美国杜邦PPA HTNFR52G30NH BK337 30%玻纤增强高刚性无卤阻燃

DuPont Performance Polymers Zytel? HTN FR52G30NH NC010 Polyphthalamide (PPA) (Unverified Data**)

Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 30% Glass Fiber Reinforced

DuPont Performance Polymers

产品说明:

30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide

Zytel HTNFR52G30NH NC010 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It is also a PPA resin and it uses a non-halogenated fla

Information provided by DuPont Performance Polymers

DuPont Performance Polymers Zytel? HTN FR52G30NH NC010 Polyphthalamide (PPA) (Unverified Data**) 物性表

物理性能额定值 (公制) 额定值 (英制) 测试方法

密度 1.44 g/cc 0.0520 lb/in3 DAM; ISO 1183

线性成型收缩率,Flow 0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577

线性成型收缩率，横向 0.010 cm/cm 0.010 in/in DAM; ISO 294-4 2577

机械性能额定值 (公制) 额定值 (英制) 测试方法

抗张强度(断裂) 130 MPa 18900 psi 50%RH; ISO 527-1/-2

150 MPa 21800 psi DAM; ISO 527-1/-2

抗张强度 9.87 MPa
@Strain 0.200 %, Temperature 150 °C
1430 psi
@Strain 0.200 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

11.62 MPa
@Strain 0.110 %, Temperature 40.0 °C
1685 psi
@Strain 0.110 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

12.69 MPa
@Strain 0.110 %, Temperature -40.0 °C
1841 psi
@Strain 0.110 %, Temperature -40.0 °F
50%RH; ISO 11403-1 -2

13.04 MPa
@Strain 0.110 %, Temperature 23.0 °C
1891 psi
@Strain 0.110 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

13.14 MPa
@Strain 0.270 %, Temperature 175 °C
1906 psi
@Strain 0.270 %, Temperature 347 °F
DAM; ISO 11403-1 -2

13.72 MPa
@Strain 0.270 %, Temperature 150 °C
1990 psi
@Strain 0.270 %, Temperature 302 °F
DAM; ISO 11403-1 -2

17.16 MPa
@Strain 0.140 %, Temperature 23.0 °C
2489 psi
@Strain 0.140 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

19.61 MPa
@Strain 0.160 %, Temperature -40.0 °C
2844 psi
@Strain 0.160 %, Temperature -40.0 °F
DAM; ISO 11403-1 -2

31.31 MPa
@Strain 0.870 %, Temperature 150 °C
4541 psi
@Strain 0.870 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

34.48 MPa
@Strain 1.03 %, Temperature 175 °C
5001 psi
@Strain 1.03 %, Temperature 347 °F
DAM; ISO 11403-1 -2

36.87 MPa
@Strain 1.01 %, Temperature 150 °C
5348 psi
@Strain 1.01 %, Temperature 302 °F
DAM; ISO 11403-1 -2

43.17 MPa
@Strain 0.440 %, Temperature 40.0 °C
6261 psi
@Strain 0.440 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

43.52 MPa
@Strain 1.57 %, Temperature 150 °C
6312 psi
@Strain 1.57 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

46.16 MPa
@Strain 0.440 %, Temperature 23.0 °C
6695 psi
@Strain 0.440 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

46.47 MPa
@Strain 1.85 %, Temperature 175 °C
6740 psi
@Strain 1.85 %, Temperature 347 °F
DAM; ISO 11403-1 -2

49.45 MPa
@Strain 1.73 %, Temperature 150 °C
7172 psi
@Strain 1.73 %, Temperature 302 °F
DAM; ISO 11403-1 -2

50.65 MPa
@Strain 2.30 %, Temperature 150 °C
7346 psi
@Strain 2.30 %, Temperature 302 °F
50%RH; ISO 11403-1 -2

52.7 MPa
@Strain 0.470 %, Temperature -40.0 °C
7640 psi
@Strain 0.470 %, Temperature -40.0 °F
50%RH; ISO 11403-1 -2

52.78 MPa
@Strain 0.470 %, Temperature 23.0 °C
7655 psi
@Strain 0.470 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

