美国杜邦PPA HTN52G35HSL BK083 35%玻纤增强 高刚性 热稳定。
DuPont Performance Polymers Zytel? HTN 52G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 40% Glass Fiber Reinforced
DuPont Performance Polymers
产品说明:
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel? HTN 52G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**) 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | 1.46 g/cc | 0.0527 lb/in3 | DAM; ISO 1183 |
填料含量 | 35 % | 35 % | DAM |
吸水率 | 0.50 %
@Temperature 23.0 °C
|
0.50 %
@Temperature 73.4 °F
|
Immersion 24h; DAM; ISO 62, Similar to |
线性成型收缩率,Flow | 0.0030 cm/cm
@Thickness 2.00 mm
|
0.0030 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
线性成型收缩率,横向 | 0.0090 cm/cm
@Thickness 2.00 mm
|
0.0090 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(断裂) | 187 MPa
@Temperature 23.0 °C
|
27100 psi
@Temperature 73.4 °F
|
DAM; ISO 527 |
伸长率 (断裂) | 2.1 %
@Temperature 23.0 °C
|
2.1 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
拉伸模量 | 11.6 GPa
@Temperature 23.0 °C
|
1680 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 |
弯曲模量 | 10.3 GPa
@Temperature 23.0 °C
|
1490 ksi
@Temperature 73.4 °F
|
DAM; ISO 178 |
简支梁无缺口冲击强度 | 3.50 J/cm2
@Temperature -30.0 °C
|
16.7 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eU |
4.00 J/cm2
@Temperature -30.0 °C
|
19.0 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eU | |
4.50 J/cm2
@Temperature 23.0 °C
|
21.4 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eU | |
简支梁缺口冲击强度 | 0.600 J/cm2
@Temperature -30.0 °C
|
2.86 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eA |
0.700 J/cm2
@Temperature -30.0 °C
|
3.33 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eA | |
0.800 J/cm2
@Temperature 23.0 °C
|
3.81 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | 1.00e+15 ohm-cm
@Temperature 23.0 °C
|
1.00e+15 ohm-cm
@Temperature 73.4 °F
|
DAM; IEC 60093 |
表面电阻 | = 1.00e+15 ohm
@Temperature 23.0 °C
|
= 1.00e+15 ohm
@Temperature 73.4 °F
|
DAM; IEC 60093 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 | 500 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
278 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ISO 11359-1/-2 |
500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
线性热膨胀系数,横向流动 | 61.0 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
33.9 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ISO 11359-1/-2 |
67.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
37.2 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
80.0 μm/m-°C
@Temperature 55.0 - 160 °C
|
44.4 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ISO 11359-1/-2 | |
熔融温度 | 310 °C | 590 °F | 10°C/min, First Heat; DAM; ISO 11357-1/-3 |
载荷下热变形温度(1.8 MPa) | 285 °C | 545 °F | DAM; ISO 75-1/-2 |
UL RTI | 150 °C
@Thickness 0.750 mm
|
302 °F
@Thickness 0.0295 in
|
DAM; UL 746B |
150 °C
@Thickness 1.50 mm
|
302 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
150 °C
@Thickness 3.00 mm
|
302 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
UL RTI,机械冲击 | 125 °C
@Thickness 0.750 mm
|
257 °F
@Thickness 0.0295 in
|
DAM; UL 746B |
125 °C
@Thickness 3.00 mm
|
257 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
UL RTI,机械无冲击 | 130 °C
@Thickness 0.750 mm
|
266 °F
@Thickness 0.0295 in
|
DAM; UL 746B |
150 °C
@Thickness 3.00 mm
|
302 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
可燃性(UL94) | HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
DAM; IEC 60695-11-10 |
HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; IEC 60695-11-10 | |
HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; IEC 60695-11-10 | |
HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
DAM; UL94 | |
HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; UL94 | |
HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; UL94 | |
灼热丝易燃指数 | 700 °C
@Thickness 1.50 mm
|
1290 °F
@Thickness 0.0591 in
|
DAM; IEC 60695-2-12 |
725 °C
@Thickness 1.50 mm
|
1340 °F
@Thickness 0.0591 in
|
DAM; Ignition; IEC 60695-2-13 | |
750 °C
@Thickness 0.750 mm
|
1380 °F
@Thickness 0.0295 in
|
DAM; IEC 60695-2-12 | |
775 °C
@Thickness 0.750 mm
|
1430 °F
@Thickness 0.0295 in
|
DAM; Ignition; IEC 60695-2-13 | |
775 °C
@Thickness 3.00 mm
