巴塞尔医疗级LDPE 1840H 吹塑级 医疗级LDPE 医疗包装应用 FDA USP认证。
Purell PE 1840 H
低密度聚乙烯
LyondellBasell Industries
产品说明:
Purell PE 1840 H is a low density polyethylene with good flexibility and delivered in pellet form. It is used by our customers mainly for small blow moulding of heathcare applications such as ampoules but also be used in film applications and injection moulding.
Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical (P AD) and Business contacts first.
Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical (P AD) and Business contacts first.
To discuss a medical/pharmaceutical application please contact: your local Distributor or your local LyondellBasell contact.
Purell PE 1840 H 物性表
基本信息 | |
---|---|
特性 |
|
用途 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 0.919 | g/cm3 | ISO 1183, ASTM D1505 |
熔流率(熔体流动速率)(190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
肖氏硬度 | |||
邵氏 D | 47 | ASTM D2240 | |
邵氏 D | 45 | ISO 868 | |
球压硬度(H 49/30) | 15.0 | MPa | ISO 2039-1 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | |||
1% 正割 | 254 | MPa | ASTM D638 |
23°C | 200 | MPa | ISO 527-2 |
抗张强度 | |||
屈服 | 10.8 | MPa | ASTM D638 |
屈服, 23°C | 9.00 | MPa | ISO 527-2 |
断裂 | 12.2 | MPa | ASTM D638 |
拉伸应变 | |||
屈服 | 15 | % | ISO 527-2 |
断裂 | 670 | % | ASTM D638 |
弯曲模量 - 1% 正割 | 241 | MPa | ASTM D790 |
摩擦系数 | 0.75 | ISO 8295 |
薄膜 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
薄膜厚度 - 经测试 | 50 | μm | |
可供应的薄膜厚度 | 30 to 80 μ | ||
抗张强度 | ISO 527-3 | ||
MD : 50 μm, 吹塑薄膜 | 27.0 | MPa | ISO 527-3 |
TD : 50 μm, 吹塑薄膜 | 17.0 | MPa | ISO 527-3 |
伸长率 | ISO 527-3 | ||
MD : 断裂, 50 μm, 吹塑薄膜 | 200 | % | ISO 527-3 |
TD : 断裂, 50 μm, 吹塑薄膜 | 600 | % | ISO 527-3 |
落锤冲击(50 μm) | 120 | g | ASTM D1709 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
维卡软化温度 | |||
-- | 87.0 | °C | ASTM D1525 |
-- | 88.0 | °C | ISO 306/A50 |
溶融温度(DSC) | 108 | °C | ISO 3146 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
Gardner光泽度(60°, 50.0 μm, 吹塑薄膜) | 75 | ASTM D523 | |
光泽度(20°, 50.0 μm, 吹塑薄膜) | 20 | ASTM D2457 | |
雾度(50.0 μm, 吹塑薄膜) | 11 | % | ASTM D1003 |
补充信息 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
Failure Energy(50.0 μm) | 45.0 | J/cm | DIN 53373 |
Film properties tested using 50 μm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 2:1. |
挤出 | 额定值 | 单位制 | |
---|---|---|---|
熔体温度 | 170 到 220 | °C |