东莞市广裕塑胶原料有限公司
美国杜邦PA6 7301 高粘度 挤出级 抗冲击PA6
DuPont Performance Polymers Zytel? 7301 NC010 Nylon 6 (Unverified Data**)
Polymer,Thermoplastic,Nylon,Nylon 6
DuPont Performance Polymers
产品说明:
Zytel? 7301 NC010 is a general purpose, unlubricated polyamide 6 resin for extrusion applications.
Information provided by DuPont Performance PolymersA6
DuPont Performance Polymers Zytel? 7301 NC010 Nylon 6 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.13 g/cc | 1.13 g/cc | DAM; ASTM D792 |
| 密度 | 1.13 g/cc | 0.0408 lb/in3 | DAM; ISO 1183 |
| Water Absorption | 3.0 %
@Temperature 23.0 °C
|
3.0 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 9.5 %
@Temperature 23.0 °C
|
9.5 %
@Temperature 73.4 °F
|
Saturation, immersed; DAM; ISO 62, Similar to | |
| 线性成型收缩率 | 0.010 cm/cm
@Thickness 3.00 mm
|
0.010 in/in
@Thickness 0.118 in
|
Flow; DAM |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | 60.0 MPa
@Temperature 23.0 °C
|
8700 psi
@Temperature 73.4 °F
|
50%RH; ASTM D638 |
| 80.0 MPa
@Temperature 23.0 °C
|
11600 psi
@Temperature 73.4 °F
|
DAM; ASTM D638 | |
| 抗张强度(屈服) | 41.0 MPa
@Temperature 23.0 °C
|
5950 psi
@Temperature 73.4 °F
|
50%RH; ASTM D638 |
| 50.0 MPa
@Temperature 23.0 °C
|
7250 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 80.0 MPa
@Temperature 23.0 °C
|
11600 psi
@Temperature 73.4 °F
|
DAM; ASTM D638 | |
| 80.0 MPa
@Temperature 23.0 °C
|
11600 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | 25 %
@Temperature 23.0 °C
|
25 %
@Temperature 73.4 °F
|
DAM; nominal; ISO 527 |
| 50 %
@Temperature 23.0 °C
|
50 %
@Temperature 73.4 °F
|
50mm/min; DAM; ISO 527 | |
| 60 %
@Temperature 23.0 °C
|
60 %
@Temperature 73.4 °F
|
DAM; ASTM D638 | |
| = 100 %
@Temperature 23.0 °C
|
= 100 %
@Temperature 73.4 °F
|
50mm/min; 50%RH; ISO 527 | |
| 240 %
@Temperature 23.0 °C
|
240 %
@Temperature 73.4 °F
|
50%RH; ASTM D638 | |
| Elongation at Yield | 4.5 %
@Temperature 23.0 °C
|
4.5 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 4.8 %
@Temperature 23.0 °C
|
4.8 %
@Temperature 73.4 °F
|
DAM; ASTM D638 | |
| 23 %
@Temperature 23.0 °C
|
23 %
@Temperature 73.4 °F
|
50%RH; ASTM D638 | |
| 拉伸模量 | 1.50 GPa
@Temperature 23.0 °C
|
218 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 2.90 GPa
@Temperature 23.0 °C
|
421 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 弯曲强度 | 27.0 MPa
@Strain 5.00 %, Temperature 23.0 °C
|
3920 psi
@Strain 5.00 %, Temperature 73.4 °F
|
50%RH; ASTM D790 |
| 110 MPa
@Strain 5.00 %, Temperature 23.0 °C
|
16000 psi
@Strain 5.00 %, Temperature 73.4 °F
|
DAM; ASTM D790 | |
| 弯曲模量 | 0.695 GPa
@Temperature 23.0 °C
|
101 ksi
@Temperature 73.4 °F
|
50%RH; ASTM D790 |
| 2.30 GPa
@Temperature 23.0 °C
|
334 ksi
@Temperature 73.4 °F
|
DAM; ISO 178 | |
| 2.78 GPa
@Temperature 23.0 °C
|
403 ksi
@Temperature 73.4 °F
|
DAM; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.620 J/cm
@Temperature 23.0 °C
|
1.16 ft-lb/in
@Temperature 73.4 °F
|
DAM; ASTM D256 |
| 7.50 J/cm
@Temperature 23.0 °C
|
14.1 ft-lb/in
@Temperature 73.4 °F
|
50%RH; ASTM D256 | |
| Izod Impact, Unnotched | NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
50%RH; ASTM D4812 |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
DAM; ASTM D4812 | |
| 悬壁梁缺口冲击强度 | 6.00 kJ/m2
@Temperature -40.0 °C
|
2.86 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 180/1A |
| 6.00 kJ/m2
@Temperature 23.0 °C
|
