PC LUPOY 1303-10C

Introduction: LUPOY PC 1303-10C resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.

Main Characteristics: Medium viscosity, UV stabilizer, Good mold release

Applications: Appliances, Outdoor appliance, Automotive components

Physical Properties	Metric	English	Comments
Density	1.20g/cc	0.0434lb/in3	ASTM D792
Water Absorption	0.15 % @Time 86400 sec	0.15 % @Time 24.0 hour	ASTM D570
Moisture Absorption at Equilibrium	0.32 %	0.32 %	50% RH; ASTM D570
Linear Mold Shrinkage, Flow	0.0050-0.0070cm/cm	0.0050-0.0070in/in	ASTM D955
Melt Flow	10g/10 min @Load 1.20 kg, Temperature 300 °C	10g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	73	73	ASTM D785
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength, Ultimate	71.0MPa	10300psi	ASTM D638

PC LUPOY 1303-10C

特性:

为非结晶性热塑性塑料，优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。

优点：

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．H.D.T.高；

4．耐疲劳性差；

5、耐候性佳；

6．电气特性优；

7．无味无臭对人体无害符合卫生安全；

8．成形收缩率低、尺寸安定性良好。

应用

PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃，PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗，用于飞机舱罩，照明设备、工业安全档板和防弹玻璃。

汽车制造业

聚碳酸酯具有良好的抗冲击、抗热畸变性能，而且耐候性好、硬度高，因此适用于生产轿车和轻型卡车的各种零部件，其主要集中在照明系统、仪表板、加热板、除霜器及聚碳酸酯合金制的保险杠等。

建材行业

聚碳酸酯板材具有良好的透光性，抗冲击性，耐紫外线辐射及其制品的尺寸稳定性和良好的成型加工性能，使其比建筑业传统使用的无机玻璃具有明显的技术性能优势。中国建有聚碳酸酯建材中空板生产线20余条，年需用聚碳酸酯7万吨左右，到2005年达到14万吨。

PC LUPOY 1303-10C我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！