53.31 MPa
@Strain 2.79 %, Temperature 175 °C
7732 psi
@Strain 2.79 %, Temperature 347 °F
DAM; ISO 11403-1 -2

58.12 MPa
@Strain 2.61 %, Temperature 150 °C
8430 psi
@Strain 2.61 %, Temperature 302 °F
DAM; ISO 11403-1 -2

59.93 MPa
@Strain 0.540 %, Temperature -40.0 °C
8692 psi
@Strain 0.540 %, Temperature -40.0 °F
DAM; ISO 11403-1 -2

64.99 MPa
@Strain 0.750 %, Temperature 40.0 °C
9426 psi
@Strain 0.750 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

70.7 MPa
@Strain 0.740 %, Temperature 23.0 °C
10300 psi
@Strain 0.740 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

76.73 MPa
@Strain 0.740 %, Temperature 23.0 °C
11130 psi
@Strain 0.740 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

81.39 MPa
@Strain 1.06 %, Temperature 40.0 °C
11800 psi
@Strain 1.06 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

85.54 MPa
@Strain 0.810 %, Temperature -40.0 °C
12410 psi
@Strain 0.810 %, Temperature -40.0 °F
50%RH; ISO 11403-1 -2

87.91 MPa
@Strain 1.01 %, Temperature 23.0 °C
12750 psi
@Strain 1.01 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

92.6 MPa
@Strain 0.890 %, Temperature -40.0 °C
13400 psi
@Strain 0.890 %, Temperature -40.0 °F
DAM; ISO 11403-1 -2

100.96 MPa
@Strain 1.06 %, Temperature 23.0 °C
14643 psi
@Strain 1.06 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

111.33 MPa
@Strain 1.13 %, Temperature -40.0 °C
16147 psi
@Strain 1.13 %, Temperature -40.0 °F
50%RH; ISO 11403-1 -2

112.01 MPa
@Strain 2.21 %, Temperature 40.0 °C
16246 psi
@Strain 2.21 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

124.37 MPa
@Strain 1.29 %, Temperature -40.0 °C
18038 psi
@Strain 1.29 %, Temperature -40.0 °F
DAM; ISO 11403-1 -2

125 MPa
@Strain 1.97 %, Temperature 23.0 °C
18100 psi
@Strain 1.97 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

伸长率 (断裂) 2.0 % 2.0 % 50%RH; ISO 527-1/-2

2.2 % 2.2 % DAM; ISO 527-1/-2

拉伸模量 10.5 GPa 1520 ksi DAM; ISO 527-1/-2

10.5 GPa 1520 ksi 50%RH; ISO 527-1/-2

弯曲强度 200 MPa 29000 psi 50%RH; ISO 178

230 MPa 33400 psi DAM; ISO 178

弯曲模量 9.00 GPa 1310 ksi DAM; ISO 178

10.0 GPa 1450 ksi 50%RH; ISO 178

割线模量 1.98 GPa
@Strain 3.45 %, Temperature 100 °C
287 ksi
@Strain 3.45 %, Temperature 212 °F
50%RH; ISO 11403-1 -2

