Vydyne? R513H

聚酰胺66

13% 玻璃纤维增强材料

Ascend Performance Materials Operations LLC

产品说明：

Vydyne R513H is general-purpose, 13% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow, and mold release. Glass-reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, higher impact, and better dimensional stability when compared with unreinforced PA66. This product has good chemical resistance to a broad range of chemicals, including many aliphatic and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils.

Vydyne R513H has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts.

Vydyne R513H is heat-stabilized and formulated to minimize the oxidative and thermal degradation of the PA66 polymer when exposed to elevated temperatures for extended periods of time. Vydyne R513H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275° F, with short-term peak temperatures as high as 475° F.

Typical Applications/End Uses:

Vydyne R513H resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips, which require high rigidity and strength.

东莞市崀峰是一般纳税人可以开13%税，主营: ABS、PC/ABS、PBT/ABS、PBT/ASA、PC/ASA、PC/PBT、PC/PTFE、POM/PTFE、POM/FEP、SAS、HDPE、LDPE、GPPS、HIPS(475) 、PP、PE、PPA、PFA、PVDF、PA、PMMA、POM、PC、PBT、PPO、PPS、LCP、TPU、TPR、TPV、TPEE、PTFE、TPE、PVC、K胶、PET、EVA、ASA、PSU、PPU、PUR、PA6T、PA46 PA9T 等高性能（耐高温）塑胶原料,0769-898-761-36手机136-52-520-830,QQ:1873-834-210 周先生:134-234-831-21,Q:64-27-740-36,材料订购说明：提供物性、报价、UL报告、ROSH标准、SGS检测报告,本公司为华东地区长期经销代理韩国乐天化学公司秉承“以诚为本,信誉至上”的经营宗旨,【诚信经营】【服务至上】【品质保障】创立了自己的经营理念.

Vydyne? R513H 物性表

基本信息
黄卡编号	E70062-249082
填料/增强材料	玻璃纤维增强材料, 13% 填料按重量
添加剂	热稳定剂润滑剂
特性	刚性，高高强度抗溶剂性良好的流动性耐化学性良好耐汽油性耐油性能耐油脂性能热稳定性润滑脱模性能良好
用途	齿轮动力/其它工具汽车的发动机罩下的零件外壳
机构评级	ASTM D 4066 PA0121G15 ASTM D 6779 PA0121G15
UL文件号	E70062
外观	自然色
形式	粒子
加工方法	注射成型
多点数据	Isothermal Stress vs. Strain (ISO 11403-1)

物理性能	干燥	调节后的	单位制	测试方法
密度	1.23	--	g/cm3	ISO 1183
收缩率				ISO 294-4
垂直流动方向 : 23°C, 2.00 mm	1.0	--	%	ISO 294-4
流动方向 : 23°C, 2.00 mm	0.50	--	%	ISO 294-4
吸水率				ISO 62
23°C, 24 hr	1.0	--	%	ISO 62
平衡, 23°C, 50% RH	2.2	--	%	ISO 62

机械性能	干燥	调节后的	单位制	测试方法
拉伸模量(23°C)	6200	3900	MPa	ISO 527-2
拉伸应力(断裂, 23°C)	115	75.0	MPa	ISO 527-2
拉伸应变(断裂, 23°C)	3.0	13	%	ISO 527-2
弯曲模量(23°C)	5200	3150	MPa	ISO 178
弯曲应力(23°C)	165	106	MPa	ISO 178
泊松比	0.40	--		ISO 527-2

冲击性能	干燥	调节后的	单位制	测试方法
简支梁缺口冲击强度				ISO 179
-30°C	6.0	5.3	kJ/m2	ISO 179
23°C	6.0	7.5	kJ/m2	ISO 179
简支梁无缺口冲击强度				ISO 179
-30°C	31	37	kJ/m2	ISO 179
23°C	38	42	kJ/m2	ISO 179
悬壁梁缺口冲击强度				ISO 180
-30°C	5.0	5.4	kJ/m2	ISO 180
23°C	5.1	8.5	kJ/m2	ISO 180

热性能	干燥	调节后的	单位制	测试方法
热变形温度
0.45 MPa, 未退火	258	--	°C	ISO 75-2/B
1.8 MPa, 未退火	240	--	°C	ISO 75-2/A
熔融温度	260	--	°C	ISO 11357-3
线形热膨胀系数				ISO 11359-2
流动 : 23 到 55°C, 2.00 mm	3.0E-5	--	cm/cm/°C	ISO 11359-2
横向 : 23 到 55°C, 2.00 mm	1.1E-4	--	cm/cm/°C	ISO 11359-2
RTI Elec				UL 746
0.750 mm	140	--	°C	UL 746
1.50 mm	140	--	°C	UL 746
3.00 mm	140	--	°C	UL 746
RTI Imp				UL 746
0.750 mm	120	--	°C	UL 746
1.50 mm	120	--	°C	UL 746
3.00 mm	120	--	°C	UL 746
RTI				UL 746
0.750 mm	125	--	°C	UL 746
1.50 mm	140	--	°C	UL 746
3.00 mm	140	--	°C	UL 746

电气性能	干燥	调节后的	单位制	测试方法
体积电阻率(0.750 mm)	1.0E+13	--	ohms·cm	IEC 60093
介电强度(1.00 mm)	20	--	kV/mm	IEC 60243
耐电弧性(3.00 mm)	PLC 6	--		ASTM D495
漏电起痕指数(3.00 mm)	250 到 399	--	V	IEC 60112
高电弧燃烧指数(HAI)				UL 746
0.750 mm	PLC 0	--		UL 746
1.50 mm	PLC 0	--		UL 746
3.00 mm	PLC 0	--		UL 746
高电压电弧起痕速率 (HVTR)	PLC 1	--		UL 746
热丝引燃 (HWI)				UL 746
0.750 mm	PLC 4	--		UL 746
1.50 mm	PLC 3	--		UL 746
3.00 mm	PLC 4	--		UL 746

可燃性	干燥	调节后的	单位制	测试方法
UL 阻燃等级				UL 94
0.750 mm	HB	--		UL 94
1.50 mm	HB	--		UL 94
3.00 mm	HB	--		UL 94
灼热丝易燃指数				IEC 60695-2-12
0.750 mm	675	--	°C	IEC 60695-2-12
1.50 mm	675	--	°C	IEC 60695-2-12
3.00 mm	675	--	°C	IEC 60695-2-12
热灯丝点火温度				IEC 60695-2-13
0.750 mm	700	--	°C	IEC 60695-2-13
1.50 mm	700	--	°C	IEC 60695-2-13
3.00 mm	700	--	°C	IEC 60695-2-13
极限氧指数	25	--	%	ISO 4589-2

注射	干燥	单位制
干燥温度	80.0	°C
干燥时间	4.0	hr
建议的最大回制料比例	25	%
料筒后部温度	280 到 310	°C
料筒中部温度	280 到 310	°C
料筒前部温度	280 到 310	°C
射嘴温度	280 到 310	°C
加工（熔体）温度	285 到 305	°C
模具温度	65.0 到 95.0	°C