

176.85 MPa
@Strain 1.91 %, Temperature 0.000 °C
25650 psi
@Strain 1.91 %, Temperature 32.0 °F
DAM; ISO 11403-1 -2

177.53 MPa
@Strain 1.80 %, Temperature -20.0 °C
25749 psi
@Strain 1.80 %, Temperature -4.00 °F
50%RH; ISO 11403-1 -2

188.54 MPa
@Strain 2.00 %, Temperature -20.0 °C
27345 psi
@Strain 2.00 %, Temperature -4.00 °F
DAM; ISO 11403-1 -2

伸长率 (断裂) 2.0 % 2.0 % DAM; ISO 527-1/-2

2.0 % 2.0 % 50%RH; ISO 527-1/-2

拉伸模量 11.0 GPa 1600 ksi 50%RH; ISO 527-1/-2

12.0 GPa 1740 ksi DAM; ISO 527-1/-2

弯曲强度 225 MPa 32600 psi 50%RH; ISO 178

250 MPa 36300 psi DAM; ISO 178

弯曲模量 10.5 GPa 1520 ksi DAM; ISO 178

割线模量 6.52 GPa
@Strain 1.84 %, Temperature 40.0 °C
945 ksi
@Strain 1.84 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

8.5587 GPa
@Strain 0.920 %, Temperature 40.0 °C
1241.4 ksi
@Strain 0.920 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