2.69 GPa
@Strain 2.38 %, Temperature 100 °C
390 ksi
@Strain 2.38 %, Temperature 212 °F
50%RH; ISO 11403-1 -2

2.85 GPa
@Strain 3.14 %, Temperature 100 °C
414 ksi
@Strain 3.14 %, Temperature 212 °F
DAM; ISO 11403-1 -2

3.562 GPa
@Strain 1.50 %, Temperature 100 °C
516.6 ksi
@Strain 1.50 %, Temperature 212 °F
50%RH; ISO 11403-1 -2

3.80 GPa
@Strain 2.17 %, Temperature 100 °C
551 ksi
@Strain 2.17 %, Temperature 212 °F
DAM; ISO 11403-1 -2

4.80 GPa
@Strain 1.36 %, Temperature 100 °C
697 ksi
@Strain 1.36 %, Temperature 212 °F
DAM; ISO 11403-1 -2

4.84 GPa
@Strain 0.700 %, Temperature 100 °C
701 ksi
@Strain 0.700 %, Temperature 212 °F
50%RH; ISO 11403-1 -2

5.18 GPa
@Strain 2.11 %, Temperature 80.0 °C
751 ksi
@Strain 2.11 %, Temperature 176 °F
DAM; ISO 11403-1 -2

6.07 GPa
@Strain 1.75 %, Temperature 40.0 °C
880 ksi
@Strain 1.75 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

6.14 GPa
@Strain 0.710 %, Temperature 100 °C
891 ksi
@Strain 0.710 %, Temperature 212 °F
DAM; ISO 11403-1 -2

6.42 GPa
@Strain 1.47 %, Temperature 80.0 °C
931 ksi
@Strain 1.47 %, Temperature 176 °F
DAM; ISO 11403-1 -2

6.43 GPa
@Strain 0.110 %, Temperature 100 °C
932 ksi
@Strain 0.110 %, Temperature 212 °F
50%RH; ISO 11403-1 -2

7.14 GPa
@Strain 1.27 %, Temperature 40.0 °C
1040 ksi
@Strain 1.27 %, Temperature 104 °F
50%RH; ISO 11403-1 -2

7.16 GPa
@Strain 1.61 %, Temperature 23.0 °C
1040 ksi
@Strain 1.61 %, Temperature 73.4 °F
50%RH; ISO 11403-1 -2

7.74 GPa
@Strain 0.930 %, Temperature 80.0 °C
1120 ksi
@Strain 0.930 %, Temperature 176 °F
DAM; ISO 11403-1 -2

7.79 GPa
@Strain 0.190 %, Temperature 100 °C
1130 ksi
@Strain 0.190 %, Temperature 212 °F
DAM; ISO 11403-1 -2

7.80 GPa
@Strain 1.83 %, Temperature 23.0 °C
1130 ksi
@Strain 1.83 %, Temperature 73.4 °F
DAM; ISO 11403-1 -2

8.07 GPa
@Strain 2.22 %, Temperature -40.0 °C
1170 ksi
@Strain 2.22 %, Temperature -40.0 °F
DAM; ISO 11403-1 -2

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.44 g/cc	0.0520 lb/in3	DAM; ISO 1183
线性成型收缩率,Flow	0.0030 cm/cm	0.0030 in/in	DAM; ISO 294-4 2577
线性成型收缩率，横向	0.010 cm/cm	0.010 in/in	DAM; ISO 294-4 2577

