美国杜邦PA6T/XT HTN51G35EF BK083 玻纤增强 耐水解 热稳定 耐磨损
DuPont Performance Polymers Zytel? HTN 51G35EF BK083 Polyphthalamide (PPA) (Unverified Data**)
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 40% Glass Fiber Reinforced
DuPont Performance Polymers
产品说明:
35% Glass Reinforced PPA High Performance Polyamide Developed for Electrical and Electronics Applications
Zytel HTN51G35EF BK083 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin developed for electrical and electron
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel? HTN 51G35EF BK083 Polyphthalamide (PPA) (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.47 g/cc | 0.0531 lb/in3 | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0060 cm/cm | 0.0060 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 220 MPa | 31900 psi | DAM; ISO 527-1/-2 |
| 抗张强度 | 8.88 MPa
@Strain 0.190 %, Temperature 150 °C
|
1290 psi
@Strain 0.190 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 |
| 12.91 MPa
@Strain 0.280 %, Temperature 180 °C
|
1872 psi
@Strain 0.280 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 20.41 MPa
@Strain 0.360 %, Temperature 150 °C
|
2960 psi
@Strain 0.360 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 24.59 MPa
@Strain 0.650 %, Temperature 150 °C
|
3566 psi
@Strain 0.650 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 38.11 MPa
@Strain 1.15 %, Temperature 180 °C
|
5527 psi
@Strain 1.15 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 38.35 MPa
@Strain 1.40 %, Temperature 150 °C
|
5562 psi
@Strain 1.40 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 40.83 MPa
@Strain 0.550 %, Temperature 90.0 °C
|
5922 psi
@Strain 0.550 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 46.25 MPa
@Strain 2.23 %, Temperature 150 °C
|
6708 psi
@Strain 2.23 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 48.71 MPa
@Strain 1.24 %, Temperature 150 °C
|
7065 psi
@Strain 1.24 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 48.84 MPa
@Strain 2.11 %, Temperature 180 °C
|
7084 psi
@Strain 2.11 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 55.6 MPa
@Strain 3.25 %, Temperature 180 °C
|
8060 psi
@Strain 3.25 %, Temperature 356 °F
|
DAM; ISO 11403-1 -2 | |
| 60.42 MPa
@Strain 2.38 %, Temperature 150 °C
|
8763 psi
@Strain 2.38 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 65.19 MPa
@Strain 0.600 %, Temperature 90.0 °C
|
9455 psi
@Strain 0.600 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 66.06 MPa
@Strain 1.14 %, Temperature 90.0 °C
|
9581 psi
@Strain 1.14 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 66.18 MPa
@Strain 3.75 %, Temperature 150 °C
|
9599 psi
@Strain 3.75 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 73.19 MPa
@Strain 0.620 %, Temperature 40.0 °C
|
10620 psi
@Strain 0.620 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 80.45 MPa
@Strain 1.80 %, Temperature 90.0 °C
|
11670 psi
@Strain 1.80 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 83.19 MPa
@Strain 0.720 %, Temperature 23.0 °C
|
12070 psi
@Strain 0.720 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 88.89 MPa
@Strain 2.62 %, Temperature 90.0 °C
|
12890 psi
@Strain 2.62 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 91.36 MPa
@Strain 0.760 %, Temperature 23.0 °C
|
13250 psi
@Strain 0.760 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 97.16 MPa
@Strain 0.780 %, Temperature -20.0 °C
|
14090 psi
@Strain 0.780 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 98.0 MPa
@Strain 0.897 %, Temperature 40.0 °C
|
14200 psi
@Strain 0.897 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 98.97 MPa
@Strain 0.800 %, Temperature 0.000 °C
|
14350 psi
@Strain 0.800 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 102.66 MPa
@Strain 1.02 %, Temperature 90.0 °C
|
14890 psi
@Strain 1.02 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 104.24 MPa
@Strain 0.910 %, Temperature 40.0 °C
|
15119 psi
@Strain 0.910 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 107 MPa
@Strain 0.882 %, Temperature 0.000 °C