2.86 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
50%RH; ISO 180/1U |
| 简支梁无缺口冲击强度 | NB
@Temperature -40.0 °C
|
NB
@Temperature -40.0 °F
|
DAM; ISO 179/1eU |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
50%RH; ISO 179/1eU | |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
DAM; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.600 J/cm2
@Temperature 23.0 °C
|
2.86 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+12 ohm-cm
@Temperature 23.0 °C
|
1.00e+12 ohm-cm
@Temperature 73.4 °F
|
50%RH; IEC 60093 |
| 1.00e+15 ohm-cm
@Temperature 23.0 °C
|
1.00e+15 ohm-cm
@Temperature 73.4 °F
|
DAM; IEC 60093 | |
| Surface Resistance | 1.00e+10 ohm
@Temperature 23.0 °C
|
1.00e+10 ohm
@Temperature 73.4 °F
|
50%RH; IEC 60167 |
| 1.00e+13 ohm
@Temperature 23.0 °C
|
1.00e+13 ohm
@Temperature 73.4 °F
|
DAM; IEC 60167 | |
| 介电常数 | 3.5
@Frequency 1.00e+6 Hz, Temperature 23.0 °C
|
3.5
@Frequency 1.00e+6 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 |
| 7.0
@Frequency 1.00e+6 Hz, Temperature 23.0 °C
|
7.0
@Frequency 1.00e+6 Hz, Temperature 73.4 °F
|
50%RH; IEC 60250 | |
| Comparative Tracking Index | 600 V
@Temperature 23.0 °C
|
600 V
@Temperature 73.4 °F
|
DAM; IEC 60112 |
| 600 V
@Temperature 23.0 °C
|
600 V
@Temperature 73.4 °F
|
50%RH; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 |
| 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 线性热膨胀系数,横向流动 | 100 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
55.6 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 |
| 100 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
55.6 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 熔融温度 | 220 °C | 428 °F | DAM; ASTM D3418 |
| 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | |
| 载荷下热变形温度(0.46 MPa) | 158 °C | 316 °F | DAM; ASTM D648 |
| 160 °C | 320 °F | DAM; ISO 75-1/-2 | |
| 载荷下热变形温度(1.8 MPa) | 55.0 °C | 131 °F | DAM; ISO 75-1/-2 |
| 55.0 °C | 131 °F | DAM; ASTM D648 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 230 °C | 446 °F | DAM; Optimum; Extrusion |
| 230 - 240 °C | 446 - 464 °F | DAM; Extrusion | |
| 260 - 280 °C | 500 - 536 °F | DAM; Injection Molding | |
| 270 °C | 518 °F | DAM; Optimum; Injection Molding | |
| 模具温度 | 70.0 °C | 158 °F | DAM; optimum; Injection Molding |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |
| 干燥温度 | 80.0 °C | 176 °F | DAM; Extrusion |
| 80.0 °C | 176 °F | DAM; Injection Molding | |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding |
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |
| 水分含量 | = 0.040 % | = 0.040 % | DAM; Extrusion |
| = 0.20 % | = 0.20 % | DAM; Injection Molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| 特性 | Chemical Resistance, Good | DAM |
PA6为乳白色或微黄色透明到不透明角质状结晶性聚合物，可自由着色，韧性、耐磨性、自润滑性好、刚性小、耐低温，耐细菌、能慢燃，离火慢熄，有滴落、起泡现象，成型加工性:可注塑、吹塑、浇塑、喷涂、粉末成型、机加工、焊接、粘接。PA6是吸水率最高的PA，尺寸稳定性差，并影响电性能(击穿电压)。PA6最高使用温度可达180℃,加抗冲改性剂后会降至160℃，用15%-50%玻纤增强，可提高至199℃，无机填充PA能提高其热变形温度。
PA6的化学物理特性和PA66很相似，然而，它的熔点较低，而且工艺温度范围很宽。它的抗冲击性和抗溶解性比PA66要好,但吸湿性也更强。因为塑件的许多品质特性都要受到吸湿性的影响，因此使用PA6设计产品时要充分考虑到这一点。为了提高PA6塑胶原料的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。对于没有添加剂的产品，PA6的收缩率在1%到1.5%之间。成型组装的收缩率主要受材料结晶度和吸湿性影响。实际的收缩率还和塑件设计、壁厚及其它工艺参数成函数关系
广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，,PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，PVDF，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。