8.69 GPa
@Strain 1.60 %, Temperature 23.0 °C
1260 ksi
@Strain 1.60 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.62 g/cc	0.0585 lb/in3	DAM; ISO 1183
粘度测试	120 cm3/g	120 cm3/g	DAM; ISO 307 1157 1628
线性成型收缩率,Flow	0.0030 cm/cm	0.0030 in/in	DAM; ISO 294-4 2577
线性成型收缩率，横向	0.0080 cm/cm	0.0080 in/in	DAM; ISO 294-4 2577
熔体流动速率	26 g/10 min @Load 2.16 kg, Temperature 325 °C	26 g/10 min @Load 4.76 lb, Temperature 617 °F	DAM; cm3/10min; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	150 MPa	21800 psi	50%RH; ISO 527-1/-2
	170 MPa	24700 psi	DAM; ISO 527-1/-2
抗张强度	18.83 MPa @Strain 0.330 %, Temperature 150 °C	2731 psi @Strain 0.330 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	20.45 MPa @Strain 0.290 %, Temperature 90.0 °C	2966 psi @Strain 0.290 %, Temperature 194 °F	50%RH; ISO 11403-1 -2
	21.71 MPa @Strain 0.180 %, Temperature 0.000 °C	3149 psi @Strain 0.180 %, Temperature 32.0 °F	50%RH; ISO 11403-1 -2
	22.15 MPa @Strain 0.350 %, Temperature 150 °C	3213 psi @Strain 0.350 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	22.19 MPa @Strain 0.190 %, Temperature 40.0 °C	3218 psi @Strain 0.190 %, Temperature 104 °F	DAM; ISO 11403-1 -2
	22.3 MPa @Strain 0.180 %, Temperature -20.0 °C	3230 psi @Strain 0.180 %, Temperature -4.00 °F	50%RH; ISO 11403-1 -2
	22.54 MPa @Strain 0.260 %, Temperature 90.0 °C	3269 psi @Strain 0.260 %, Temperature 194 °F	DAM; ISO 11403-1 -2
	22.73 MPa @Strain 0.240 %, Temperature 40.0 °C	3297 psi @Strain 0.240 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	22.8 MPa @Strain 0.190 %, Temperature 0.000 °C	3310 psi @Strain 0.190 %, Temperature 32.0 °F	DAM; ISO 11403-1 -2
	23.63 MPa @Strain 0.210 %, Temperature 23.0 °C	3427 psi @Strain 0.210 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	25.24 MPa @Strain 0.210 %, Temperature -20.0 °C	3661 psi @Strain 0.210 %, Temperature -4.00 °F	DAM; ISO 11403-1 -2
	25.57 MPa @Strain 0.200 %, Temperature 23.0 °C	3709 psi @Strain 0.200 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	52.02 MPa @Strain 1.32 %, Temperature 150 °C	7545 psi @Strain 1.32 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	60.09 MPa @Strain 1.37 %, Temperature 150 °C	8715 psi @Strain 1.37 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	62.98 MPa @Strain 1.17 %, Temperature 90.0 °C	9134 psi @Strain 1.17 %, Temperature 194 °F	50%RH; ISO 11403-1 -2
	65.3 MPa @Strain 2.32 %, Temperature 150 °C	9470 psi @Strain 2.32 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	69.2 MPa @Strain 3.31 %, Temperature 150 °C	10000 psi @Strain 3.31 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	74.6 MPa @Strain 1.00 %, Temperature 90.0 °C	10800 psi @Strain 1.00 %, Temperature 194 °F	DAM; ISO 11403-1 -2
	75.91 MPa @Strain 2.39 %, Temperature 150 °C	11010 psi @Strain 2.39 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	78.74 MPa @Strain 0.920 %, Temperature 40.0 °C	11420 psi @Strain 0.920 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	80.8 MPa @Strain 3.40 %, Temperature 150 °C	11700 psi @Strain 3.40 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	82.4 MPa @Strain 2.03 %, Temperature 90.0 °C	12000 psi @Strain 2.03 %, Temperature 194 °F	50%RH; ISO 11403-1 -2
	82.87 MPa @Strain 0.720 %, Temperature 40.0 °C	12020 psi @Strain 0.720 %, Temperature 104 °F	DAM; ISO 11403-1 -2
	85.18 MPa @Strain 0.730 %, Temperature 0.000 °C	12350 psi @Strain 0.730 %, Temperature 32.0 °F	50%RH; ISO 11403-1 -2
