PPA 美国杜邦 79G13HSL NC010
DuPont Performance Polymers Zytel? 79G13HSL NC010 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.04 g/cc | 0.0376 lb/in3 | |
| 1.21 g/cc | 0.0437 lb/in3 | DAM; ISO 1183 | |
| 吸水率 | 6.5 %
@Thickness 2.00 mm
|
6.5 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 | 2.20 %
@Thickness 2.00 mm
|
2.20 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 | 46700 cP
@Shear Rate 5000 1/s, Temperature 305 °C
|
46700 cP
@Shear Rate 5000 1/s, Temperature 581 °F
|
ISO 11403-1 -2 |
| 50730 cP
@Shear Rate 5000 1/s, Temperature 295 °C
|
50730 cP
@Shear Rate 5000 1/s, Temperature 563 °F
|
ISO 11403-1 -2 | |
| 55340 cP
@Shear Rate 5000 1/s, Temperature 285 °C
|
55340 cP
@Shear Rate 5000 1/s, Temperature 545 °F
|
ISO 11403-1 -2 | |
| 141400 cP
@Shear Rate 500 1/s, Temperature 305 °C
|
141400 cP
@Shear Rate 500 1/s, Temperature 581 °F
|
ISO 11403-1 -2 | |
| 157800 cP
@Shear Rate 500 1/s, Temperature 295 °C
|
157800 cP
@Shear Rate 500 1/s, Temperature 563 °F
|
ISO 11403-1 -2 | |
| 176700 cP
@Shear Rate 500 1/s, Temperature 285 °C
|
176700 cP
@Shear Rate 500 1/s, Temperature 545 °F
|
ISO 11403-1 -2 | |
| 粘度测试 | 150 cm3/g | 150 cm3/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0050 cm/cm | 0.0050 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 74 | 74 | 50%RH; ISO 2039-2 |
| 90 | 90 | DAM; ISO 2039-2 | |
| 抗张强度(断裂) | 67.0 MPa | 9720 psi | 50%RH; ISO 527-1/-2 |
| 118 MPa | 17100 psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | 4.0 % | 4.0 % | DAM; ISO 527-1/-2 |
| 10 % | 10 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 3.70 GPa | 537 ksi | 50%RH; ISO 527-1/-2 |
| 5.10 GPa | 740 ksi | DAM; ISO 527-1/-2 | |
| 悬壁梁缺口冲击强度 | 8.00 kJ/m2 | 3.81 ft-lb/in2 | DAM; ISO 180/1A |
| 9.00 kJ/m2 | 4.28 ft-lb/in2 | 50%RH; ISO 180/1A | |
| 4.00 kJ/m2
@Temperature -30.0 °C
|
1.90 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 180/1A | |
| 6.00 kJ/m2
@Temperature -30.0 °C
|
2.86 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 180/1A | |
| 简支梁无缺口冲击强度 | 5.90 J/cm2 | 28.1 ft-lb/in2 | 50%RH; ISO 179/1eU |
| 6.70 J/cm2 | 31.9 ft-lb/in2 | DAM; ISO 179/1eU | |
| 5.40 J/cm2
@Temperature -30.0 °C
|
25.7 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eU | |
| 5.90 J/cm2
@Temperature -30.0 °C
|
28.1 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.800 J/cm2 | 3.81 ft-lb/in2 | DAM; ISO 179/1eA |
| 1.40 J/cm2 | 6.66 ft-lb/in2 | 50%RH; ISO 179/1eA | |
| 0.600 J/cm2
@Temperature -30.0 °C
|
2.86 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eA | |
| 0.600 J/cm2
@Temperature -30.0 °C
|
2.86 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | 4030 MPa
@Time 3600 sec
|
585000 psi
@Time 1.00 hour
|
50%RH; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 3180 MPa
@Time 3.60e+6 sec
|
461000 psi
@Time 1000 hour
|
50%RH; ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | 250 V | 250 V | DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 50.0 μm/m-°C | 27.8 μin/in-°F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 130 μm/m-°C | 72.2 μin/in-°F | DAM; ISO 11359-1/-2 |
| 熔融温度 | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 260 °C | 500 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 242 °C | 468 °F | DAM; ISO 75-1/-2 |
| 维卡软化温度 | 239 °C | 462 °F | DAM; 50°C/h 50N; ISO 306 |
| 可燃性(UL94) | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; IEC 60695-11-10 |
| HB
@Thickness 0.800 mm
|
HB
@Thickness 0.0315 in
|
DAM; IEC 60695-11-10 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Additives | Lubricants | |
| Delivery Form | Pellets | |
| Odour | class 4 | VDA 270; C3 |
| 加工 | Injection Moulding | |
| 供货地区 | Europe | |
| Near East/Africa | ||
| 特殊特性 | Heat stabilised or stable to heat | |
| UL recognition | UL | DAM |