TPU DESMOPAN 5377A

Physical Properties	Metric	English	Comments
Density	1.14g/cc	0.0412lb/in3	ISO 1183
Mechanical Properties	Metric	English	Comments
Hardness, Shore A	77	77	ISO 868
Hardness, Shore D	28	28	ISO 868
Tensile Strength, Ultimate	27.0MPa	3920psi	200 mm/min; DIN 53504
Tensile Stress	1.30MPa @Strain 10.0 %	189psi @Strain 10.0 %	200 mm/min; DIN 53504
	3.60MPa @Strain 50.0 %	522psi @Strain 50.0 %	200 mm/min; DIN 53504
	4.90MPa @Strain 100 %	711psi @Strain 100 %	200 mm/min; DIN 53504
	8.90MPa @Strain 300 %	1290psi @Strain 300 %	200 mm/min; DIN 53504
Elongation at Break	644 %	644 %	200 mm/min; DIN 53504
Tensile Modulus	0.0210GPa @Temperature 60.0 °C	3.05ksi @Temperature 140 °F	storage; ISO 6721-1,-4
	0.0290GPa @Temperature 20.0 °C	4.21ksi @Temperature 68.0 °F	storage; ISO 6721-1,-4
	0.180GPa @Temperature -20.0 °C	26.1ksi @Temperature -4.00 °F	storage; ISO 6721-1,-4
Rebound	45 %	45 %	Resilience; ISO 4662

TPU DESMOPAN 5377A

性能

1. 力学性能：TPU弹性体的力学性能主要包括：硬度，拉伸强度，压缩性能，撕裂强度，回弹性和耐磨性能，耐屈扰性等，而TPU 弹性塑料的力学性能，除这些性能外，还有较高剪切强度和冲击功等。

（a）硬度：硬度是材料抵抗变形，刻痕和划伤的能力的一种指标。TPU硬度通常用邵尔A（Shore A）和邵尔D（shore D）硬度计测定，邵尔A用于比较软的TPU，邵尔D用于较硬的TPU。硬度主要由TPU结构中的硬段含量来决定，硬段含量越高，TPU的硬度就会随之上升。硬度上升后，TPU的其他性能也会发生改变，拉伸模量和撕裂强度增加，刚性和压缩应力（负荷能力）增加，伸长率降低，密度和动态生热增加，耐环境性能增加。TPU的硬度与温度存在一定关系。从室温冷却降温至突变温度（-4~-12℃），硬度无明显变化；在突变温度下，TPU硬度突然增加而变得很硬并失去弹性，这是由于软段结晶作用的结果。

（b）硬度与定伸应力和伸长率的关系以及硬度与撕裂强度的关系。随着TPU硬度的增加，100%定伸应力和300%定伸应力迅速增加，伸长率下降。这主要是由于硬段含量增加的结果：硬段含量高，其所形成硬段相越易形成次晶或结晶结构增加了物理交联的数量而限制材料变形。若使材料变形必须提高应力，从而提高了定伸应力，同时伸长率下降。TPU硬度与撕裂强度的关系，随硬度增加，撕裂强度迅速增加，其理由亦与模量的解释相同。

各种TPU成型品的用途:

手机壳

汽车部件

球型联轴节；防尘盖；踏板刹车器；门锁撞针；衬套

板簧衬套；轴承；防震部件；内外装饰件；防滑链等

机械·工业用部件

各种齿轮；密封件（主要起耐磨和耐油作用）；防震部件；取模针；衬套；轴承

盖类；连接器；橡胶筛；印刷胶辊等

服饰辅料

女士文胸肩带、服装松紧带等。

鞋类

垒球鞋、棒球鞋、高尔夫球鞋、足球鞋鞋底及鞋前掌

女士鞋后跟；滑雪靴；安全靴，高档鞋底等