	87.81 MPa @Strain 0.810 %, Temperature 23.0 °C	12740 psi @Strain 0.810 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	88.7 MPa @Strain 0.730 %, Temperature -20.0 °C	12900 psi @Strain 0.730 %, Temperature -4.00 °F	50%RH; ISO 11403-1 -2
	88.9 MPa @Strain 2.91 %, Temperature 90.0 °C	12900 psi @Strain 2.91 %, Temperature 194 °F	50%RH; ISO 11403-1 -2
	91.67 MPa @Strain 0.770 %, Temperature 0.000 °C	13300 psi @Strain 0.770 %, Temperature 32.0 °F	DAM; ISO 11403-1 -2
	91.76 MPa @Strain 0.760 %, Temperature 23.0 °C	13310 psi @Strain 0.760 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	97.54 MPa @Strain 0.800 %, Temperature -20.0 °C	14150 psi @Strain 0.800 %, Temperature -4.00 °F	DAM; ISO 11403-1 -2
	104.12 MPa @Strain 1.76 %, Temperature 90.0 °C	15101 psi @Strain 1.76 %, Temperature 194 °F	DAM; ISO 11403-1 -2
	112.47 MPa @Strain 1.62 %, Temperature 40.0 °C	16312 psi @Strain 1.62 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	118.53 MPa @Strain 2.50 %, Temperature 90.0 °C	17191 psi @Strain 2.50 %, Temperature 194 °F	DAM; ISO 11403-1 -2
	128.53 MPa @Strain 1.27 %, Temperature 40.0 °C	18642 psi @Strain 1.27 %, Temperature 104 °F	DAM; ISO 11403-1 -2
	129.37 MPa @Strain 1.40 %, Temperature 23.0 °C	18764 psi @Strain 1.40 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	130.1 MPa @Strain 2.30 %, Temperature 40.0 °C	18870 psi @Strain 2.30 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	132.82 MPa @Strain 1.26 %, Temperature 0.000 °C	19264 psi @Strain 1.26 %, Temperature 32.0 °F	50%RH; ISO 11403-1 -2
	140.43 MPa @Strain 1.34 %, Temperature 23.0 °C	20368 psi @Strain 1.34 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	141.24 MPa @Strain 1.27 %, Temperature -20.0 °C	20485 psi @Strain 1.27 %, Temperature -4.00 °F	50%RH; ISO 11403-1 -2
	143.2 MPa @Strain 1.33 %, Temperature 0.000 °C	20770 psi @Strain 1.33 %, Temperature 32.0 °F	DAM; ISO 11403-1 -2
	153.44 MPa @Strain 2.00 %, Temperature 23.0 °C	22255 psi @Strain 2.00 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	154.25 MPa @Strain 1.41 %, Temperature -20.0 °C	22372 psi @Strain 1.41 %, Temperature -4.00 °F	DAM; ISO 11403-1 -2
	157.6 MPa @Strain 1.80 %, Temperature 40.0 °C	22860 psi @Strain 1.80 %, Temperature 104 °F	DAM; ISO 11403-1 -2
	163.4 MPa @Strain 1.80 %, Temperature 0.000 °C	23700 psi @Strain 1.80 %, Temperature 32.0 °F	50%RH; ISO 11403-1 -2
	165.5 MPa @Strain 1.80 %, Temperature 23.0 °C	24000 psi @Strain 1.80 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	176.85 MPa @Strain 1.91 %, Temperature 0.000 °C	25650 psi @Strain 1.91 %, Temperature 32.0 °F	DAM; ISO 11403-1 -2
	177.53 MPa @Strain 1.80 %, Temperature -20.0 °C	25749 psi @Strain 1.80 %, Temperature -4.00 °F	50%RH; ISO 11403-1 -2
	188.54 MPa @Strain 2.00 %, Temperature -20.0 °C	27345 psi @Strain 2.00 %, Temperature -4.00 °F	DAM; ISO 11403-1 -2
伸长率 (断裂)	2.0 %	2.0 %	DAM; ISO 527-1/-2
	2.0 %	2.0 %	50%RH; ISO 527-1/-2
拉伸模量	11.0 GPa	1600 ksi	50%RH; ISO 527-1/-2
	12.0 GPa	1740 ksi	DAM; ISO 527-1/-2
弯曲强度	225 MPa	32600 psi	50%RH; ISO 178
	250 MPa	36300 psi	DAM; ISO 178
弯曲模量	10.5 GPa	1520 ksi	DAM; ISO 178
割线模量	6.52 GPa @Strain 1.84 %, Temperature 40.0 °C	945 ksi @Strain 1.84 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	8.5587 GPa @Strain 0.920 %, Temperature 40.0 °C	1241.4 ksi @Strain 0.920 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	8.69 GPa @Strain 1.60 %, Temperature 23.0 °C	1260 ksi @Strain 1.60 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2