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	130 MPa	18900 psi	50%RH; ISO 527-1/-2
	150 MPa	21800 psi	DAM; ISO 527-1/-2
抗张强度	9.87 MPa @Strain 0.200 %, Temperature 150 °C	1430 psi @Strain 0.200 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	11.62 MPa @Strain 0.110 %, Temperature 40.0 °C	1685 psi @Strain 0.110 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	12.69 MPa @Strain 0.110 %, Temperature -40.0 °C	1841 psi @Strain 0.110 %, Temperature -40.0 °F	50%RH; ISO 11403-1 -2
	13.04 MPa @Strain 0.110 %, Temperature 23.0 °C	1891 psi @Strain 0.110 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	13.14 MPa @Strain 0.270 %, Temperature 175 °C	1906 psi @Strain 0.270 %, Temperature 347 °F	DAM; ISO 11403-1 -2
	13.72 MPa @Strain 0.270 %, Temperature 150 °C	1990 psi @Strain 0.270 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	17.16 MPa @Strain 0.140 %, Temperature 23.0 °C	2489 psi @Strain 0.140 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	19.61 MPa @Strain 0.160 %, Temperature -40.0 °C	2844 psi @Strain 0.160 %, Temperature -40.0 °F	DAM; ISO 11403-1 -2
	31.31 MPa @Strain 0.870 %, Temperature 150 °C	4541 psi @Strain 0.870 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	34.48 MPa @Strain 1.03 %, Temperature 175 °C	5001 psi @Strain 1.03 %, Temperature 347 °F	DAM; ISO 11403-1 -2
	36.87 MPa @Strain 1.01 %, Temperature 150 °C	5348 psi @Strain 1.01 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	43.17 MPa @Strain 0.440 %, Temperature 40.0 °C	6261 psi @Strain 0.440 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	43.52 MPa @Strain 1.57 %, Temperature 150 °C	6312 psi @Strain 1.57 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	46.16 MPa @Strain 0.440 %, Temperature 23.0 °C	6695 psi @Strain 0.440 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	46.47 MPa @Strain 1.85 %, Temperature 175 °C	6740 psi @Strain 1.85 %, Temperature 347 °F	DAM; ISO 11403-1 -2
	49.45 MPa @Strain 1.73 %, Temperature 150 °C	7172 psi @Strain 1.73 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	50.65 MPa @Strain 2.30 %, Temperature 150 °C	7346 psi @Strain 2.30 %, Temperature 302 °F	50%RH; ISO 11403-1 -2
	52.7 MPa @Strain 0.470 %, Temperature -40.0 °C	7640 psi @Strain 0.470 %, Temperature -40.0 °F	50%RH; ISO 11403-1 -2
	52.78 MPa @Strain 0.470 %, Temperature 23.0 °C	7655 psi @Strain 0.470 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	53.31 MPa @Strain 2.79 %, Temperature 175 °C	7732 psi @Strain 2.79 %, Temperature 347 °F	DAM; ISO 11403-1 -2
	58.12 MPa @Strain 2.61 %, Temperature 150 °C	8430 psi @Strain 2.61 %, Temperature 302 °F	DAM; ISO 11403-1 -2
	59.93 MPa @Strain 0.540 %, Temperature -40.0 °C	8692 psi @Strain 0.540 %, Temperature -40.0 °F	DAM; ISO 11403-1 -2
	64.99 MPa @Strain 0.750 %, Temperature 40.0 °C	9426 psi @Strain 0.750 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	70.7 MPa @Strain 0.740 %, Temperature 23.0 °C	10300 psi @Strain 0.740 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	76.73 MPa @Strain 0.740 %, Temperature 23.0 °C	11130 psi @Strain 0.740 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	81.39 MPa @Strain 1.06 %, Temperature 40.0 °C	11800 psi @Strain 1.06 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	85.54 MPa @Strain 0.810 %, Temperature -40.0 °C	12410 psi @Strain 0.810 %, Temperature -40.0 °F	50%RH; ISO 11403-1 -2
