东莞市广裕塑胶原料有限公司
上海罗地亚PA66 D218CR V33 33%玻纤增强 耐水解PA612
TECHNYL eXten? D 218CR V33 BLACK
Polyamide 66/610 Copolymer
33% 玻璃纤维增强材料
Solvay Engineering Plastics
产品说明：
TECHNYL eXten? D 218CR V33 Black is a glass fiber reinforced grade based on polyamide blend of polyamide 6.10 and polyamide 66, heat stabilized, for injection moulding. This grade shows outstanding resistance to hydrolysis and chemical resistance to long life automotive coolants. It also offers an excellent crack resistance to calcium chloride road salts, good injection process ability, high surface aspect quality, and high overall mechanical and thermal properties.
TECHNYL eXten? D 218CR V33 BLACK 物性表
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 密度 | 1.35 | -- | g/cm3 | ISO 1183/A |
| 吸水率 | ISO 62 | |||
| 23°C, 24 hr | 0.30 | -- | % | ISO 62 |
| 饱和, 23°C | 3.6 | -- | % | ISO 62 |
| 平衡, 23°C, 50% RH | 1.3 | -- | % | ISO 62 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量(23°C) | 11300 | 8900 | MPa | ISO 527-2/1A |
| 拉伸应力(断裂, 23°C) | 196 | 132 | MPa | ISO 527-2/1A |
| 拉伸应变(断裂, 23°C) | 3.3 | 4.8 | % | ISO 527-2 |
| 弯曲模量(23°C) | 10200 | 8000 | MPa | ISO 178 |
| 弯曲应力(23°C) | 280 | 220 | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 简支梁缺口冲击强度(23°C) | 15 | -- | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m2 | ISO 179/1eU |
| 23°C | 94 | -- | kJ/m2 | ISO 179/1eU |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 热变形温度 | ||||
| 0.45 MPa, 未退火 | 225 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, 未退火 | 218 | -- | °C | ISO 75-2/Af |
| 熔融温度 | 220 到 260 | -- | °C | ISO 11357-3 |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 体积电阻率 | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| 介电强度(2.00 mm) | 34 | -- | kV/mm | IEC 60243-1 |
| 漏电起痕指数(解决方案 B) | 600 | -- | V | IEC 60112 |
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| UL 阻燃等级(0.40 mm) | HB | -- | UL 94 |
| 注射 | 干燥 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80 | °C | |
| 建议的最大水分含量 | 0.20 | % | |
| 料筒后部温度 | 265 到 275 | °C | |
| 料筒中部温度 | 270 到 280 | °C | |
| 料筒前部温度 | 275 到 285 | °C | |
| 模具温度 | 70 到 100 | °C |
| 注射说明 |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
上海罗地亚PA66 A216 纯树脂尼龙 刚性和尺寸稳定性良好
上海罗地亚PA66 A218 纯树脂尼龙66 良好热稳定
上海罗地亚PA66 A246M 超韧超高抗冲击强度尼龙66
上海罗地亚PA66 A50H1 无卤防火PA66 热稳定 UL94-V0.
上海罗地亚PA66 B50H1 无卤无磷防火 UL94-V0级纯树脂
上海罗地亚PA66 D247F 高抗冲击 耐碱 耐化学PA66
上海罗地亚PA66 A216 V15 15%玻纤增强 刚性 韧性良好。
上海罗地亚PA66 A216 V20 20%玻纤增强 刚性 韧性良好
上海罗地亚PA66 A216 V30 30%玻纤增强 良好的热稳定
上海罗地亚PA66 A216 V33 33%玻纤增强 高刚性 高强度PA66
上海罗地亚PA66 A216 V40 40%玻纤增强 高刚性 高强度
上海罗地亚PA66 A216V30Y17 玻纤含量30% 和热保护稳定剂
上海罗地亚PA66 A216V50 玻纤增强50% 低吸收尺寸稳定
上海罗地亚PA66 A218V30 30%玻纤增强 耐高温热稳定
上海罗地亚PA66 D218CRV33 33%玻纤增强 耐水解PA66
上海罗地亚PA66 A218V15 15%玻纤增强 热稳定PA66
上海罗地亚PA66 B218V20 20%玻纤增强 高刚性 耐热 热稳定PA66
上海罗地亚PA66 A218V25 25%玻纤增强 耐高温热稳定
上海罗地亚PA66 A218 V35 35%玻纤增强 注塑级 热稳定PA66
上海罗地亚PA66 A218V40 40%玻纤增强 高强度高钢性尺寸稳定
上海罗地亚PA66 A218V45 45%玻纤增强 高强度高钢性尺寸稳定
上海罗地亚PA66 A218V50 50%玻纤增强 高刚性 热稳定级PA66
上海罗地亚PA66/6 B218LV30 30%玻纤增强 抗紫外线 热稳定PA66
上海罗地亚PA66 A60 G1 V25 25%玻纤增强 无卤阻燃 注塑级PA66
上海罗地亚PA66 A60G1V30 30%玻纤含量 无卤阻燃PA66
上海罗地亚PA66 A20 V25 25%玻纤增强 无卤红磷防火V0
上海罗地亚PA66 A20 V35 35%玻纤增强 无卤红磷阻燃 UL94-V0
上海罗地亚PA66 A 30H1 V25 25%玻纤增强 无卤阻燃 热稳定PA66
上海罗地亚PA66 A 30H1 V30 30%玻纤增强 无卤阻燃 热稳定PA66