Asaflex? 825

苯乙烯-丁二烯-苯乙烯嵌段共聚物

AKelastomers

产品说明：

Injection- and blow-molding grade. For transparent products with superior impact strength. Blended with GPPS (general-purpose polystyrene) or SC for films with good thermal stability. Capability for profile-extrusion products. It is supplied in pellet form.
Cosmetics caps, stationery goods, other consumer goods. Blended with GPPS for PSP* laminate films and IC magazine rails, and with SC* for shrink films.
* Styrenic copolymer from PS Japan Corp. similar to Asaflex? 825 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS.

Asaflex? 825 物性表

基本信息
特性	共聚物抗撞击性，高清晰度，高热稳定性，良好
用途	Cosmetic Packaging Water Sports Equipment 薄膜层压板文具消费品应用领域型材
外观	清晰/透明
形式	粒子
加工方法	吹塑成型型材挤出成型注射成型

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm3	ISO 1183
熔流率（熔体流动速率）(200°C/5.0 kg)	6.0	g/10 min	ISO 1133
收缩率	0.20 到 0.80	%
吸水率(23°C, 24 hr)	0.10	%	ISO 62

硬度	额定值	单位制	测试方法
洛氏硬度(R 计秤)	55		ISO 2039-2
肖氏硬度(邵氏 D)	71		ISO 868

机械性能	额定值	单位制	测试方法
拉伸应力(屈服)	27.0	MPa	ISO 527-2/5
拉伸应变(断裂)	200	%	ISO 527-2/5
弯曲模量	1200	MPa	ISO 178
弯曲应力	37.0	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度(完全断裂)	2.0	kJ/m2	ISO 179
简支梁无缺口冲击强度(完全断裂)	100	kJ/m2	ISO 179

热性能	额定值	单位制	测试方法
热变形温度(1.8 MPa, 未退火)	57.0	°C	ISO 75-2/A
维卡软化温度	82.0	°C	ISO 306/A50

光学性能	额定值	单位制	测试方法
透射率(2000 μm)	90.0	%	ISO 3537
雾度(2000 μm)	0.50	%	ISO 3537

产品实拍：