	87.91 MPa @Strain 1.01 %, Temperature 23.0 °C	12750 psi @Strain 1.01 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	92.6 MPa @Strain 0.890 %, Temperature -40.0 °C	13400 psi @Strain 0.890 %, Temperature -40.0 °F	DAM; ISO 11403-1 -2
	100.96 MPa @Strain 1.06 %, Temperature 23.0 °C	14643 psi @Strain 1.06 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	111.33 MPa @Strain 1.13 %, Temperature -40.0 °C	16147 psi @Strain 1.13 %, Temperature -40.0 °F	50%RH; ISO 11403-1 -2
	112.01 MPa @Strain 2.21 %, Temperature 40.0 °C	16246 psi @Strain 2.21 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	124.37 MPa @Strain 1.29 %, Temperature -40.0 °C	18038 psi @Strain 1.29 %, Temperature -40.0 °F	DAM; ISO 11403-1 -2
	125 MPa @Strain 1.97 %, Temperature 23.0 °C	18100 psi @Strain 1.97 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
伸长率 (断裂)	2.0 %	2.0 %	50%RH; ISO 527-1/-2
	2.2 %	2.2 %	DAM; ISO 527-1/-2
拉伸模量	10.5 GPa	1520 ksi	DAM; ISO 527-1/-2
	10.5 GPa	1520 ksi	50%RH; ISO 527-1/-2
弯曲强度	200 MPa	29000 psi	50%RH; ISO 178
	230 MPa	33400 psi	DAM; ISO 178
弯曲模量	9.00 GPa	1310 ksi	DAM; ISO 178
	10.0 GPa	1450 ksi	50%RH; ISO 178
割线模量	1.98 GPa @Strain 3.45 %, Temperature 100 °C	287 ksi @Strain 3.45 %, Temperature 212 °F	50%RH; ISO 11403-1 -2
	2.69 GPa @Strain 2.38 %, Temperature 100 °C	390 ksi @Strain 2.38 %, Temperature 212 °F	50%RH; ISO 11403-1 -2
	2.85 GPa @Strain 3.14 %, Temperature 100 °C	414 ksi @Strain 3.14 %, Temperature 212 °F	DAM; ISO 11403-1 -2
	3.562 GPa @Strain 1.50 %, Temperature 100 °C	516.6 ksi @Strain 1.50 %, Temperature 212 °F	50%RH; ISO 11403-1 -2
	3.80 GPa @Strain 2.17 %, Temperature 100 °C	551 ksi @Strain 2.17 %, Temperature 212 °F	DAM; ISO 11403-1 -2
	4.80 GPa @Strain 1.36 %, Temperature 100 °C	697 ksi @Strain 1.36 %, Temperature 212 °F	DAM; ISO 11403-1 -2
	4.84 GPa @Strain 0.700 %, Temperature 100 °C	701 ksi @Strain 0.700 %, Temperature 212 °F	50%RH; ISO 11403-1 -2
	5.18 GPa @Strain 2.11 %, Temperature 80.0 °C	751 ksi @Strain 2.11 %, Temperature 176 °F	DAM; ISO 11403-1 -2
	6.07 GPa @Strain 1.75 %, Temperature 40.0 °C	880 ksi @Strain 1.75 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	6.14 GPa @Strain 0.710 %, Temperature 100 °C	891 ksi @Strain 0.710 %, Temperature 212 °F	DAM; ISO 11403-1 -2
	6.42 GPa @Strain 1.47 %, Temperature 80.0 °C	931 ksi @Strain 1.47 %, Temperature 176 °F	DAM; ISO 11403-1 -2
	6.43 GPa @Strain 0.110 %, Temperature 100 °C	932 ksi @Strain 0.110 %, Temperature 212 °F	50%RH; ISO 11403-1 -2
	7.14 GPa @Strain 1.27 %, Temperature 40.0 °C	1040 ksi @Strain 1.27 %, Temperature 104 °F	50%RH; ISO 11403-1 -2
	7.16 GPa @Strain 1.61 %, Temperature 23.0 °C	1040 ksi @Strain 1.61 %, Temperature 73.4 °F	50%RH; ISO 11403-1 -2
	7.74 GPa @Strain 0.930 %, Temperature 80.0 °C	1120 ksi @Strain 0.930 %, Temperature 176 °F	DAM; ISO 11403-1 -2
	7.79 GPa @Strain 0.190 %, Temperature 100 °C	1130 ksi @Strain 0.190 %, Temperature 212 °F	DAM; ISO 11403-1 -2
	7.80 GPa @Strain 1.83 %, Temperature 23.0 °C	1130 ksi @Strain 1.83 %, Temperature 73.4 °F	DAM; ISO 11403-1 -2
	8.07 GPa @Strain 2.22 %, Temperature -40.0 °C	1170 ksi @Strain 2.22 %, Temperature -40.0 °F	DAM; ISO 11403-1 -2

