德国朗盛PA66 AKV40H2.0 40%玻纤增强 高抗冲击 热稳定黑色PA66
Lanxess Durethan? AKV 40 H2.0 901510 Nylon 66, Glass Fiber Reinforced
Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 40% Glass Fiber Filled
Lanxess
产品说明:
PA 66, 40% glass fibers, injection molding, heat-aging stabilized
Information provided by LANXESS.
PA 66, 40% glass fibers, injection molding, heat-aging stabilized
Information provided by LANXESS.
Lanxess Durethan? AKV 40 H2.0 901510 Nylon 66, Glass Fiber Reinforced 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.46 g/cc | 1.46 g/cc | ISO 1183 |
| 平衡吸湿 | 1.7 % | 1.7 % | 50% RH; ISO 62 |
| 饱和吸水率 | 4.5 % | 4.5 % | ISO 62 |
| 线性成型收缩率,Flow | 0.00030 cm/cm | 0.00030 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 2577 |
| 0.00050 cm/cm | 0.00050 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | |
| 0.0026 cm/cm | 0.0026 in/in | 150x105x3; 300°C / MT 80°C; 400 bar; ISO 2577 | |
| 0.0034 cm/cm | 0.0034 in/in | 60x60x2; 300°C / MT 80°C; 600 bar; ISO 294-4 | |
| 线性成型收缩率，横向 | 0.00030 cm/cm | 0.00030 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 2577 |
| 0.00050 cm/cm | 0.00050 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | |
| 0.0094 cm/cm | 0.0094 in/in | 60x60x2; 300°C / MT 80°C; 600 bar; ISO 294-4 | |
| 0.0133 cm/cm | 0.0133 in/in | 150x105x3; 300°C / MT 80°C; 400 bar; ISO 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 145 MPa | 21000 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 210 MPa | 30500 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| 伸长率 (断裂) | 3.0 % | 3.0 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 5.0 % | 5.0 % | cond.; ISO 527-1, -2; 5 mm/min | |
| 拉伸模量 | 8.80 GPa | 1280 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 13.0 GPa | 1890 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| 弯曲强度 | 240 MPa
@Strain 5.00 %
|
34800 psi
@Strain 5.00 %
|
cond., 2 mm/min; ISO 178-A |
| 320 MPa
@Strain 4.00 %
|
46400 psi
@Strain 4.00 %
|
d.a.m., 2 mm/min; ISO 178-A | |
| 210 MPa
@Strain 3.50 %
|
30500 psi
@Strain 3.50 %
|
cond., 2 mm/min; ISO 178-A | |
| 弯曲模量 | 8.00 GPa | 1160 ksi | cond., 2 mm/min; ISO 178-A |
| 12.0 GPa | 1740 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| 悬壁梁缺口冲击强度 | 10.0 kJ/m2
@Temperature -30.0 °C
|
4.76 ft-lb/in2
@Temperature -22.0 °F
|
d.a.m.; ISO 180-1U |
| 10.0 kJ/m2
@Temperature -30.0 °C
|
4.76 ft-lb/in2
@Temperature -22.0 °F
|
cond.; ISO 180-1U | |
| 简支梁无缺口冲击强度 | 8.00 J/cm2
@Temperature -30.0 °C
|
38.1 ft-lb/in2
@Temperature -22.0 °F
|
d.a.m.; ISO 179-1eU |
| 9.00 J/cm2
@Temperature 23.0 °C
|
42.8 ft-lb/in2
@Temperature 73.4 °F
|
d.a.m.; ISO 179-1eU | |
| 9.00 J/cm2
@Temperature -30.0 °C
|
42.8 ft-lb/in2
@Temperature -22.0 °F
|
cond.; ISO 179-1eU | |
| 10.0 J/cm2
@Temperature 23.0 °C
|
47.6 ft-lb/in2
@Temperature 73.4 °F
|
cond.; ISO 179-1eU | |
| 简支梁缺口冲击强度 | 1.00 J/cm2
@Temperature -30.0 °C
|
4.76 ft-lb/in2
@Temperature -22.0 °F
|
d.a.m.; ISO 179-1eA |
| 1.20 J/cm2
@Temperature -30.0 °C
|
5.71 ft-lb/in2
@Temperature -22.0 °F
|
cond.; ISO 179-1eA | |
| 1.50 J/cm2
@Temperature 23.0 °C
|
7.14 ft-lb/in2
@Temperature 73.4 °F
|
d.a.m.; ISO 179-1eA | |
| 2.30 J/cm2
@Temperature 23.0 °C
|
10.9 ft-lb/in2
@Temperature 73.4 °F
|
cond.; ISO 179-1eA | |
| 拉伸蠕变模量(1 hr) | 7700 MPa | 1.12e+6 psi | cond.; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 6800 MPa | 986000 psi | cond.; ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | cond.; IEC 60093 |