美国杜邦PA66 HTN51G15HSL NC010 15%玻纤增强高刚性耐高温耐热老化。

美国杜邦PA66 HTN51G15HSL BK083 15%玻纤增强高刚性耐高温耐热老化耐水解级。

美国杜邦PA66 HTNWR51G30 NC010 30%玻纤增强高刚性耐高温防火阻燃。

美国杜邦PA66 HTN51G35L NC010 35%玻纤增强高刚性 UL94-V0

美国杜邦PA66 HTN51G35HSL NC010 35%玻纤增强高刚性耐高温耐热老化。

美国杜邦PA66 HTN51G35HSL BK083 35%玻纤增强高刚性耐高温耐热老化黑色

美国杜邦PA66 HTN51G35EF BK083 35%玻纤增强热稳定耐磨损

美国杜邦PA66 HTN51G35HSLR BK420 35%玻纤增强热稳定耐水解，

美国杜邦PA66 HTN51G35FWS BK083 35%玻纤增强热稳定耐疲劳耐水解级，

美国杜邦PA66 HTN51G35HSLR BK420J 35%玻纤增强热稳定耐疲劳耐水解级

美国杜邦PA66 HTNFR51G35L BK337 35%玻纤增强高刚性防火阻燃。

美国杜邦PA66 HTN51G50HSL BK083 50%玻纤增强热稳定耐水解，

美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强热稳定耐水解耐化学

美国杜邦PA66 HTN51G45HSL BK083 45%玻纤增强热稳定耐水解耐化学

美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强热稳定耐水解耐化学

美国杜邦PA66 HTN52G35HSL BK083 35%玻纤增强高刚性热稳定。

美国杜邦PA66 HTN52G35EF BK420 35%玻纤增强高刚性热稳定

美国杜邦PA66 HTN52G45HSL BK083 45%玻纤增强高刚性热稳定。

美国杜邦PA66 HTNFR52G30NH BK337 30%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G30NH NC010 30%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G30BL NC010 30%玻纤增强高刚性防火阻燃

美国杜邦PA66 HTNFR52G30BL BK337 30%玻纤增强高刚性防火阻燃

美国杜邦PA66 HTNFR52G35NHF BK337 35%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G35NHF WT010 35%玻纤增强高刚性阻燃白色

美国杜邦PA66 HTNFG52G35HSL BK011 35%玻纤增强热稳定食品级

美国杜邦PA66 HTNFG52G35HSLR BK011 35%玻纤增强热稳定耐水解食品级

美国杜邦PA66 HTNFR52G20NH NC010 20%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G45NHF NC010 45%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G45NHF BK337 45%玻纤增强高刚性无卤阻燃黑色

美国杜邦PA66 HTNFR52G45BL BK337 45%玻纤增强高刚性防火阻燃

美国杜邦PA66 HTNLT52G30NH BL662 30%玻纤增强高刚性无卤阻燃蓝色

美国杜邦PA66 HTN59G55LWSF BK083 55%玻纤增强高刚性低吸水

美国杜邦PA66 HTNFE350064 BK544 15%碳纤增强高刚性耐磨损

美国杜邦PA66 HTNFR55G50NHLW BK046 50%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR55G50NHLW NC010 50%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTN510EFT NC010 高抗冲击热稳定高温尼龙树脂

美国杜邦PA66 HTNFE18502 NC010 超韧耐寒抗冲耐高温热稳定

美国杜邦PA66 HTNFE8200 NC010 超韧耐寒抗冲耐高温热稳定

美国杜邦PA66 HTNFE8200 BK431 超高抗冲击强度耐高低温耐疲劳耐化学

美国杜邦PA66 HTN53G50HSLR BK083 50%玻纤增强高刚性耐水解

美国杜邦PA66 HTN53G50HSL NC010 50%玻纤增强高刚性耐水解

美国杜邦PA66 HTN54G15HSLR NC010 15%玻纤增强高抗冲耐水解

美国杜邦PA66 HTN54G15HSL BK031 15%玻纤增强高抗冲耐水解

美国杜邦PA66 HTN54G35HSLR NC010 35%玻纤增强高抗冲耐水解

美国杜邦PA66 HTN42G30EF NC010 30%玻纤增强高刚性热稳定

美国杜邦PA66 HTN53G60LRHF BK083 60%玻纤增强高刚性热稳定

美国杜邦PA66 HTN55G55TLW BK117 55%玻纤增强高抗冲耐低温耐水解

美国杜邦PA66 HTN55G55TLW BK773 55%玻纤增强高抗冲耐低温耐水解

美国杜邦PA66 HTN53G55LWSF BK045P 55%玻纤增强高刚性耐化学

美国杜邦PA66 HTN53G50LWSF BK702A 55%玻纤增强高刚性热稳定

美国杜邦PA66 HTN92G35DH2 BK083 35%玻纤增强高刚性高流动

美国杜邦PA66 HTNFR42G30NH NC010 35%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR42G30NH BK337 35%玻纤增强高刚性无卤阻燃黑色

广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，PA46，PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。

免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。

000 美国杜邦HTN.jpg

000 HTN52G30NH .jpg

000 PA6T 产品图片.jpg

PA66 仓库图片 .jpg

000 广裕公司办公图片.jpg