美国杜邦PA66 HTN51G15HSL NC010 15%玻纤增强高刚性耐高温耐热老化。

美国杜邦PA66 HTN51G15HSL BK083 15%玻纤增强高刚性耐高温耐热老化耐水解级。

美国杜邦PA66 HTNWR51G30 NC010 30%玻纤增强高刚性耐高温防火阻燃。

美国杜邦PA66 HTN51G35L NC010 35%玻纤增强高刚性 UL94-V0

美国杜邦PA66 HTN51G35HSL NC010 35%玻纤增强高刚性耐高温耐热老化。

美国杜邦PA66 HTN51G35HSL BK083 35%玻纤增强高刚性耐高温耐热老化黑色

美国杜邦PA66 HTN51G35EF BK083 35%玻纤增强热稳定耐磨损

美国杜邦PA66 HTN51G35HSLR BK420 35%玻纤增强热稳定耐水解，

美国杜邦PA66 HTN51G35FWS BK083 35%玻纤增强热稳定耐疲劳耐水解级，

美国杜邦PA66 HTN51G35HSLR BK420J 35%玻纤增强热稳定耐疲劳耐水解级

美国杜邦PA66 HTNFR51G35L BK337 35%玻纤增强高刚性防火阻燃。

美国杜邦PA66 HTN51G50HSL BK083 50%玻纤增强热稳定耐水解，

美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强热稳定耐水解耐化学

美国杜邦PA66 HTN51G45HSL BK083 45%玻纤增强热稳定耐水解耐化学

美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强热稳定耐水解耐化学

美国杜邦PA66 HTN52G35HSL BK083 35%玻纤增强高刚性热稳定。

美国杜邦PA66 HTN52G35EF BK420 35%玻纤增强高刚性热稳定

美国杜邦PA66 HTN52G45HSL BK083 45%玻纤增强高刚性热稳定。

美国杜邦PA66 HTNFR52G30NH BK337 30%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G30NH NC010 30%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G30BL NC010 30%玻纤增强高刚性防火阻燃

美国杜邦PA66 HTNFR52G30BL BK337 30%玻纤增强高刚性防火阻燃

美国杜邦PA66 HTNFR52G35NHF BK337 35%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G35NHF WT010 35%玻纤增强高刚性阻燃白色

美国杜邦PA66 HTNFG52G35HSL BK011 35%玻纤增强热稳定食品级

美国杜邦PA66 HTNFG52G35HSLR BK011 35%玻纤增强热稳定耐水解食品级

美国杜邦PA66 HTNFR52G20NH NC010 20%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G45NHF NC010 45%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR52G45NHF BK337 45%玻纤增强高刚性无卤阻燃黑色

美国杜邦PA66 HTNFR52G45BL BK337 45%玻纤增强高刚性防火阻燃

美国杜邦PA66 HTNLT52G30NH BL662 30%玻纤增强高刚性无卤阻燃蓝色

美国杜邦PA66 HTN59G55LWSF BK083 55%玻纤增强高刚性低吸水

美国杜邦PA66 HTNFE350064 BK544 15%碳纤增强高刚性耐磨损

美国杜邦PA66 HTNFR55G50NHLW BK046 50%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR55G50NHLW NC010 50%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTN510EFT NC010 高抗冲击热稳定高温尼龙树脂

美国杜邦PA66 HTNFE18502 NC010 超韧耐寒抗冲耐高温热稳定

美国杜邦PA66 HTNFE8200 NC010 超韧耐寒抗冲耐高温热稳定

美国杜邦PA66 HTNFE8200 BK431 超高抗冲击强度耐高低温耐疲劳耐化学

美国杜邦PA66 HTN53G50HSLR BK083 50%玻纤增强高刚性耐水解

美国杜邦PA66 HTN53G50HSL NC010 50%玻纤增强高刚性耐水解

美国杜邦PA66 HTN54G15HSLR NC010 15%玻纤增强高抗冲耐水解

美国杜邦PA66 HTN54G15HSL BK031 15%玻纤增强高抗冲耐水解

美国杜邦PA66 HTN54G35HSLR NC010 35%玻纤增强高抗冲耐水解

美国杜邦PA66 HTN42G30EF NC010 30%玻纤增强高刚性热稳定

美国杜邦PA66 HTN53G60LRHF BK083 60%玻纤增强高刚性热稳定

美国杜邦PA66 HTN55G55TLW BK117 55%玻纤增强高抗冲耐低温耐水解

美国杜邦PA66 HTN55G55TLW BK773 55%玻纤增强高抗冲耐低温耐水解

美国杜邦PA66 HTN53G55LWSF BK045P 55%玻纤增强高刚性耐化学

美国杜邦PA66 HTN53G50LWSF BK702A 55%玻纤增强高刚性热稳定

美国杜邦PA66 HTN92G35DH2 BK083 35%玻纤增强高刚性高流动

美国杜邦PA66 HTNFR42G30NH NC010 35%玻纤增强高刚性无卤阻燃

美国杜邦PA66 HTNFR42G30NH BK337 35%玻纤增强高刚性无卤阻燃黑色

广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，PA46，PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。

免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。