东莞塑运塑胶有限公司
ABS美国英力士H801耐热级
物性表
| 拉伸强度 | ASTM D638/ISO 527 | 15 | kg/cm2(MPa)[Lb/in2] | |
| 断裂伸长率 | ASTM D638/ISO 527 | % | ||
| 拉伸模量 | ASTM D638/ISO 527 | 2400 | kg/cm2(MPa)[Lb/in2] | |
| 伸长率 | ASTM D638/ISO 527 | % | ||
| 弯曲模量 | ASTM D790/ISO 178 | 2300 | kg/cm2(MPa)[Lb/in2] | |
| 弯曲强度 | ASTM D790/ISO 178 | 77 | kg/cm2(MPa)[Lb/in2] | |
| 洛氏硬度 | ASTM D785 | |||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 100 | kg·cm/cm(J/M)ft·lb/in |
| 1/4" -30℃ | ASTM D256/ISO 179 | 90 | kg·cm/cm(J/M)ft·lb/in | |
| 1/8" 23℃ | ASTM D256/ISO 179 | 16 | kg·cm/cm(J/M)ft·lb/in | |
| 1/8" -30℃ | ASTM D256/ISO 179 | 8.0 | kg·cm/cm(J/M)ft·lb/in | |
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 23℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | % | ||
| 比重（密度） | ASTM D792/ISO 1183 | 1.04 | ||
| 成型收缩率 | ASTM D955 | % | ||
| 熔融指数（活动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | 9.0 | g/10min |
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | % | ||
| 热变形温度 | 退火 | ASTM D648/ISO 75 | ℃（℉） | |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | ||
| 维卡软化点 | ASTM D1525/ISO R306 | 104 | ℃（℉） | |
| 熔点 | - | ℃（℉） | ||
| 熄灭性（率） | UL94 | |||
| 线性收缩系数 | ASTM D696/ISO 11359 | mm/mm.℃ | ||
| 备注 | ||||
| 颜色 | ||||
| 特性 | 中等耐热性，增加流量 | |||
| 用处 | ||||
| 枯燥条件 | ||||
| 加工温度 | 射嘴 | ℃ | ||
| 料筒前段 | ℃ | |||
| 料筒中段 | ℃ | |||
| 料筒后段 | ℃ | |||
| 熔体温度 | ℃ | |||
| 模具温度 | ℃ | |||
| 压力 | 注塑压力 | Mpa | ||
| 保压压力 | Mpa | |||
| 背压 | Mpa | |||
| 螺杆转速 | rpm | |||
ABS美国英力士系列
ABS |
美国英力士 |
348 |
ABS |
美国英力士 |
H605 |
ABS |
美国英力士 |
H701 |
ABS |
美国英力士 |
H702 |
ABS |
美国英力士 |
H801 |
ABS |
美国英力士 |
H802 |
ABS |
美国英力士 |
H950 |
ABS |
美国英力士 |
N240 |
ABS |
美国英力士 |
N450 |
ABS |
美国英力士 |
P2H-AT |
ABS |
泰国英力士 |
648 |
ABS |
泰国英力士 |
N240 |
价钱阐明