沙伯基础医疗级PEI 1000 医疗级 USP Class VI, FDA 认证
ULTEM? 1000 resin
聚醚酰亚胺
产品说明：
ULTEM? 1000 resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM? 1000 resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures.
ULTEM? 1000 resin 物性表
| 基本信息 |
|
| 特性 |
- 高强度
- 耐化学性良好
- 耐热性，高
- 通用
- 无定形的
- 阻燃性
|
| 用途 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.27 |
g/cm3 |
ASTM D792 |
| 熔流率（熔体流动速率）(337°C/6.6 kg) |
9.0 |
g/10 min |
ASTM D1238 |
| 收缩率 - 流动(3.20 mm) |
0.50 到 0.70 |
% |
内部方法 |
| 吸水率 |
|
|
ASTM D570 |
| 24 hr |
0.25 |
% |
ASTM D570 |
| 平衡, 23°C |
1.3 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度(M 级) |
109 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量1 |
3590 |
MPa |
ASTM D638 |
| 抗张强度2(屈服) |
110 |
MPa |
ASTM D638 |
| 伸长率3 |
|
|
ASTM D638 |
| 屈服 |
7.0 |
% |
ASTM D638 |
| 断裂 |
60 |
% |
ASTM D638 |
| 弯曲模量4(100 mm 跨距) |
3520 |
MPa |
ASTM D790 |
| 弯曲强度5(屈服, 100 mm 跨距) |
165 |
MPa |
ASTM D790 |
| 泊松比 |
0.36 |
|
ASTM D638 |
| 泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮) |
10.0 |
mg |
ASTM D1044 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度(23°C) |
53 |
J/m |
ASTM D256 |
| 无缺口悬臂梁冲击(23°C) |
1300 |
J/m |
ASTM D4812 |
| 反向缺口冲击(3.20 mm) |
1300 |
J/m |
ASTM D256 |
| 落锤冲击(23°C) |
36.6 |
J |
ASTM D3029 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm |
210 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm |
201 |
°C |
ASTM D648 |
| 维卡软化温度 |
219 |
°C |
ASTM D15256 |
| 线形热膨胀系数 |
|
|
ASTM E831 |
| 流动 : -20 到 150°C |
5.6E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : -20 到 150°C |
5.4E-5 |
cm/cm/°C |
ASTM E831 |
| 导热系数 |
0.22 |
W/m/K |
ASTM C177 |
| RTI Elec |
170 |
°C |
UL 746 |
| RTI Imp |
170 |
°C |
UL 746 |
| RTI |
170 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 体积电阻率 |
1.0E+17 |
ohms·cm |
ASTM D257 |
| 介电强度 |
|
|
ASTM D149 |
| 1.60 mm, in Air |
33 |
kV/mm |
ASTM D149 |
| 1.60 mm, in Oil |
28 |
kV/mm |
ASTM D149 |
| 3.20 mm, in Oil |
20 |
kV/mm |
ASTM D149 |
| 介电常数 |
|
|
ASTM D150 |
| 100 Hz |
3.15 |
|
ASTM D150 |
| 1 kHz |
3.15 |
|
ASTM D150 |
| 耗散因数 |
|
|
ASTM D150 |
| 100 Hz |
1.5E-3 |
|
ASTM D150 |
| 1 kHz |
1.2E-3 |
|
ASTM D150 |
| 2.45 GHz |
2.5E-3 |
|
ASTM D150 |
| 耐电弧性7 |
PLC 5 |
|
ASTM D495 |
| 相比耐漏电起痕指数(CTI) |
PLC 4 |
|
UL 746 |
| 高电弧燃烧指数(HAI) |
PLC 3 |
|
UL 746 |
| 高电压电弧起痕速率 (HVTR) |
PLC 2 |
|
UL 746 |
| 热丝引燃 (HWI) |
PLC 1 |
|
UL 746 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 0.400 mm |
V-2 |
|
UL 94 |
| 0.750 mm |
V-0 |
|
UL 94 |
| 3.00 mm |
5VA |
|
UL 94 |
| 极限氧指数 |
47 |
% |
ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min |
0.700 |
|
ASTM E662 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
149 |
°C |
|
| 干燥时间 |
4.0 到 6.0 |
hr |
|
| 干燥时间，最大 |
24 |
hr |
|
| 建议的最大水分含量 |
0.020 |
% |
|
| 建议注射量 |
40 到 60 |
% |
|
| 料筒后部温度 |
332 到 399 |
°C |
|
| 料筒中部温度 |
338 到 399 |
°C |
|
| 料筒前部温度 |
343 到 399 |
°C |
|
| 射嘴温度 |
343 到 399 |
°C |
|
| 加工（熔体）温度 |
349 到 399 |
°C |
|
| 模具温度 |
135 到 163 |
°C |
|
| 背压 |
0.345 到 0.689 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.025 到 0.076 |
mm |
|
| 挤出 |
额定值 |
单位制 |
|
| 干燥温度 |
138 到 149 |
°C |
|
| 干燥时间 |
4.0 到 6.0 |
hr |
|
| 建议的最大水分含量 |
0.010 到 0.020 |
% |
|
| 料筒1区温度 |
324 到 349 |
°C |
|
| 料筒2区温度 |
329 到 357 |
°C |
|
| 料筒3区温度 |
329 到 357 |
°C |
|
| 料筒4区温度 |
329 到 357 |
°C |
|
| 料筒5区温度 |
329 到 357 |
°C |
|
| 接头温度 |
329 到 357 |
°C |
|
| 口模温度 |
327 到 357 |
°C |
|
| 挤压说明 |
| Drying Time (Cumulative): 24 hrsHead - Zone 6 - Top Temperature: 329 - 357 °CHead - Zone 7 - Bottom Temperature: 329 - 357 °CMelt Temperature (Parison): 321 - 357 °CMold Temperature: 66 - 177 °CScrew Speed: 10 - 70 rpm |
| 备注 |
| 1 . |
5.0 mm/min |
| 2 . |
类型 1, 5.0 mm/min |
| 3 . |
类型 1, 5.0 mm/min |
| 4 . |
2.6 mm/min |
| 5 . |
2.6 mm/min |
| 6 . |
标准 B (120°C/h), 载荷2 (50N) |
| 7 . |
钨电极 |