上海罗地亚PA66 A230F 注塑级纯树脂 良好的低温抗冲击性
Solvay TECHNYL? A 246M PA66, DRY
Polymer,Thermoplastic,Nylon,Nylon 66
Solvay
产品说明:
Description: Unreinforced and modified polyamide 66, with very high impact resistance even at low temperature, for injection molding.
Available in: Europe and North America
Product Applications: TECHNYL?? A 246M offers an excellent notched impact resistance at low temperature make it suitable for: sports and leisure applications, for shoe soles, ski components, ski and surf bindings, toy applications, such as, the bumper of a remote-controlled car. This product is available in natural, white and black.
Information provided by Rhodia, Rhodia has been acquired by Solvay.
Solvay TECHNYL? A 246M PA66, DRY 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183/A |
| 吸水率 | 1.05 %
@Temperature 23.0 °C, Time 86400 sec
|
1.05 %
@Temperature 73.4 °F, Time 24.0 hour
|
ISO 62 |
| 线性成型收缩率 | 0.010 cm/cm | 0.010 in/in | Isotropy |
| 线性成型收缩率,Flow | 0.019 cm/cm | 0.019 in/in | |
| 线性成型收缩率，横向 | 0.019 cm/cm | 0.019 in/in |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 44.0 MPa | 6380 psi | ISO 527 Type 1A |
| 抗张强度(屈服) | 42.0 MPa | 6090 psi | ISO 527 type 1 A |
| 47.0 MPa | 6820 psi | ISO 527 type 1 A | |
| 拉伸模量 | 1.90 GPa | 276 ksi | ISO 527 Type 1A |
| 弯曲强度 | 70.0 MPa | 10200 psi | ISO 178 |
| 弯曲模量 | 1.80 GPa | 261 ksi | ISO 178 |
| 悬壁梁缺口冲击强度 | 22.0 kJ/m2
@Temperature -30.0 °C
|
10.5 ft-lb/in2
@Temperature -22.0 °F
|
ISO 180/1eA |
| 60.0 kJ/m2
@Temperature 23.0 °C
|
28.6 ft-lb/in2
@Temperature 73.4 °F
|
ISO 180/1eA | |
| 简支梁无缺口冲击强度 | 1.60 J/cm2
@Temperature -30.0 °C
|
7.61 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179/1eU |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 179/1eU | |
| 简支梁缺口冲击强度 | 9.10 J/cm2 | 43.3 ft-lb/in2 | ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| 表面电阻 | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| 介电常数 | 3.2 | 3.2 | IEC 60250 |
| 介电强度 | 3.20 kV/mm | 81.3 kV/in | IEC 60243 |
| 耗散因数 | 0.020 | 0.020 | IEC 60250 |
| 相比耐漏电起痕指数(CTI) | 450 V | 450 V | Solution B; IEC 60112 |
| 575 V | 575 V | Solution A; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 μm/m-°C
@Temperature 23.0 - 85.0 °C
|
38.9 μin/in-°F
@Temperature 73.4 - 185 °F
|
ISO 11359 |
| 熔融温度 | 263 °C | 505 °F | ISO 11357 |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | ISO 75/Af |
| 可燃性(UL94) | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
1210 |
| 极限氧指数 | 24.5 % | 24.5 % | ISO 4589 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 进料温度 | 250 - 270 °C | 482 - 518 °F | |
| 料筒前部温度 | 270 - 290 °C | 518 - 554 °F | |
| 模具温度 | 60.0 - 80.0 °C | 140 - 176 °F | |
| 干燥温度 | 80.0 °C | 176 °F | |
| 水分含量 | = 0.20 % | = 0.20 % |
| 材料描述 | 测试方法 | |
|---|---|---|
| Compression Zone | 260-280°C |
上海罗地亚PA66 A230F 注塑级纯树脂 良好的低温抗冲击性
上海罗地亚PA66 A216 纯树脂尼龙 刚性和尺寸稳定性良好
上海罗地亚PA66 A218 纯树脂尼龙66 良好热稳定
上海罗地亚PA66 A246M 超韧超高抗冲击强度尼龙66
上海罗地亚PA66 A50H1 无卤防火PA66 热稳定 UL94-V0.
上海罗地亚PA66 B50H1 无卤无磷防火 UL94-V0级纯树脂
上海罗地亚PA66 D247F 高抗冲击 耐碱 耐化学PA66
上海罗地亚PA66 A216 V15 15%玻纤增强 刚性 韧性良好。
上海罗地亚PA66 A216 V20 20%玻纤增强 刚性 韧性良好
上海罗地亚PA66 A216 V30 30%玻纤增强 良好的热稳定
上海罗地亚PA66 A216 V33 33%玻纤增强 高刚性 高强度PA66
上海罗地亚PA66 A216 V40 40%玻纤增强 高刚性 高强度
上海罗地亚PA66 A216V30Y17 玻纤含量30% 和热保护稳定剂
上海罗地亚PA66 A216V50 玻纤增强50% 低吸收尺寸稳定
上海罗地亚PA66 A218V30 30%玻纤增强 耐高温热稳定
上海罗地亚PA66 D218CRV33 33%玻纤增强 耐水解PA66
上海罗地亚PA66 A218V15 15%玻纤增强 热稳定PA66
上海罗地亚PA66 B218V20 20%玻纤增强 高刚性 耐热 热稳定PA66
上海罗地亚PA66 A218V25 25%玻纤增强 耐高温热稳定
上海罗地亚PA66 A218 V35 35%玻纤增强 注塑级 热稳定PA66
上海罗地亚PA66 A218V40 40%玻纤增强 高强度高钢性尺寸稳定
上海罗地亚PA66 A218V45 45%玻纤增强 高强度高钢性尺寸稳定
上海罗地亚PA66 A218V50 50%玻纤增强 高刚性 热稳定级PA66
上海罗地亚PA66/6 B218LV30 30%玻纤增强 抗紫外线 热稳定PA66
上海罗地亚PA66 A60 G1 V25 25%玻纤增强 无卤阻燃 注塑级PA66
上海罗地亚PA66 A60G1V30 30%玻纤含量 无卤阻燃PA66
上海罗地亚PA66 A20 V25 25%玻纤增强 无卤红磷防火V0
上海罗地亚PA66 A20 V35 35%玻纤增强 无卤红磷阻燃 UL94-V0
上海罗地亚PA66 A 30H1 V25 25%玻纤增强 无卤阻燃 热稳定PA66
上海罗地亚PA66 A 30H1 V30 30%玻纤增强 无卤阻燃 热稳定PA66
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。