|
1430 °F
@Thickness 0.118 in
|
DAM; Ignition; IEC 60695-2-13 | |
850 °C
@Thickness 3.00 mm
|
1560 °F
@Thickness 0.118 in
|
DAM; IEC 60695-2-12 |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
加工(熔体)温度 | 325 °C | 617 °F | DAM; Optimum |
320 - 330 °C | 608 - 626 °F | DAM | |
模具温度 | 85.0 - 105 °C | 185 - 221 °F | DAM |
干燥温度 | 100 °C | 212 °F | DAM |
干燥时间 | 6.00 - 8.00 hour | 6.00 - 8.00 hour | DAM |
水分含量 | = 0.10 % | = 0.10 % | DAM |
材料描述 | 测试方法 | |
---|---|---|
添加剂 | Heat Stabilizer | DAM |
Lubricant | DAM | |
外观 | Black Color | DAM |
Filler | Glass Reinforced | DAM |
形式 | Pellets | DAM |
Generic | Polyphthalamide (PPA) | DAM |
Material Status | Current | DAM |
部件标识代码 | PA6T/66-GF35 | ISO 11469; DAM |
PPA-GF35 | SAE J1344; DAM | |
Polymer Family | High performance polyamide | DAM |
Polymer Type | Partially Aromatic PA, PPA | DAM |
加工方法 | Injection Molding | DAM |
产品分类 | Glass Reinforced Resins | DAM |
Region Available - Global | Yes | DAM |
树脂识别 | PA6T/66-GF35 | ISO 1043; DAM |
符合RoHS指令 | Contact Manufacturer | DAM |
美国杜邦PA66 HTN51G15HSL NC010 15%玻纤增强 高刚性 耐高温 耐热老化。
美国杜邦PA66 HTN51G15HSL BK083 15%玻纤增强 高刚性 耐高温 耐热老化 耐水解级。
美国杜邦PA66 HTNWR51G30 NC010 30%玻纤增强 高刚性 耐高温 防火阻燃。
美国杜邦PA66 HTN51G35L NC010 35%玻纤增强 高刚性 UL94-V0
美国杜邦PA66 HTN51G35HSL NC010 35%玻纤增强 高刚性 耐高温 耐热老化。
美国杜邦PA66 HTN51G35HSL BK083 35%玻纤增强 高刚性 耐高温 耐热老化 黑色
美国杜邦PA66 HTN51G35EF BK083 35%玻纤增强 热稳定 耐磨损
美国杜邦PA66 HTN51G35HSLR BK420 35%玻纤增强 热稳定 耐水解,
美国杜邦PA66 HTN51G35FWS BK083 35%玻纤增强 热稳定 耐疲劳 耐水解级,
美国杜邦PA66 HTN51G35HSLR BK420J 35%玻纤增强 热稳定 耐疲劳 耐水解级
美国杜邦PA66 HTNFR51G35L BK337 35%玻纤增强 高刚性 防火阻燃。
美国杜邦PA66 HTN51G50HSL BK083 50%玻纤增强 热稳定 耐水解,
美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强 热稳定 耐水解 耐化学
美国杜邦PA66 HTN51G45HSL BK083 45%玻纤增强 热稳定 耐水解 耐化学
美国杜邦PA66 HTN51G45HSL NC010 45%玻纤增强 热稳定 耐水解 耐化学
美国杜邦PA66 HTN52G35HSL BK083 35%玻纤增强 高刚性 热稳定。
美国杜邦PA66 HTN52G35EF BK420 35%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN52G45HSL BK083 45%玻纤增强 高刚性 热稳定。
美国杜邦PA66 HTNFR52G30NH BK337 30%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G30NH NC010 30%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G30BL NC010 30%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNFR52G30BL BK337 30%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNFR52G35NHF BK337 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G35NHF WT010 35%玻纤增强 高刚性 阻燃白色
美国杜邦PA66 HTNFG52G35HSL BK011 35%玻纤增强 热稳定 食品级
美国杜邦PA66 HTNFG52G35HSLR BK011 35%玻纤增强 热稳定 耐水解 食品级
美国杜邦PA66 HTNFR52G20NH NC010 20%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G45NHF NC010 45%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR52G45NHF BK337 45%玻纤增强 高刚性 无卤阻燃 黑色
美国杜邦PA66 HTNFR52G45BL BK337 45%玻纤增强 高刚性 防火阻燃
美国杜邦PA66 HTNLT52G30NH BL662 30%玻纤增强 高刚性 无卤阻燃 蓝色
美国杜邦PA66 HTN59G55LWSF BK083 55%玻纤增强 高刚性 低吸水
美国杜邦PA66 HTNFE350064 BK544 15%碳纤增强 高刚性 耐磨损
美国杜邦PA66 HTNFR55G50NHLW BK046 50%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR55G50NHLW NC010 50%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTN510EFT NC010 高抗冲击 热稳定 高温尼龙树脂
美国杜邦PA66 HTNFE18502 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 NC010 超韧耐寒抗冲 耐高温 热稳定
美国杜邦PA66 HTNFE8200 BK431 超高抗冲击强度 耐高低温 耐疲劳 耐化学
美国杜邦PA66 HTN53G50HSLR BK083 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN53G50HSL NC010 50%玻纤增强 高刚性 耐水解
美国杜邦PA66 HTN54G15HSLR NC010 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G15HSL BK031 15%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN54G35HSLR NC010 35%玻纤增强 高抗冲 耐水解
美国杜邦PA66 HTN42G30EF NC010 30%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN53G60LRHF BK083 60%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN55G55TLW BK117 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN55G55TLW BK773 55%玻纤增强 高抗冲 耐低温 耐水解
美国杜邦PA66 HTN53G55LWSF BK045P 55%玻纤增强 高刚性 耐化学
美国杜邦PA66 HTN53G50LWSF BK702A 55%玻纤增强 高刚性 热稳定
美国杜邦PA66 HTN92G35DH2 BK083 35%玻纤增强 高刚性 高流动
美国杜邦PA66 HTNFR42G30NH NC010 35%玻纤增强 高刚性 无卤阻燃
美国杜邦PA66 HTNFR42G30NH BK337 35%玻纤增强 高刚性 无卤阻燃 黑色
广裕塑胶现货供应:PP,PE,PVC,ABS,PC,PC/ABS,PA6,PA66,PA46,PA6T,PA9T,PAMXD6,IXEF,PA11,PA12,PBT,PET,PPS,LCP,PEI,PPSU,PSU,PVDF,PEEK,TPU,TPV,TPE,食品级降解塑料(PBAT,PLA,PBS,PBST)等。
免费提供原料:物性表,UL黄卡,随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。