LNP? STAT-LOY? NX03583 compound
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin containing Anti-Static, Flame Retardant. Added features of this material include: Antistat.
Also known as: LNP* STAT-LOY* Compound PDX-03583
Product reorder name: NX03583
Also known as: LNP* STAT-LOY* Compound PDX-03583
Product reorder name: NX03583
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
添加剂
|
|
|||
|
特性
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.26
|
g/cm3
|
ASTM D792 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量3
|
2160
|
MPa
|
ASTM D638 |
|
抗张强度
|
ASTM D638 | ||
|
屈服
|
56.2
|
MPa
|
|
|
断裂
|
49.6
|
MPa
|
|
|
伸长率
|
ASTM D638 | ||
|
屈服
|
100
|
%
|
|
|
断裂
|
5.0
|
%
|
|
|
弯曲模量
|
2160
|
MPa
|
ASTM D790 |
|
弯曲强度
|
84.8
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度(23°C)
|
640
|
J/m
|
ASTM D256 |
|
装有测量仪表的落镖冲击(23°C, Energy at Peak Load)
|
38.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度(1.8 MPa, 未退火, 3.20 mm)
|
99.4
|
°C
|
ASTM D648 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+10 到 1.0E+12
|
ohm
|
ASTM D257 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级(1.59 mm, Testing by SABIC)
|
V-0
|
|
UL 94 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
82.2
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
199 到 210
|
°C
|
|
|
料筒中部温度
|
210 到 221
|
°C
|
|
|
料筒前部温度
|
221 到 232
|
°C
|
|
|
加工（熔体）温度
|
199 到 232
|
°C
|
|
|
模具温度
|
37.8 到 54.4
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
| 备注 |
  |