茂名市顺源塑料有限公司
高密度聚乙烯(HDPE) TR144
| 性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
| 基本性能
|
密度
|
ASTM D-1505
|
0.946
|
g/cm3
|
|
| 熔体流动速率
|
190℃/2.16kg
|
ASTM D-1238
|
0.2
|
g/10min
|
|
| 190℃/2.16kg(HLMI)
|
ASTM D-1238
|
15
|
g/10min
|
||
| 机械性能
|
挠曲模量
|
ASTM D-790
|
1103
|
MPa
|
|
| 落镖冲击强度
|
ASTM D-1709
|
100
|
g
|
||
| 拉伸屈服强度(MD)
|
ASTM D-882
|
26
|
MPa
|
||
| 拉伸屈服强度(TD)
|
25
|
MPa
|
|||
| 断裂拉伸强度(MD)
|
ASTM D-882
|
32
|
MPa
|
||
| 断裂拉伸强度(TD)
|
31
|
MPa
|
|||
| 断裂伸长率(MD)
|
ASTM D-882
|
500
|
%
|
||
| 断裂伸长率(TD)
|
600
|
%
|
|||
| 其它性能
|
典型吹膜性能
|
0.025mm
|
吹胀比4:1
|
||
| 埃尔曼多夫撕裂(MD)
|
ASTM D-1922
|
26
|
g
|
||
| 埃尔曼多夫撕裂(TD)
|
410
|
g
|
|||