上海沐音新材料有限公司
XANTAR? LDS 3710
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
Laser Direct Structuring (LDS)*, Vicat 120°C, Black color only
*The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser Electronics AG. Please address straight to LPKF Laser Electronics AG (www.LPKF.de).
*The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser Electronics AG. Please address straight to LPKF Laser Electronics AG (www.LPKF.de).
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
||||
|
供货地区
|
|
|||
|
外观
|
|
|||
|
形式
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
1.19
|
g/cm3
|
ISO 1183 |
|
溶化体积流率（MVR）(260°C/5.0 kg)
|
14.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动方向
|
0.60
|
%
|
ISO 294-4 |
|
吸水率(饱和, 23°C)
|
0.60
|
%
|
ISO 62 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
2200
|
MPa
|
ISO 527-2 |
|
拉伸应力(屈服)
|
50.0
|
MPa
|
ISO 527-2 |
|
拉伸应变(屈服)
|
4.0
|
%
|
ISO 527-2 |
|
标称拉伸断裂应变
|
50
|
%
|
ISO 527-2 |
|
弯曲模量
|
2250
|
MPa
|
ISO 178 |
|
弯曲应力
|
80.0
|
MPa
|
ISO 178 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
ISO 179/1eA | ||
|
-30°C
|
60
|
kJ/m2
|
|
|
23°C
|
70
|
kJ/m2
|
|
|
简支梁无缺口冲击强度
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
ISO 180/4A | ||
|
-20°C
|
40
|
kJ/m2
|
|
|
23°C
|
60
|
kJ/m2
|
|
|
多轴向仪器化冲击能量
|
|||
|
-20°C3
|
4.00
|
J
|
内部方法 |
|
23°C
|
35.0
|
J
|
ISO 6603-2 |
|
23°C3
|
10.0
|
J
|
内部方法 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度(1.8 MPa, 未退火)
|
102
|
°C
|
ISO 75-2/A |
|
维卡软化温度
|
122
|
°C
|
ISO 306/B50 |
|
线形热膨胀系数
|
ISO 11359-2 | ||
|
流动
|
7.0E-5
|
cm/cm/°C
|
|
|
横向
|
7.0E-5
|
cm/cm/°C
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
1.0E+15
|
ohm·cm
|
IEC 60093 |
|
相对电容率(1.00 GHz)
|
2.80
|
|
IEC 60250 |
|
耗散因数(1.00 GHz)
|
5.0E-3
|
|
IEC 60250 |
| 备注 |
  |