| 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | d.a.m.; IEC 60093 | |
| 表面电阻 | 1.00e+13 ohm | 1.00e+13 ohm | cond.; IEC 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | d.a.m.; IEC 60093 | |
| 介电常数 | 4.0
@Frequency 100 Hz
|
4.0
@Frequency 100 Hz
|
d.a.m.; IEC 60250 |
| 4.0
@Frequency 1.00e+6 Hz
|
4.0
@Frequency 1.00e+6 Hz
|
d.a.m.; IEC 60250 | |
| 4.5
@Frequency 1.00e+6 Hz
|
4.5
@Frequency 1.00e+6 Hz
|
cond.; IEC 60250 | |
| 10
@Frequency 100 Hz
|
10
@Frequency 100 Hz
|
cond.; IEC 60250 | |
| 介电强度 | 35.0 kV/mm
@Thickness 1.00 mm
|
889 kV/in
@Thickness 0.0394 in
|
cond.; IEC 60243-1 |
| 40.0 kV/mm
@Thickness 1.00 mm
|
1020 kV/in
@Thickness 0.0394 in
|
d.a.m.; IEC 60243-1 | |
| 耗散因数 | 0.011
@Frequency 100 Hz
|
0.011
@Frequency 100 Hz
|
d.a.m.; IEC 60250 |
| 0.015
@Frequency 1.00e+6 Hz
|
0.015
@Frequency 1.00e+6 Hz
|
d.a.m.; IEC 60250 | |
| 0.065
@Frequency 1.00e+6 Hz
|
0.065
@Frequency 1.00e+6 Hz
|
cond.; IEC 60250 | |
| 0.235
@Frequency 100 Hz
|
0.235
@Frequency 100 Hz
|
cond.; IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 525 V | 525 V | d.a.m.; Solution A; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 20.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
11.1 μin/in-°F
@Temperature 73.4 - 131 °F
|
ISO 11359-1, -2 |
| 线性热膨胀系数,横向流动 | 90.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
50.0 μin/in-°F
@Temperature 73.4 - 131 °F
|
ISO 11359-1, -2 |
| 熔融温度 | 263 °C | 505 °F | 10°C/min; ISO 11357-1, -3 |
| 载荷下热变形温度(0.46 MPa) | 250 °C | 482 °F | ISO 75-1, -2 |
| 载荷下热变形温度(1.8 MPa) | 250 °C | 482 °F | ISO 75-1, -2 |
| 维卡软化温度 | = 230 °C
@Load 5.10 kg
|
= 446 °F
@Load 11.2 lb
|
120°C/hour; ISO 306 |
| = 230 °C
@Load 5.10 kg
|
= 446 °F
@Load 11.2 lb
|
50°C/hour; ISO 306 | |
| 可燃性(UL94) | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|
||
| 极限氧指数 | 26 % | 26 % | Method A; ISO 4589-2 |
| 灼热丝试验 | 600 °C
@Diameter 2.00 mm
|
1110 °F
@Diameter 0.0787 in
|
GWIT; IEC 60695-2-13 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 280 - 300 °C | 536 - 572 °F | |
| 290 °C | 554 °F | for test specimens; ISO 294 | |
| 模具温度 | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| 干燥温度 | 80.0 °C | 176 °F | |
| 干燥时间 | 2 - 6 hour | 2 - 6 hour | |
| 水分含量 | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| 材料描述 | 测试方法 | |
|---|---|---|
| ISO Shortname | ISO-PA 66, MHR, 14-120, GF40 |
德国朗盛PA66 DP 2801 无卤防火PA66 UL94-V0
德国朗盛PA66 A 30 S FN31 无卤防火 热稳定尼龙树脂
德国朗盛PA66 DP AKV 30 FN00 30%玻纤增强 无卤阻燃PA66
德国朗盛PA66 AKV 25 F30 25%玻纤增强 防火阻燃 耐热老化PA66
德国朗盛PA66 AKV30FN04 30%玻纤增强 无卤防火 热稳定PA66
德国朗盛PA66 DP2802/30 30%玻纤增强 无卤防火PA66
德国朗盛PA66 AKV15 15%玻纤增强 高强度PA66
德国朗盛PA66 AKV15H1.0 15%玻纤增强 高强度PA66
德国朗盛PA66 AKV15H2.0 15%玻纤增强 高强度 耐热老化PA66
德国朗盛PA66 AKV25 25%玻纤增强 高强度PA66
德国朗盛PA66 AKV30 30%玻纤增强 高强度 注塑级PA66
德国朗盛PA66 AKV35 35%玻纤增强 高强度 高刚性PA66
德国朗盛PA66 AKV50 50%玻纤增强 高强度 高刚性PA66
德国朗盛PA66 AKV50H1.0 50%玻纤增强 高强度 高刚性
德国朗盛PA66 AKV35H1,0 35%玻纤增强 高强度 注塑级PA66
德国朗盛PA66 AKV15H2.0 15%玻纤增强 高强度PA66
德国朗盛PA66 AKV30H3.0 30%玻纤增强 高强度 热稳定PA66
德国朗盛PA66 AKV35H2.0 35%玻纤增强 高强度 耐热老化PA66
德国朗盛PA66 AKV30H2.0 30%玻纤增强 高强度 热稳定性良好PA66
德国朗盛PA66 AKV325H2.0 25%玻纤增强 高强度 热稳定PA66
德国朗盛PA66 AKV35H3.0 35%玻纤增强 高强度 耐热老化PA66
德国朗盛PA66 AKV35H2.0 35%玻纤增强 高强度 耐热老化PA66
德国朗盛PA66 AKV50H2.0 50%玻纤增强 高强度 热稳定PA66
德国朗盛PA66 AKV25H2.0 25%玻纤增强 高强度 热稳定黑色PA66
德国朗盛PA66 AKV25H3.0 25%玻纤增强 高强度 热稳定PA66
德国朗盛PA66 AKV230H2.0 30%玻纤增强 高抗冲击 热稳定黑色PA66
德国朗盛PA66 AKV40H2.0 40%玻纤增强 高抗冲击 热稳定黑色PA66
德国朗盛PA66 AKV50H3.0 50%玻纤增强 高强度 热稳定PA66