CYCOLOY? CX7211 resin
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
CYCOLOY CX7211 PC/ABS resin is a non-filled, injection moldable grade which has UL 94 rating at 2.5 mm 5VA. CYCOLOY CX7211 resin provides all color options and features an excellent balance of flow, impact and heat properties, which makes it an excellent candidate for thin wall applications.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料1
|
||||
|
UL 黄卡2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.18
|
g/cm3
|
ASTM D792 |
|
--
|
1.19
|
g/cm3
|
ISO 1183 |
|
熔流率（熔体流动速率）(260°C/2.16 kg)
|
16
|
g/10 min
|
ASTM D1238 |
|
溶化体积流率（MVR）(260°C/2.16 kg)
|
14.0
|
cm3/10min
|
ISO 1133 |
|
收缩率 - 流动(3.20 mm)
|
0.40 到 0.60
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.24
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.12
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
--3
|
2950
|
MPa
|
ASTM D638 |
|
--
|
2800
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服4
|
66.0
|
MPa
|
ASTM D638 |
|
屈服
|
62.0
|
MPa
|
ISO 527-2/50 |
|
断裂4
|
60.0
|
MPa
|
ASTM D638 |
|
断裂
|
55.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服4
|
4.0
|
%
|
ASTM D638 |
|
屈服
|
4.0
|
%
|
ISO 527-2/50 |
|
断裂4
|
98
|
%
|
ASTM D638 |
|
断裂
|
90
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距5
|
2750
|
MPa
|
ASTM D790 |
|
--6
|
2500
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
--6,7
|
100
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距5
|
103
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度8
|
ISO 179/1eA | ||
|
-30°C
|
10
|
kJ/m2
|
|
|
23°C
|
40
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
130
|
J/m
|
ASTM D256 |
|
23°C
|
630
|
J/m
|
ASTM D256 |
|
-30°C9
|
10
|
kJ/m2
|
ISO 180/1A |
|
23°C9
|
40
|
kJ/m2
|
ISO 180/1A |
|
装有测量仪表的落镖冲击(23°C, Total Energy)
|
60.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
94.0
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 6.40 mm
|
102
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 3.20 mm
|
89.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
96.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距10
|
90.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
105
|
°C
|
ASTM D152511,ISO 306/B50,ISO 306/B120 |
|
Ball Pressure Test(75°C)
|
Pass
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
6.1E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -40 到 40°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
横向 : -40 到 40°C
|
5.5E-5
|
cm/cm/°C
|
ASTM E831 |
|
横向 : -40 到 40°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
导热系数
|
0.20
|
W/m/K
|
ISO 8302 |
|
RTI Elec
|
90.0
|
°C
|
UL 746 |
|
RTI Imp
|
90.0
|
°C
|
UL 746 |
|
RTI
|
90.0
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
1.0E+15
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
IEC 60243-1 | ||
|
0.800 mm, 在油中
|
35
|
kV/mm
|
|
|
1.60 mm, 在油中
|
25
|
kV/mm
|
|
|
3.20 mm, 在油中
|
17
|
kV/mm
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 0
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
1.25 mm
|
V-1
|
|
|
|
1.50 mm
|
V-0
|
|
|
|
2.00 mm
|
5VB
|
|
|
|
2.50 mm
|
5VA
|
|
|
|
灼热丝易燃指数(1.00 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
1.00 mm
|
800
|
°C
|
|
|
3.00 mm
|
800
|
°C
|
|
|
极限氧指数
|
32
|
%
|
ISO 4589-2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
82.2 到 87.8
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
8.0
|
hr
|
|
|
建议的最大水分含量
|
0.040
|
%
|
|
|
建议注射量
|
30 到 80
|
%
|
|
|
料筒后部温度
|
221 到 254
|
°C
|
|
|
料筒中部温度
|
221 到 266
|
°C
|
|
|
料筒前部温度
|
243 到 277
|
°C
|
|
|
射嘴温度
|
243 到 277
|
°C
|
|
|
加工（熔体）温度
|
243 到 277
|
°C
|
|
|
模具温度
|
60.0 到 82.2
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.038 到 0.076
|
mm
|
| 备注 |
  |