PA66 DENILUB Y 30G 0Mo
General | |
Material Status |
|
Availability |
Africa Middle EastAsia PacificEuropeLatin AmericaNorth America |
Filler / Reinforcement |
|
Additive |
|
Features |
LubricatedWear Resistant |
Processing Method |
|
Physical | Nominal Value |
Unit |
Test Method |
Density |
g/cm3 |
ISO 1183 | |
Molding Shrinkage |
ASTM D955 | ||
Flow |
in/in |
||
Across Flow |
in/in |
||
Mechanical | Nominal Value |
Unit |
Test Method |
Tensile Modulus |
psi |
ISO 527-2 | |
Tensile Stress(Break) |
psi |
ISO 527-2 | |
Tensile Strain(Break) |
% |
ISO 527-2 | |
Coefficient of Friction |
ASTM D1894 | ||
Dynamic |
|||
Static |
|||
Wear Factor2 |
10^-10 m3 h/N·m·h |
||
Impact | Nominal Value |
Unit |
Test Method |
Notched Izod Impact Strength |
ft·lb/in2 |
ISO 180/A | |
Unnotched Izod Impact Strength |
ft·lb/in2 |
ISO 180 |
PA66 DENILUB Y 30G 0Mo
PA特性
1、具有优良的耐磨性、自润滑性,机械强度较高。但吸水性较大,因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性,其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时,一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性,经常加入各种各样的改性剂。玻璃就是最常见的添加剂,有时为了提高抗冲击性还加入合成橡胶,如EPDM和SBR等。PA66的粘性较低,因此流动性很好(但不如PA6)。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间,加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性,但对酸和其它一些氯化剂的抵抗力较弱。
PA66应用
高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等