PPS RYTON XE5515BL
Ryton? XE5515BL 15% glass fiber reinforced polyphenylene sulfide alloy compound provides excellent mechanical strength and chemical resistance at elevated temperatures and is suitable for extrusion or blow molding.
Key Attributes: Chemical Resistant; Good Strength
Applications: Automotive Applications
Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42g/cc | 0.0513lb/in3 | ASTM D792 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050cm/cm @Thickness 3.20 mm |
0.0050in/in @Thickness 0.126 in |
ASTM D255 |
| Linear Mold Shrinkage, Transverse | 0.0060cm/cm @Thickness 3.20 mm |
0.0060in/in @Thickness 0.126 in |
ASTM D255 |
| Melt Flow | 12g/10 min @Load 5.00 kg, Temperature 316 °C |
12g/10 min @Load 11.0 lb, Temperature 601 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 118 | 118 | ASTM D785 |
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength at Break | 110MPa | 16000psi | ISO 527-2 |
| Tensile Strength | 103MPa | 14900psi | ASTM D638 |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-2 |
| Tensile Modulus | 5.80GPa | 841ksi | ISO 527-2 |
| 6.21GPa | 901ksi | ASTM D638 | |
| Flexural Strength | 159MPa | 23100psi | ASTM D790 |
| 170MPa | 24700psi | ISO 178 | |
| Flexural Modulus | 5.50GPa | 798ksi | ISO 178 |
| 5.52GPa | 801ksi | ASTM D790 | |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Izod Impact, Notched | 0.960J/cm @Thickness 3.18 mm |
1.80ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 6.90J/cm @Thickness 3.18 mm |
12.9ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Notched (ISO) | 10.0kJ/m2 | 4.76ft-lb/in2 | Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 45.0kJ/m2 | 21.4ft-lb/in2 | ISO 180 |