上海沐音新材料有限公司
LNP? FARADEX? NX07344 compound
聚碳酸酯+丙烯腈丁二烯苯乙烯
玻璃纤维增强材料; 不锈钢纤维
产品说明:
FARADEX NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material include: EMI/RFI Shielding and ESD.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
填料/增强材料
|
|
|||
|
特性
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.46
|
g/cm3
|
ASTM D792,ISO 1183 |
|
收缩率
|
内部方法 | ||
|
流动
|
0.38
|
%
|
|
|
横向流动
|
0.46
|
%
|
|
|
吸水率
|
|||
|
24 hr, 50% RH
|
0.080
|
%
|
ASTM D570 |
|
平衡, 23°C, 50% RH
|
0.040
|
%
|
ISO 62 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
6000
|
MPa
|
ASTM D638 |
|
--
|
5800
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
断裂4
|
60.0
|
MPa
|
ASTM D638 |
|
断裂
|
62.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
断裂4
|
1.8
|
%
|
ASTM D638 |
|
断裂
|
1.8
|
%
|
ISO 527-2/5 |
|
弯曲模量5(50.0 mm 跨距)
|
5300
|
MPa
|
ASTM D790 |
|
弯曲应力
|
|||
|
--6,7
|
105
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
90.0
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距5
|
90.0
|
MPa
|
ASTM D790 |
|
断裂弯曲应变8
|
2.8
|
%
|
ISO 178 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度9(23°C)
|
7.6
|
kJ/m2
|
ISO 179/1eA |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
44
|
J/m
|
ASTM D256 |
|
23°C
|
60
|
J/m
|
ASTM D256 |
|
-30°C10
|
5.3
|
kJ/m2
|
ISO 180/1A |
|
23°C10
|
6.0
|
kJ/m2
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
-30°C
|
330
|
J/m
|
ASTM D4812 |
|
23°C
|
350
|
J/m
|
ASTM D4812 |
|
-30°C10
|
21
|
kJ/m2
|
ISO 180/1U |
|
23°C10
|
21
|
kJ/m2
|
ISO 180/1U |
|
装有测量仪表的落镖冲击(23°C, Total Energy)
|
11.5
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
1.8 MPa, 未退火, 3.20 mm
|
94.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
96.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距11
|
96.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
105
|
°C
|
ASTM D152512,ISO 306/B12012 |
|
--
|
101
|
°C
|
ASTM D152513 |
|
--
|
102
|
°C
|
ISO 306/A50 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
3.1E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 60°C
|
2.9E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
5.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : 23 到 60°C
|
7.4E-5
|
cm/cm/°C
|
ISO 11359-2 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+3 到 1.0E+6
|
ohm
|
ASTM D257 |
|
体积电阻率
|
1.0E+4 到 1.0E+6
|
ohm·cm
|
ASTM D257 |
|
屏蔽效力
|
内部方法 | ||
|
1.50 mm
|
47 到 53
|
dB
|
|
|
3.00 mm
|
60 到 70
|
dB
|
|
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级(1.50 mm)
|
V-0
|
|
UL 94 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
85.0 到 90.0
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.040
|
%
|
|
|
料筒后部温度
|
260 到 300
|
°C
|
|
|
料筒中部温度
|
260 到 300
|
°C
|
|
|
料筒前部温度
|
265 到 300
|
°C
|
|
|
射嘴温度
|
265 到 300
|
°C
|
|
|
加工（熔体）温度
|
270 到 300
|
°C
|
|
|
模具温度
|
60.0 到 100
|
°C
|
|
|
背压
|
4.00
|
MPa
|
|
|
螺杆转速
|
30 到 100
|
rpm
|
| 备注 |
  |