|
15500 psi
@Strain 0.882 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 112.48 MPa
@Strain 1.02 %, Temperature 23.0 °C
|
16314 psi
@Strain 1.02 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 116.13 MPa
@Strain 0.930 %, Temperature -20.0 °C
|
16843 psi
@Strain 0.930 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 125.83 MPa
@Strain 1.36 %, Temperature 90.0 °C
|
18250 psi
@Strain 1.36 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 131.27 MPa
@Strain 1.30 %, Temperature 40.0 °C
|
19039 psi
@Strain 1.30 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 134.89 MPa
@Strain 1.14 %, Temperature 0.000 °C
|
19564 psi
@Strain 1.14 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 137.92 MPa
@Strain 1.31 %, Temperature 23.0 °C
|
20004 psi
@Strain 1.31 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 146.77 MPa
@Strain 1.80 %, Temperature 90.0 °C
|
21287 psi
@Strain 1.80 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 153.67 MPa
@Strain 1.28 %, Temperature -20.0 °C
|
22288 psi
@Strain 1.28 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 156.27 MPa
@Strain 1.48 %, Temperature 40.0 °C
|
22665 psi
@Strain 1.48 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 156.32 MPa
@Strain 1.66 %, Temperature 40.0 °C
|
22672 psi
@Strain 1.66 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 159.92 MPa
@Strain 1.46 %, Temperature 23.0 °C
|
23194 psi
@Strain 1.46 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 162.15 MPa
@Strain 1.62 %, Temperature 23.0 °C
|
23518 psi
@Strain 1.62 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 177.86 MPa
@Strain 2.09 %, Temperature 40.0 °C
|
25796 psi
@Strain 2.09 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 181.2 MPa
@Strain 1.65 %, Temperature 0.000 °C
|
26280 psi
@Strain 1.65 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 187.3 MPa
@Strain 1.72 %, Temperature 0.000 °C
|
27170 psi
@Strain 1.72 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 189.71 MPa
@Strain 1.97 %, Temperature 40.0 °C
|
27515 psi
@Strain 1.97 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 191.21 MPa
@Strain 1.74 %, Temperature -20.0 °C
|
27733 psi
@Strain 1.74 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 204.28 MPa
@Strain 1.96 %, Temperature 0.000 °C
|
29628 psi
@Strain 1.96 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 205.31 MPa
@Strain 2.10 %, Temperature 23.0 °C
|
29778 psi
@Strain 2.10 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 210.24 MPa
@Strain 2.06 %, Temperature 0.000 °C
|
30493 psi
@Strain 2.06 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 216.76 MPa
@Strain 2.02 %, Temperature -20.0 °C
|
31438 psi
@Strain 2.02 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 2.4 % | 2.4 % | DAM; ISO 527-1/-2 |
| 拉伸模量 | 12.1 GPa | 1750 ksi | DAM; ISO 527-1/-2 |
| 弯曲强度 | 300 MPa | 43500 psi | DAM; ISO 178 |
| 弯曲模量 | 11.0 GPa | 1600 ksi | DAM; ISO 178 |
| 割线模量 | 1.01 GPa
@Strain 5.47 %, Temperature 200 °C
|
147 ksi
@Strain 5.47 %, Temperature 392 °F
|
DAM; ISO 11403-1 -2 |
| 1.29 GPa
@Strain 4.02 %, Temperature 200 °C
|
187 ksi
@Strain 4.02 %, Temperature 392 °F
|
DAM; ISO 11403-1 -2 | |
| 1.75 GPa
@Strain 2.63 %, Temperature 200 °C
|
254 ksi
@Strain 2.63 %, Temperature 392 °F
|
DAM; ISO 11403-1 -2 | |
| 2.71 GPa
@Strain 1.30 %, Temperature 200 °C
|
393 ksi
@Strain 1.30 %, Temperature 392 °F
|
DAM; ISO 11403-1 -2 | |
| 4.2425 GPa
@Strain 0.400 %, Temperature 200 °C
|
615.33 ksi
@Strain 0.400 %, Temperature 392 °F
|
DAM; ISO 11403-1 -2 | |
| 7.40 GPa
@Strain 2.54 %, Temperature 40.0 °C
|
1070 ksi
@Strain 2.54 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 8.70 GPa
@Strain 2.33 %, Temperature 23.0 °C
|
1260 ksi
@Strain 2.33 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 8.86 GPa
@Strain 2.30 %, Temperature 40.0 °C
|
1280 ksi
@Strain 2.30 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 9.07 GPa
@Strain 1.81 %, Temperature 40.0 °C
|
1320 ksi
@Strain 1.81 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 |