Terluran? GP-22
丙烯腈丁二烯苯乙烯
产品说明：
Terluran GP-22 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector
| 基本信息 |
|
| 特性 |
- 高光
- 抗撞击性，良好
- 良好的着色性
- 流动性中等
- 通用
- 优良外观
|
| 用途 |
- 电器用具
- 家用货品
- 汽车领域的应用
- 通用
- 外壳
- 玩具
- 卫浴产品
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
- Creep Modulus vs. Time (ISO 11403-1)
- Isochronous Stress vs. Strain (ISO 11403-1)
- Isothermal Stress vs. Strain (ISO 11403-1)
- Secant Modulus vs. Strain (ISO 11403-1)
- Shear Modulus vs. Temperature (ISO 11403-1)
- Specific Volume vs Temperature (ISO 11403-2)
- Viscosity vs. Shear Rate (ISO 11403-2)
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.04 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） |
|
|
ASTM D1238 |
| 200°C/5.0 kg |
1.5 |
g/10 min |
ASTM D1238 |
| 220°C/10.0 kg |
19 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR） |
|
|
|
| 230°C/3.8 kg |
4.80 |
cm3/10min |
ASTM D1238 |
| 220°C/10.0 kg |
19.0 |
cm3/10min |
ISO 1133 |
| 收缩率 |
|
|
|
| 流动 |
0.40 到 0.70 |
% |
ASTM D955 |
| -- |
0.40 到 0.70 |
% |
ISO 294-4 |
| 吸水率 |
|
|
|
| 饱和, 23°C |
1.0 |
% |
ASTM D570, ISO 62 |
| 平衡, 23°C, 50% RH |
0.22 |
% |
ISO 62 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度(R 级) |
103 |
|
ASTM D785 |
| 球压硬度 |
97.0 |
MPa |
ISO 2039-1 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
2300 |
MPa |
ASTM D638, ISO 527-2 |
| 抗张强度(屈服, 23°C) |
45.0 |
MPa |
ASTM D638, ISO 527-2 |
| 拉伸应变 |
|
|
|
| 屈服, 23°C |
2.6 |
% |
ISO 527-2 |
| 断裂 |
2.6 |
% |
ASTM D638 |
| 标称拉伸断裂应变(23°C) |
10 |
% |
ISO 527-2 |
| 弯曲模量 |
2300 |
MPa |
ASTM D790 |
| 弯曲强度 |
65.0 |
MPa |
ASTM D790, ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179 |
| -30°C |
8.0 |
kJ/m2 |
ISO 179 |
| 23°C |
22 |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度 |
|
|
ISO 179 |
| -30°C |
100 |
kJ/m2 |
ISO 179 |
| 23°C |
180 |
kJ/m2 |
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
|
| -30°C |
59 |
J/m |
ASTM D256 |
| -18°C |
100 |
J/m |
ASTM D256 |
| 23°C |
300 |
J/m |
ASTM D256 |
| -30°C |
8.0 |
kJ/m2 |
ISO 180/A |
| 23°C |
26 |
kJ/m2 |
ISO 180/A |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火 |
90.6 |
°C |
ASTM D648 |
| 0.45 MPa, 退火 |
104 |
°C |
ASTM D648 |
| 0.45 MPa, 退火 |
99.0 |
°C |
ISO 75-2/B |
| 1.8 MPa, 未退火 |
77.8 |
°C |
ASTM D648 |
| 1.8 MPa, 退火 |
98.9 |
°C |
ASTM D648 |
| 1.8 MPa, 退火 |
94.0 |
°C |
ISO 75-2/A |
| 维卡软化温度 |
|
|
|
| -- |
105 |
°C |
ISO 306/A50 |
| -- |
96.0 |
°C |
ISO 306/B50 |
| 线形热膨胀系数 - 流动 |
8.0E-5 到 1.1E-4 |
cm/cm/°C |
ISO 11359-2 |
| 导热系数 |
0.17 |
W/m/K |
DIN 52612 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+13 |
ohms |
IEC 60093 |
| 体积电阻率 |
|
|
|
| -- |
1.0E+15 |
ohms·cm |
ASTM D257 |
| -- |
1.0E+15 |
ohms·cm |
IEC 60093 |
| 介电常数 |
|
|
|
| 1.00 mm, 1 MHz |
2.80 |
|
ASTM D150 |
| 100 Hz |
2.90 |
|
IEC 60250 |
| 1 MHz |
2.80 |
|
IEC 60250 |
| 耗散因数 |
|
|
IEC 60250 |
| 100 Hz |
4.8E-3 |
|
IEC 60250 |
| 1 MHz |
7.9E-3 |
|
IEC 60250 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 黄度指数 |
13 |
YI |
DIN 6167 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
80.0 |
°C |
|
| 干燥时间 |
2.0 到 4.0 |
hr |
|
| 加工（熔体）温度 |
220 到 260 |
°C |
|
| 模具温度 |
30.0 到 60.0 |
°C |
|
| Injection Velocity |
200 |
mm/sec |
|