东莞市广裕塑胶原料有限公司
亨斯迈医疗级TPU A78P4766 防火医疗应用 USP VI、ISO10993认证TPU
IROGRAN A 78 P 4766
热塑性聚氨酯弹性体（聚醚）
Huntsman Corporation
产品说明：
IROGRAN A 78 P 4766 is a flame-retardant, halogen-free, thermoplastic polyether-polyurethane intended for extrusion and injection moulding applications.
Additional characteristics of the product is the high flexibility and elasticity.
PERFORMANCE FEATURES
- High hydrolysis resistance
- High microbial resistance
- Flame retardant
- Halogen-free
- UL 94 classification V0
APPLICATIONS
- Cables
- Hoses
- Spiral Hoses
- Profiles
- Cable Bushings
Additional characteristics of the product is the high flexibility and elasticity.
PERFORMANCE FEATURES
- High hydrolysis resistance
- High microbial resistance
- Flame retardant
- Halogen-free
- UL 94 classification V0
APPLICATIONS
- Cables
- Hoses
- Spiral Hoses
- Profiles
- Cable Bushings
IROGRAN A 78 P 4766 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重1 | 1.16 | g/cm3 | ASTM D792, ISO 1183 |
| 溶化体积流率（MVR）(190°C/21.6 kg) | 110 | cm3/10min | |
| 收缩率 - 流动(注塑) | 1.0 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | ASTM D2240, ISO 868 | ||
| 邵氏 A, 注塑 | 82 | ASTM D2240, ISO 868 | |
| 邵氏 D, 注塑 | 30 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Abrasion2 | 40 | mm3 | ISO 4649 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| TMA3 | 内部方法 | ||
| High : 635.0 μm | 190 | °C | 内部方法 |
| Low : 635.0 μm | 165 | °C | 内部方法 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力4 | |||
| 100%应变 | 5.79 | MPa | ASTM D412 |
| 100%应变 | 5.20 | MPa | DIN 53504 |
| 300%应变 | 9.65 | MPa | ASTM D412 |
| 300%应变 | 8.00 | MPa | DIN 53504 |
| 抗张强度5 | |||
| 断裂 | 27.6 | MPa | ASTM D412 |
| 断裂 | 30.0 | MPa | DIN 53504 |
| 伸长率6(断裂) | 800 | % | ASTM D412, DIN 53504 |
| 撕裂强度7 | |||
| -- | 71.8 | kN/m | ASTM D624 |
| -- | 40 | kN/m | ISO 34-1 |
| 压缩永久变形8 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 20 | % | ASTM D395, ISO 815 |
| 70°C, 24 hr | 40 | % | ASTM D395, ISO 815 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级 | V-0 | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | |||
| -- | 100 到 110 | °C | |
| 真空干燥机 | 80.0 到 90.0 | °C | |
| 干燥时间 | |||
| -- | 3.0 | hr | |
| 真空干燥机 | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| 料筒后部温度 | 175 到 195 | °C | |
| 料筒中部温度 | 175 到 195 | °C | |
| 料筒前部温度 | 175 到 195 | °C | |
| 射嘴温度 | 180 到 200 | °C | |
| 加工（熔体）温度 | 170 到 195 | °C | |
| 模具温度 | 20.0 到 70.0 | °C |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 100 到 110 | °C | |
| 干燥时间 | 3.0 | hr | |
| 料筒温度 | 25.0 到 40.0 | °C | |
| 料筒1区温度 | 165 到 190 | °C | |
| 料筒2区温度 | 165 到 190 | °C | |
| 料筒3区温度 | 165 到 190 | °C | |
| 料筒4区温度 | 165 到 190 | °C | |
| 料筒5区温度 | 165 到 190 | °C | |
| 接头温度 | 175 到 195 | °C | |
| 口模温度 | 175 到 200 | °C |
| 备注 | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| 8 . | Injection Molded |
?